1 COMPANY ECOSMART SURFACE TECHNOLOGIES REQUESTED BY MICHAEL MCDONALD JOB NAME SALT SPRAY/FOG TESTING JOB NUMBER #1099 ANALYST SUE KALAIN P R O D U C T A N A L Y S I S Kalain Analytical received four (4) samples for Salt Spray/Fog Testing. It was requested that the test cover 6000 hours with inspections at 1000, 2000, 4000 and 6000 hours. This report begins with the images at the start of the test on and includes: Inspection #1 at 1000 hrs on Inspection #2 at 2000 hrs on Inspection #3 at 4000 hrs on

2 Page 2 of 22 Photo Documentation Fig Coated side at beginning of salt spray test. Fig Coated side after 1000 hr. salt spray test.

3 Page 3 of 22 Fig Early stages of surface pitting corrosion is evident after 2000 hr. of salt spray test. Fig Early stages of surface pitting corrosion is evident after 4000 hr. of salt spray test.

4 Page 4 of 22 Fig Uncoated side at beginning of salt spray test. Fig Uncoated side after 1000 hr. salt spray test.

5 Page 5 of 22 Fig Surface corrosion is evident on uncoated side after 2000 hr. salt spray test. Fig Surface corrosion is evident on uncoated side after 4000 hr. salt spray test.

6 Page 6 of 22 Fig Copper tubing view #1, at beginning of salt spray test. Fig Copper tubing view #1, after 1000 hr. of salt spray test.

7 Page 7 of 22 Fig Copper tubing view #1 shows early stages of pitting corrosion visible after 2000 hr. salt spray test. Fig The oxidation appears to be accelerating on view #1 after 4000 hr. salt spray test.

8 Page 8 of 22 Fig Copper tubing view #2, at beginning of salt spray test. Fig Copper tubing view #2, after 1000 hr. of salt spray test.

9 Page 9 of 22 Fig Copper tubing view #2 shows early stages of pitting corrosion evident after 2000 hr. salt spray test. Fig The oxidation on view #2 appears to be accelerating after 4000 hr. salt spray test.

10 Page 10 of 22 Fig at beginning of salt spray test. Fig #1, after 1000 test.

Page 11 of 22 Fig. 19 11-17-13 #1, after 2000 test. No visible changes Fig.

11 Page 11 of 22 Fig #1, after 2000 test. No visible changes Fig #1 after 4000 hr. of salt spray test. Minor accumulation of sediment visible on surfaces. No apparent coating attack.

12 Page 12 of 22 Fig #2 at beginning of salt spray test. Fig #2, after 1000 test.

Page 13 of 22 Fig.23 11-17-13 #2, after 2000 test.

13 Page 13 of 22 Fig #2, after 2000 test. No visible changes. Fig #2 after 4000 hr. of salt spray test. Minor accumulation of sediment visible on surfaces. No apparent coating attack.

14 Page 14 of 22 Fig #3 at beginning of salt spray test. Fig #3, after 1000 test.

Page 15 of 22 Fig. 27 11-17-13 #3, after 2000 test.

28 2-9-14 #3 after 4000 hr. of salt spray test.

15 Page 15 of 22 Fig #3, after 2000 test. No visible changes. Fig #3 after 4000 hr. of salt spray test. Minor accumulation of sediment visible on surfaces. No apparent coating attack.

16 Page 16 of 22 Fig #4 at beginning of salt spray test. Fig #4, after 1000 test.

Page 17 of 22 Fig. 31 11-17-13 #4, after 2000 test.

32 2-9-14 #4 after 4000 hr. of salt spray test.

17 Page 17 of 22 Fig #4, after 2000 test. No visible changes. Fig #4 after 4000 hr. of salt spray test. Minor accumulation of sediment visible on surfaces. No apparent coating attack.

18 Page 18 of 22 Fig #5 at beginning of salt spray test. Fig #5, after 1000 test.

Page 19 of 22 Fig. 35 11-17-13 #5, after 2000 test.

36 2-9-14 #5 after 4000 hr. of salt spray test.

19 Page 19 of 22 Fig #5, after 2000 test. No visible changes. Fig #5 after 4000 hr. of salt spray test. Minor accumulation of sediment visible on surfaces. No apparent coating attack.

20 Page 20 of 22 Fig #6 at beginning of salt spray test. Fig #6, after 1000 test.

Page 21 of 22 Fig. 39 11-17-13 #6, after 2000 test.

40 2-9-14 #6 after 4000 hr. of salt spray test.

21 Page 21 of 22 Fig #6, after 2000 test. No visible changes. Fig #6 after 4000 hr. of salt spray test. Minor accumulation of sediment visible on surfaces. No apparent coating attack.

22 Page 22 of 22 Sue Kalain Technician Authorized Signature on file Date: This Certificate shall not be reproduced in full without the written approval of Kalain Analytical. The recording of false, fictitious or fraudulent statements or entries on this document may be punished as a felony under Federal statutes including United States Code, Title 18, Chapter 47. The Seller hereby warrants that the information covered by this Certificate has been processed to conform to the work statement on the face of the purchase order and specification requirements shown above and that the test results and/or statements hereon are correct to the best of our knowledge, and represents the samples supplied. The foregoing warranties are sole and exclusive. Seller shall not be liable for any indirect, special or consequential damages. In no event shall Seller's liability exceed the purchase price of the services involved.

3M Scotchkote System Application Guide. High Performance Corrosion Resistant System for Plastisol Coated Metal Cladding

3M Scotchkote System Application Guide. High Performance Corrosion Resistant System for Plastisol Coated Metal Cladding High Performance Corrosion Resistant System for Plastisol Coated Metal Cladding - Issue 1 Surface Preparation & Cleaning Application of Patch Primer to Corroded Areas Application of Primer to Patch Primed