1 Section Guide RELEASE FILMS Name Description Maximum use temperature Elongation at break Wrightlon 5200 ETFE 350 % Blue / Red / Clear 1 A4000 FEP 300 % Clear / Red / Violet / White 2 Wrightlon 4600 PMP 250 % Blue / Clear 3 Wrightlon 4800 PET 110 % Translucent white 4 Wrightlon % Blue 5 Wrightlon 3800 PET 120 % Translucent white 6 Wrightlon % Red 7 Dahlar Release Bag % Green 8 Airtech MR1 Fluoropolymer 400 % Blue 9 Resin compatibility Available perforations Page

2 WRIGHTLON 5200 High performance fluoropolymer release film ETFE Elongation at break 350 % ASTM D 882 Tensile strength 7000 psi (48 MPa) ASTM D 882 Compatible with most resin systems Yield 22.8 m /Kg/25.4 ƒm Blue/Red/Clear Unlimited Thickness Width Length Weight / roll Forms available* inch (15 ƒm) 48 inches (1.22 m) 600 feet (183 m) 13 lbs (6 Kg) SHT (Blue) inch (25 ƒm) 48 inches (1.22 m) 600 feet (183 m) 22 lbs (10 Kg) SHT (Blue) inch (25 ƒm) 60 inches (1.52 m) 600 feet (183 m) 26 lbs (12 Kg) SHT (Blue) inch (25 ƒm) 60 inches (1.52 m) 300 feet (91 m) 26 lbs (12 Kg) SHT (Blue) inch (25 ƒm) 48 inches (1.22 m) 600 feet (183 m) 22 lbs (10 Kg) SHT (Red) inch (25 ƒm) 50 inches (1.27 m) 500 feet (152 m) 19 lbs (9 Kg) SHT (Red) inch (25 ƒm) 60 inches (1.52 m) 417 feet (127 m) 19 lbs (9 Kg) SHT (Red) inch (25 ƒm) 60 inches (1.52 m) 600 feet (183 m) 26 lbs (12 Kg) SHT (Red) inch (50 ƒm) 50 inches (1.27 m) 250 feet (76 m) 19 lbs (9 Kg) SHT (Red) inch (25 ƒm) 120 inches (3.04 m) 600 feet (183 m) 52 lbs (24 Kg) CF to 60 inches (Blue) > Elongation at break and tensile strength are measured in machine direction. > is dependent upon the duration at maximum temperature and is process P. 1

3 A4000 High performance fluoropolymer release film A4000 release film is a high temperature and high elongation release film which will conform easily to the most resin systems and will provide a glossy finish when removed from the laminate. FEP Elongation at break 300 % ASTM D 882 Tensile strength 3000 psi (21 MPa) ASTM D 882 Compatible with most resin systems Yield 18.4 m /Kg/25.4 ƒm Clear/Red/Violet/White Thickness Width Length Weight / roll Forms available* inch (25 ƒm) 48 inches (1.22 m) 600 feet (183 m) 27 lbs (12 Kg) SHT (Clear) inch (25 ƒm) 58 inches ( 1.47 m) 497 feet (151 m) 27 lbs (12 Kg) SHT (Clear) inch (50 ƒm) 58 inches ( 1.47 m) 224 feet (68 m) 24 lbs (11 Kg) SHT (Clear) inch (25 ƒm) 50 inches (1.27 m) 500 feet (152 m) 23 lbs (10.5 Kg) SHT (Red) inch (25 ƒm) 60 inches (1.52 m) 417 feet (127 m) 23 lbs (10.5 Kg) SHT (Red) inch (25 ƒm) 72 inches (1.83 m) 347 feet (106 m) 23 lbs (10.5 Kg) SHT (Red) inch (50 ƒm) 50 inches (1.27 m) 250 feet (76 m) 23 lbs (10.5 Kg) SHT (Red) inch (50 ƒm) 60 inches (1.52 m) 208 feet (63 m) 23 lbs (10.5 Kg) SHT (Red) inch (25 ƒm) 50 inches (1.27 m) 500 feet (152 m) 23 lbs (10.5 Kg) SHT (Violet) inch (25 ƒm) 60 inches (1.52 m) 417 feet (127 m) 23 lbs (10.5 Kg) SHT (Violet) inch (25 ƒm) 72 inches (1.83 m) 347 feet (106 m) 23 lbs (10.5 Kg) SHT (Violet) inch (50 ƒm) 50 inches (1.27 m) 250 feet (76 m) 23 lbs (10.5 Kg) SHT (Violet) inch (50 ƒm) 60 inches (1.52 m) 208 feet (63 m) 23 lbs (10.5 Kg) SHT (Violet) inch (25 ƒm) 60 inches (1.52 m) 417 feet (127 m) 23 lbs (10.5 Kg) SHT (White) > is dependent upon the duration at maximum temperature and is process specific. Airtech recommends testing prior to use. >Other sizes upon request. > Bondable A4000 is available treated one side (B.O.S.) is 18 months from date of shipment when * SHT = sheeting, CF = centerfold, LFT = lay-flat tubing, LFT-G = lay-flat tubing gusseted. P. 2

4 WRIGHTLON 4600 Cost effective polyolefin copolymer release film PMP Elongation at break 250 % ASTM D 882 Tensile strength 3400 psi (23 MPa) ASTM D 882 Not recommended for use with vinylester or polyester resin system Yield 46.9 m /Kg/25.4 ƒm Blue/Clear Unlimited Thickness Width Length Weight / roll Forms available* inch (37.5 ƒm) 60 inches (1.52 m) 1668 feet (508 m) 55 lbs (25 Kg) SHT (Blue) inch (50 ƒm) 54 inches (1.37 m) 1500 feet (457 m) 60 lbs (27 Kg) SHT (Blue) Airtech recommends testing prior to use. P. 3

5 WRIGHTLON 4800 Release film for flat parts and tape layer tables PET Elongation at break 110 % ASTM D 882 Tensile strength 21,755 psi (150 MPa) ASTM D F (191 C) Phenolic resins/strong oxidizers Yield 20,150 inƒ/#/mil (28.6 mƒ/kg/25.4 m) Translucent white Thickness Width Length Weight / roll Forms available* inch (50 m) 59 inches (1.5 m) 656 feet (200 m) 48 lbs (21 kg) SHT inch (50 m) 118 inches (3 m) 656 feet (200 m) 118 lbs (53 kg) SHT > is dependent upon the duration at maximum temperature and is process P. 4

6 WRIGHTLON 3700 Low cost release film for commercial and wind energy applications and vinyl ester resin systems. > Good value for low to medium temperature applications > Blue color is visible on laminate surface > Available in P16 perforation style for infusion applications. P16 is a special perforation Elongation at break 550 % ASTM D 882 Tensile strength 7000 psi (48 MPa) ASTM D 882 Flammability (self extinguishing) Yes ATP-5034 Phenolic resins/strong oxidizers Yield 21.2 m /Kg/25.4 ƒm Blue Thickness Width Length Weight / roll Forms available* inch (25 ƒm) 60 inches (1.52 m) 2000 feet (610 m) 96 lbs (44 Kg) SHT inch (25 ƒm) 60 inches (1.52 m) 1000 feet (305 m) 96 lbs (44 Kg) SHT > is dependent upon the duration at maximum temperature and is process P. 5

7 WRIGHTLON 3800 Low temperature PET release film between tool surfaces and composite materials applied using automated tape layup and automated fiber placement equipment. The use of WL3800 allows the composite to be transferred to final cure tooling. In PET Elongation at break 120 % ASTM D 882 Tensile strength 18,855 psi (130 MPa) ASTM D F (93 C) Phenolic resins/strong oxidizers Yield 20,191 inƒ/#/mil (14.4 mƒ/kg/25.4 m) Translucent white Thickness Width Length Weight / roll Forms available* inch (50 m) 59 inches (1.5 m) 656 feet (200 m) 47 lbs (21 kg) SHT inch (50 m) 118 inches (3 m) 656 feet (200 m) 118 lbs (53 kg) SHT > is dependent upon the duration at maximum temperature and is process specific. Airtech recommends testing prior to use. > Custom designed shapes and sizes are available to fit your individual requirements. * SHT = sheeting, CF = centerfold, LFT = lay-flat tubing, LFT-G = lay-flat tubing gusseted. P. 6

8 WRIGHTLON 3900 Inexpensive polyolefin release film WL3900 release film is a high elongation film which will exhibit excellent release properties from polyester, compaction and debulking operations. Polyolefin Elongation at break 500 % ASTM D 882 Tensile strength 6000 psi (41 MPa) ASTM D 882 Compatible with most resin systems Yield 43.7 m /Kg/25.4 ƒm Red Unlimited A variety of sizes (width and thickness) available. Contact Airtech or your local distributor for current stock or a specific request. > Elongation at break and tensile strength are measured in machine direction. > is dependent upon the duration at maximum temperature and is process specific. Airtech recommends testing prior to use. > Custom designed shapes and sizes are available to fit your individual requirements. * SHT = sheeting, CF = centerfold, LFT = lay-flat tubing, LFT-G = lay-flat tubing gusseted. P. 7

9 DAHLAR RELEASE BAG 125 Economical release film can be used for cures up to 285 F (141 C) and will release from most resins associated with aerospace, marine, and recreational products. This formulation has improved tear resistance and elongation over products previously offered as low temperature, multiple process films. phenolics. Polyolefin, multi-layer Elongation at break 400 % ASTM D 882 Tensile strength 9500 psi (65 MPa) ASTM D F (141 C) Compatible with most resin systems Green Unlimited Thickness Width Length Weight / roll Forms available * inch (25 ƒm) 60 inches (1.52 m) 1000 feet (305 m) 53 lbs (24 Kg) SHT > Elongation at break and tensile strength are measured in machine direction. > is dependent upon the duration at maximum temperature and is process specific. Airtech recommends testing prior to use. > Custom designed shapes and sizes are available to fit your individual requirements. * SHT = sheeting, CF = centerfold, LFT = lay-flat tubing, LFT-G = lay-flat tubing gusseted. P. 8

10 AIRTECH MR1 Ultra high temperature release films conformability. It works well with our high temperature sealant tapes. This film will provide a smooth surface after the cure. MR1 release film is offered in inch (25 m) thickness. Fluoropolymer Elongation at break 400 % ASTM D 882 Tensile strength 4496 psi (31 MPa) ASTM D 882 Compatible with most resin systems Yield 18.3 mƒ/kg/25.4 m Blue Unlimited Thickness Width Length Weight / roll Forms available * inch (25 m) 48 inches (1.22 m) 500 feet (152 m) 22 lbs (10 Kg) SHT > Elongation at break and tensile strength are measured in machine direction. > is dependent upon the duration at maximum temperature and is process specific. Airtech recommends testing prior to use. > Custom designed shapes and sizes are available to fit your individual requirements. * SHT = sheeting, CF = centerfold, LFT = lay-flat tubing, LFT-G = lay-flat tubing gusseted. P. 9

Mex Quest Engineering (S) Pte Ltd Phone: Fax: E-mail: Website: 6746 2723 6746 3673 sales@mexquest.com.

11 Mex Quest Engineering (S) Pte Ltd Phone: Fax: Website: RESIN COMPATIBILITY Release film selection guide NOTE The following guideline is intended for reference only. Airtech cannot control processing parameters or test all the materials available. Vacuum bagging film samples are available. Risk reduction panel testing is strongly recommended. Film selection should be based on temperature requirement. P. 10

12 AVAILABLE PERFORATIONS Perforation style Nominal hole diameter Description Open area Maximum width P P2 P inch (1.143 mm) Pierced / (N/A) inch (0.381 mm) 1/4" center staggered 1/2" center 1/4" center 1.27 % 72 inches (182.9 cm) 0.71 % 72 inches (182.9 cm) 0.14 % 64 inches (162.6 cm) P inch (1.143 mm) 2" center 0.04 % 72 inches (182.9 cm) P inch (1.143 mm) 3.5" center % 72 inches (182.9 cm) P inch (0.381 mm) 2" center % 64 inches (162.6 cm) P inch (0.381 mm) 3" center % 64 inches (162.6 cm) P inch (0.381 mm) 8" center % 64 inches (162.6 cm) P inch (1.143 mm) 10" center % 72 inches (182.9 cm) P11 P inch (0.381 mm) inch (0.4 mm) 1/8" center 3 mm center 0.28 % 64 inches (162.6 cm) 0.8 % 72 inches (182.9 cm) P inch (0.381 mm) 1" center % 64 inches (162.6 cm) P34 MP22 MP inch (1.143 mm) inch (0.4 mm) inch (0.125 mm) 1/2" center 1.5 mm center 1 mm center % 72 inches (182.9 cm) 2.79 % 80 inches (203.2 cm) % 72 inches (182.9 cm) >Spacing is approximate. >Various perforation methods can be utilized including and not limited to die stamping, laser, hot pin roller, needle punching and pinwheel. >Minimums are required for some perforation patterns when not in stock. P. 11

FABRICS & BAGGING Fiberglass Cloth. Kevlar Cloth. Carbon Fiber Cloth. Mia Vacuum Bagging Supplies

FABRICS & BAGGING Fiberglass Cloth. Kevlar Cloth. Carbon Fiber Cloth. Mia Vacuum Bagging Supplies FABRICS & BAGGING This comprehensive selection of materials from the biggest names in the industry offers solutions for the construction of large, lightweight molds and production parts. 62-63 Fiberglass