Brazing, Soldering, Adhesive, Bonding & Mechanical Fastening process. Chapter 30
|
|
- Horace Wilson
- 5 years ago
- Views:
Transcription
1 Brazing, Soldering, Adhesive, Bonding & Mechanical Fastening process Chapter 30
2 Joining process Brazing A filler metal is placed between two workpieces and heated until melted Two main types of Brazing Ordinary Braze welding Use of flux is very important
3 Filler Metals Available in a wide range of brazing temperatures They come in a wide range of shapes Choice of the filler metal and its composition are important Diffusion of the filler metal in to the workpeice is an important consideration Fig: a) Brazing b) Braze welding operation
4 Fluxes The use of flux in brazing is very important Generally made of: Borax Boric acid Borates Fluorides Chlorides Wetting agents may also be added
5 Torch Brazing Brazing Methods Performed by heating the joint with a torch Depositing the filler metal in the joint Suitable part thickness ( )mm Not a automated process More than one torch can be used in this process
6 Brazing Methods Furnace Brazing Precleaned & Preloaded with brazing metal Heated in a furnace Fig:An example of furnace brazing a)before b) after
7 Other Types Of Brazing Induction Brazing Resistance Brazing Dip Brazing Infrared Brazing Diffusion Brazing
8 Braze Welding Prepared like fusion welding Filler metal is deposited at the joint with the use of an oxyacetylene torch Considerably more filler is used Temperature is minimal compared to that of fusion welding; part distortion is minimal
9 Brazing Process Capabilities Dissimilar metals can be assembled with good joint strength Shear strength of brazed joints can reach 800Mpa Fig:Joint Designs commonly used in brazing operations.the clearance between the two parts being brazed is an important factor in joint strength.if the clearance is to small, the molten braze metal will not fully penetrate the interface.
10 Good/Poor Designs
11 Soldering Different types of soldering Torch Furnace Iron Induction Resistance Dip Infrared Ultrasonic reflow (paste) Wave
12 Reflow Soldering Solvents present in the paste are evaporated The Flux in the paste is activated and the fluxing action occurs The components are carefully preheated The solder particles are melted and wet the joint The assembly is cooled
13 Wave Soldering Popular approach to attaching circuits to circuit boards Fig: a)screening or stenciling paste onto a printed circuit board: 1) Stenciling process 2) a section of a typical stencil pattern b) wave soldering process
14 Types Of Fluxes Inorganic acids or salts clean the surface rapidly Noncorrosive resinbased used in electrical applications Soldering is used extensively in electronics industry
15 Adhesive Bonding Products are joined and assembled by the use of Adhesives Adhesives properties to be considered Strength Toughness Resistance to various fluids Ability to wet the surface to be bonded
16 Types of adhesives Surface must be clean for joining parts Should avoid joints that might be subjected to peeling forces Design for adhesive bonding
17 Adhesive Peeling Test Fig : Characteristic behavior of (a) brittle (b) tough adhesive in a peeling test
18 Joint Design in Adhesive Bonding Fig:Various joint design in adhesive bonding.
19 Configurations for adhesive bonds Fig : (a) single lap (b) double lap (c) scarf (d) strap
20 Threaded Fasters Bolts Screws Nuts Mechanical Fastening Other Fastening Methods Stapling Crimping Snap-in Fasteners Shrink and press fits
21 Rivets Fig:a)solid b)tubular c) split (bifurcated) d) compression Fig : Design guidelines for riveting (a)exposed shank is too long; the result is buckling instead of upsetting (b)rivets should be placed sufficiently far from edges to avoid stress concentrations (c)joined sections should allow ample clearance for riveting tools (d) section curvature should not interfere with the riveting process
22 Joining Plastics Heat softens the plastic to a molten state Then pressure added & fusion takes place External Heat Sources Hot air Heated tools & dies Electrical-Resistance Lasers Internal Heat Sources Ultrasonic welding Friction welding
23 THE END
Brazing Braze Welding
1 2 3 4 Brazing Filler metals typically melt above 450 o C (840 o F); Below MP of host metals. Term brazing derived from brass, to harden Process originated 3000-2000 B.C. Typically, a filler (braze) metal
More informationSME 2713 Manufacturing Processes. Assoc Prof Zainal Abidin Ahmad
PROSES-PROSES PENYAMBUNGAN - 1 SME 2713 Manufacturing Processes Page 1 Outline 1. Introduction 2. Brazing 3. Soldering 4. Welding 5. Mechanical fasteners 6. Adhesives Page 2 1 1. Introduction Page 3 25
More informationWelding Engineering Dr. D. K. Dwivedi Department of Mechanical & Industrial Engineering Indian Institute of Technology, Roorkee
Welding Engineering Dr. D. K. Dwivedi Department of Mechanical & Industrial Engineering Indian Institute of Technology, Roorkee Module - 4 Arc Welding Processes Lecture - 8 Brazing, Soldering & Braze Welding
More informationFUNDAMENTAL MANUFACTURING PROCESSES Plastics Machining & Assembly NARRATION (VO): AN ASSEMBLY METHOD. NARRATION (VO): MANUALLY..., OR AUTOMATICALLY.
Copyright 2002 Society of Manufacturing Engineers --- 1 --- FUNDAMENTAL MANUFACTURING PROCESSES Plastics Machining & Assembly SCENE 1. CG: Plastics Assembly white text centered on black SCENE 2. tape 739,
More informationChapter 33: Other Welding Processes, Brazing and Soldering
Chapter 33: Other Welding Processes, Brazing and Soldering 33.1 Introduction 33.2 Other Welding and Cutting Processes Electroslag Welding FIGURE 33-1 (a) Arrangement of equipment and workpieces for making
More informationMETAL FABRICATION MECHANICAL
METAL FABRICATION MECHANICAL Machine Screws Machine screws have a parallel thread and need a threaded hole to screw into. They come in a wide variety of materials and sizes and are used for semi-permanent
More informationIntroduction to Manufacturing Processes
Introduction to Manufacturing Processes Products and Manufacturing Product Creation Cycle Design Material Selection Process Selection Manufacture Inspection Feedback Typical product cost breakdown Manufacturing
More informationName: Class: Teacher:..
Name: Class: Teacher:.. 1 Metals All metals in use today are either PURE METALS or ALLOYS. Copper, iron, tin, lead, gold and silver are all examples of PURE METALS which have been mined from the Earth
More informationAMTS STANDARD WORKSHOP PRACTICE. Bond Design
AMTS STANDARD WORKSHOP PRACTICE Reference Number: AMTS_SWP_0027_2008 Date: December 2008 Version: A 1 Contents 1 Technical Terms...3 2 Scope...3 3 Primary References...3 4 Basic...3 4.1 Typical joint types...4
More informationActivity Joinery, Fastener, Adhesive, Welding & Bonding Identification
Name: Date Completed: Activity 3.3.1 Joinery, Fastener, Adhesive, Welding & Bonding Identification Introduction When you look at a fine piece of furniture, such as a chair with many different parts, it
More informationContent. Hot-dip galvanized narrow strip. Areas of application. Product information
Steel Hot-dip galvanized narrow strip Product information Issue: October 2016, version 0 Areas of application Hot-dip galvanized narrow strip from thyssenkrupp combines the advantages of batch galvanizing
More informationRiveted Joints : Types and Uses
Riveted Joints : Types and Uses Page 1 / 10 Instructional Objectives: At the end of this lesson, the students should be able to know: Basic types of riveted joints. Different important design parameters
More informationFORM TP m a y /ju n e 2010
TEST CODE 01335020 FORM TP 2010089 m a y /ju n e 2010 CARIBBEAN EXAMINATIONS COUNCIL SECONDARY EDUCATION CERTIFICATE EXAMINATION MECHANICAL ENGINEERING TECHNOLOGY Paper 02 - Technical Proficiency 2 j hours
More informationBolt Material Types and Grades 1- Bolts made of carbon steel and alloy steel: 4.6, 4.8, 5.6, 5.8, 6.8, 8.8, 10.9 Nuts made of carbon steel and alloy
Bolt Material Types and Grades 1- Bolts made of carbon steel and alloy steel: 4.6, 4.8, 5.6, 5.8, 6.8, 8.8, 10.9 Nuts made of carbon steel and alloy steel: 4, 5, 6, 8, 10, 12 2- Bolts made of stainless
More informationDesign and Technology Resistant materials Key words and definitions
Design and Technology Resistant materials Key words and definitions Word Acrylic Definition a type of thermoplastic, which is hard and can be transparent. Used to make shop signs. Perspex is a trade/brand
More informationMECHANICAL ASSEMBLY John Wiley & Sons, Inc. M. P. Groover, Fundamentals of Modern Manufacturing 2/e
MECHANICAL ASSEMBLY Threaded Fasteners Rivets and Eyelets Assembly Methods Based on Interference Fits Other Mechanical Fastening Methods Molding Inserts and Integral Fasteners Design for Assembly Mechanical
More informationBRAZING OF TIC CERMET TO STEEL Laansoo, A.; Kübarsepp, J. & Vainola, V.
7 th International DAAAM Baltic Conference INDUSTRIAL ENGINEERING 22-24 April 2010, Tallinn, Estonia BRAZING OF TIC CERMET TO STEEL Laansoo, A.; Kübarsepp, J. & Vainola, V. Abstract: Shear strength of
More informationCeraDiodes. Soldering directions. Date: July 2014
CeraDiodes Soldering directions Date: July 2014 EPCOS AG 2014. Reproduction, publication and dissemination of this publication, enclosures hereto and the information contained therein without EPCOS' prior
More informationFasteners. Metal Fasteners, Joining, and Adhesives. Bolts. Metal Fasteners, Joining, and Adhesives
Metal Fasteners, Joining, and Adhesives Fasteners Metal assemblies are often held together with fasteners, hardware devices that mechanically join or affix two or more objects together. Assembling with
More informationjoining materials - wood
UNIT D E S I G N A N D M A N U F A C T U R E : C O U R S E M A T E R I A L Wood joints joining materials - wood The majority of joints used in woodcraft have been designed specifically to attain the maximum
More informationApplication Notes. Introduction
Introduction EMC Technology has provided an extensive collection of Application Notes that help designers mount and measure the products. These cover the complete line of Thermopads, Attenuators, SmartLoad,
More informationThis presentation is courtesy of
This presentation is courtesy of Hot Melt Assembly ASC Hot Melt Short Course October 9, 2005 Presenter: Jerry Schouten Courtesy 1 Assembly Agenda Joint design Requirements Advantages of Hot Melt Adhesive
More informationButt Two pieces of wood meeting with flat sides adjoining usually at right angles. Some type of connector is needed to prevent movement.
Wood Connections There are basically five different types of connectors: Interlocking (carpentry joints), Dowel, Metal Connectors, Special Formed Connectors and Adhesives. I Interlocking (Carpentry Joints)
More informationGold plating, 140 Gases compressed, 393 liquid,393 Grounding, safety, 403
INDEX Acids, safety, 394 Activities, 1 Adhesives, 349 Allowances manufacturing, 77 rework,82 Aluminum Plating, 139 Analysis work distribution, 20, 29 processes, 32 Analyzing job details, 19 Assemblers
More informationDesign of Machine Elements I Prof. G. Chakraborty Department of Mechanical Engineering Indian Institute of Technology Kharagpur
Design of Machine Elements I Prof. G. Chakraborty Department of Mechanical Engineering Indian Institute of Technology Kharagpur Lecture - 22 Rivet Joints Dear student, welcome to the video lectures on
More informationInduction Heating Application Viewbook
Induction Heating Application Viewbook Induction heating application notes for industry 1 Induction Heating Content: Induction heating is an ingenious and effective, non-contact process for electromagnetically
More informationExecution of brazing test samples of S235 steel sheets, with a new brass type
EUROPEAN UNION GOVERNMENT OF ROMANIA SERBIAN GOVERNMENT Structural Funds 2007-2013 Romania Republic of Serbia IPA Cross-border Cooperation Programme Project logo / LP logo Project: Promoting new ecologic
More informationISO INTERNATIONAL STANDARD. Fasteners Hot dip galvanized coatings. Éléments de fixation Revêtements de galvanisation à chaud
Provläsningsexemplar / Preview INTERNATIONAL STANDARD ISO 10684 First edition 2004-07-15 Fasteners Hot dip galvanized coatings Éléments de fixation Revêtements de galvanisation à chaud Reference number
More informationBrazeTec. Selection Rules of Brazing Alloys and Fluxes
BrazeTec Selection Rules of Brazing Alloys and Fluxes 1. Introduction Welding additives are virtually always materialspecific, meaning that they are first and foremost selected depending on the composition
More informationCH # 8. Two rectangular metal pieces, the aim is to join them
CH # 8 Screws, Fasteners, and the Design of Non-permanent Joints Department of Mechanical Engineering King Saud University Two rectangular metal pieces, the aim is to join them How this can be done? Function
More informationAN ROINN OIDEACHAIS AGUS EOLAÍOCHTA THE JUNIOR CERTIFICATE METALWORK SYLLABUS. Contents
AN ROINN OIDEACHAIS AGUS EOLAÍOCHTA THE JUNIOR CERTIFICATE METALWORK SYLLABUS Contents METALWORK...2 TECHNIQUES AND DESIGN...3 MATERIALS AND TECHNOLOGY...5 METALWORK General Aims. The course provides an
More informationAssembly Instructions for SCC1XX0 series
Technical Note 82 Assembly Instructions for SCC1XX0 series TABLE OF CONTENTS Table of Contents...1 1 Objective...2 2 VTI's 32-lead Dual In-line Package (DIL-32)...2 3 DIL-32 Package Outline and Dimensions...2
More informationNote: Conditions where bending loads are imposed on the bolt e.g. non-parallel bolting surfaces, should be avoided.
Bolted Joint Design Introduction A most important factor is machine design, and structural design is the rigid fastening together of different components. This should include the following considerations..
More informationDigital Volume Control
Digital Volume Control DCU 254 Page 1 of 5 1. Handling Handle the VC by the body to avoid mechanical stress to the leads. 2. Tools Proper tools should be used for cutting and bending, such as sharp cutters
More informationAssembly Instructions for SCA6x0 and SCA10x0 series
Technical Note 71 Assembly Instructions for SCA6x0 and SCA10x0 series TABLE OF CONTENTS Table of Contents...1 1 Objective...2 2 VTI'S DIL-8 and DIL-12 packages...2 3 Package Outline and Dimensions...2
More informationPLASTIC FURNITURE MANUFACTURING PROCESS I N T D F U R N I T U R E A N D F I T T I N G S
PLASTIC FURNITURE MANUFACTURING PROCESS I N T D 3 0 1 F U R N I T U R E A N D F I T T I N G S COMMON MANUFACTURING METHODS FOR PLASTIC FURNITURE 1. MOLDING 1. Extrusion molding 2. Injection molding 3.
More informationMIL- B Rev NAVSEA 0900-LP
I: REQUIREMENTS 1. Identify the standard the supplier uses for performing brazing. MIL- B-007883B OTHER (IF Other, Specify :) MIL- B-007883 Rev NAVSEA 0900-LP-001-7000 II: ATTRIBUTES: YES NO 2a. Does a
More information6043 DESIGN AND TECHNOLOGY
www.onlineexamhelp.com www.onlineexamhelp.com CAMBRIDGE INTERNATIONAL EXAMINATIONS GCE Ordinary Level MARK SCHEME for the October/November 2013 series 6043 DESIGN AND TECHNOLOGY 6043/01 Paper 1, maximum
More informationPrepared by Qian Ouyang. March 2, 2013
AN075 Rework Process for TQFN Packages Rework Process for TQFN Packages Prepared by Qian Ouyang March 2, 2013 AN075 Rev. 1.1 www.monolithicpower.com 1 ABSTRACT MPS proprietary Thin Quad Flat package No
More informationComparative Evaluation of Resistance Made Simple Shear Connection with Bolts and With Welding
International Journal of Engineering Inventions e-issn: 78-7461, p-issn: 319-6491 Volume 3, Issue 7 (February 014) PP: 1-5 Comparative Evaluation of Resistance Made Simple Shear Connection with Bolts and
More informationManufacturing Processes (continued)
Manufacturing (continued) Machining Some other processes Material compatibilities Process (shape) capabilities Manufacturing costs Correct pg 142, question 34i should read Fig 6.18 question 34j should
More informationBolted Joint Types Grip Washer
Structural Bolting The Research Council on Structural Connections (RCSC) prepares specifications and documents related to structural connections RCSC s Specification for Structural Joints Using ASTM A325
More informationDescribing Component shapes and features 5/9/2016. Prof. Hala J. El-Khozondar Spring Technical English Unit 3 Component and assemblies
Technical English Unit 3 Component and assemblies Prof. Hala J. El-Khozondar Spring 2016 Describing Component shapes and features Generated by Foxit PDF Creator Foxit Software Plugs and sockets: match
More informationFORM TP MAY/JUNE 2007
TEST CODE 01335020 FORM TP 2007107 MAY/JUNE 2007 CARIBBEAN EXAMINATIONS COUNCIL SECONDARY EDUCATION CERTIFICATE EXAMINATION MECHANICAL ENGINEERING TECHNOLOGY Paper 02 - Technical Proficiency 2 -y hours
More informationMIL- B B. MIL- B Rev NAVSEA 0900-LP II: ATTRIBUTES: YES NO N/A
XXVIII BRAZE/BRAZING PROCESS I: REQUIREMENTS 1. Identify the standard the supplier uses for performing brazing. MIL- B-007883B MIL- B-007883 Rev OTHER (IF Other, Specify :) NAVSEA 0900-LP-001-7000 II:
More informationManufacturing Process of the Hubble Space Telescope s Primary Mirror
Kirkwood 1 Manufacturing Process of the Hubble Space Telescope s Primary Mirror Chase Kirkwood EME 050 Winter 2017 03/11/2017 Kirkwood 2 Abstract- The primary mirror of the Hubble Space Telescope was a
More informationGreenfaulds High School
Greenfaulds High School Technical Department Standard Grade Craft & Design Knowledge & Understanding In Metal Page 1 Metals All metals in use today are either PURE METALS or ALLOYS. Copper, iron, tin,
More informationHand Torch or Flame Brazing Principles
Hand Torch or Flame Brazing Principles Introduction Hand-torch brazing is inexpensive and flexible, making it ideally suited to small production batches or production runs involving differing components.
More informationUnit 3. Engineering. Section 11. Engineering Processes LO3. AC3.1 AC3.2
Engineering Unit 3 Section 11 Engineering Processes LO3. AC3.1 AC3.2 Joining Materials Joints between materials can be temporary or permanent. Joints can be formed with adhesives, frame joints, brazed
More informationSMT Assembly Considerations for LGA Package
SMT Assembly Considerations for LGA Package 1 Solder paste The screen printing quantity of solder paste is an key factor in producing high yield assemblies. Solder Paste Alloys: 63Sn/37Pb or 62Sn/36Pb/2Ag
More informationInnovative Soldering Technology for new Material Combinations
13 th MST 4.0 Conference 20 th 21 st September 2016, Dortmund Innovative Soldering Technology for new Material Combinations Dr. Ino J. Rass, EUROMAT GmbH, Baesweiler b. Aachen Contents of Presentation
More informationCh 2: Manufacturing Operations
Ch 2: Manufacturing Operations Learning Objectives: By the end of the lecture the student should be able to: Explain the difference between technological and economical definition of manufacturing. Properly
More informationWhat is induction brazing
What is induction brazing United Induction Heating Machine Limited We are experienced in Induction Heating,induction heating machine,induction Heating equipment.they are widely used in induction heating
More informationLAMINEX manages to introduce PETG SPECTAR in to domestic and foreign markets, and has become the only extruder in Mexico.
PetG SPECTAR LAMINEX manages to introduce PETG SPECTAR in to domestic and foreign markets, and has become the only extruder in Mexico. Eastman is a global specialty chemical company that produces a broad
More informationFUNDAMENTAL MANUFACTURING PROCESSES Plastics Machining & Assembly
Copyright 2002 Society of Manufacturing Engineers --- 1 --- FUNDAMENTAL MANUFACTURING PROCESSES Plastics Machining & Assembly SCENE 1. CG: FBI warning white text centered on black to blue gradient SCENE
More informationVT-35 SOLDER PASTE PRINTING DEFECT ANALYSIS AND PREVENTION. Script Writer: Joel Kimmel, IPC
VIDEO VT-35 SOLDER PASTE PRINTING DEFECT ANALYSIS AND PREVENTION Script Writer: Joel Kimmel, IPC Below is a copy of the narration for the VT-35 videotape. The contents for this script were developed by
More informationSOLDERING. Understanding the Basics. Edited by Mel Schwartz. Materials Park, Ohio
SOLDERING Understanding the Basics Edited by Mel Schwartz ASM International Materials Park, Ohio 44073-0002 Copyright 2014 by ASM International All rights reserved No part of this book may be reproduced,
More informationPowder Actuated Fastening INTRODUCTION
Powder Actuated Fastening INTRODUCTION Powder actuated fastening systems provide a cost effective method of attaching fixtures for light duty, static load conditions. Powers' systems consist of specially
More informationPOTENTIAL HEALTH & SAFETY HAZARDS
Number: OH&S 18.50.1 Revision Date: 02/11/2015 Brazing Safe Work Procedures 1. PURPOSE 1.1. To provide safe work procedures and guidelines on brazing operations. 2. SCOPE 2.1 These procedures apply to
More informationPermanent fasteners: Riveted joints Welded joints Detachable joints: Threaded fasteners screws, bolts and nuts, studs. Cotter joints Knuckle joints
Instructional Objectives At the end of this lesson, the students should have the knowledge of Fasteners and their types: permanent and detachable fasteners. Different types of pin joints. Different types
More informationSECOND SEMESTER DIPLOMA EXAMINATION IN MECHANICAL ENGINEERING- MARCH, 2014 MANUFACTURING PROCESS PART-A
SECOND SEMESTER DIPLOMA EXAMINATION IN MECHANICAL ENGINEERING- MARCH, 2014 MANUFACTURING PROCESS PART-A 1. Give any two advantages of X-ray radiography over gamma ray radiography. X-ray radiography provides
More informationc. Pins, bolts, and retaining rings b. Washers, locking nuts, and rivets
62 20 HW 8: Fasteners / Force, Pressure, Density Mechanical Systems DUE Mon, 11/21/16 Start of class Check link on website for helpful fastener information Please use a scantron. Material is based primarily
More informationBrazing Technical Bulletin
No. T-13 Brazing Technical Bulletin Improvement of Joint Quality and Reduction of Flux Usage with Ag Based Handy One Products Lucas-Milhaupt, Inc. 5656 S. Pennsylvania Ave Cudahy, WI 53110 Phone: 414.769.6000
More informationExperimental Evaluation of Metal Composite Multi Bolt Radial Joint on Laminate Level, under uni Axial Tensile Loading
RESEARCH ARTICLE OPEN ACCESS Experimental Evaluation of Metal Composite Multi Bolt Radial Joint on Laminate Level, under uni Axial Tensile Loading C Sharada Prabhakar *, P Rameshbabu** *Scientist, Advanced
More informationTechnical Department
Technical Department Design & Manufacture Knowledge & Understanding In Metal Page 1 Metals All metals in use today are either PURE METALS or ALLOYS. Copper, iron, tin, lead, gold and silver are all examples
More informationAWS C3.9M/C3.9:2009 An American National Standard. Specification for Resistance Brazing
An American National Standard Specification for Resistance Brazing An American National Standard Approved by the American National Standards Institute July 30, 2008 Specification for Resistance Brazing
More informationSubject Index. Bearing damage, in bolted, composite-metal
STP927-EB/Nov. 1986 Subject Index A Adhesive binding, use in structural steel joints, 72-93 Adhesives creep strength, 76, 93 Versilok 204, 76 Aircraft crack failure in, 9-12, 37-38, 63-64, 95,118,222 crack
More informationINTRODUCTION. Tube and fitting
Service Application Manual SAM Chapter 630-41A Section 21 SOLDERING & BRAZING COPPER TUBE The Copper Development Association Inc. INTRODUCTION The material that follows is adapted from publications first
More informationExperiments on soldering printed circuit boards, with a new ecologic filler alloy
EUROPEAN UNION GOVERNMENT OF ROMANIA SERBIAN GOVERNMENT Structural Funds 2007-2013 Romania Republic of Serbia IPA Cross-border Cooperation Programme Project logo / LP logo Project: Promoting new ecologic
More informationVolume Control PJ AN
- AN Page 1 of 9 1. Handling Handle the VC by the body to avoid mechanical stress to the leads. 2. Tools Proper tools should be used for cutting and bending, such as sharp cutters and soft-sided tweezers.
More informationProfile Wrapping. TKH-Technical Briefing Note 6. Industrieverband Klebstoffe e.v. Version: March 2009
TKH-Technical Briefing Note 6 Profile Wrapping Version: March 2009 Published by Technische Kommission Holzklebstoffe (TKH) (Technical Committee on Wood Adhesives) of Industrieverband Klebstoffe e.v. (German
More informationWelded connections Welded connections are basically the same design in AISI as in AISC. Minor differences are present and outlined below.
Cold-Formed Steel Design for the Student E. CONNECTIONS AND JOINTS E1 General Provisions Connections shall be designed to transmit the maximum design forces acting on the connected members. Proper regard
More informationOur Top 10 Commonly Asked Soldering Questions This Year
Our Top 10 Commonly Asked Soldering Questions This Year 1 Chip Component Shifting Can be related to components floating on the molten solder plus the equipment may have vibrations, which may not be felt
More information(( Manufacturing )) Fig. (1): Some casting with large or complicated shape manufactured by sand casting.
(( Manufacturing )) Expendable Mold Casting Processes: Types of expendable mold casting are: 1 ) Sand casting. 2 ) Shell molding. 3 ) Vacuum molding. 4 ) Investment casting. 5 ) Expanded polystyrene process.
More informationInstallation Precautions
Installation Precautions 1. Lead orming (1) Avoid bending the leads at the base and ensure that the leads are fixed in place. (2) Bend the leads at a point at least 2mm away from the base. (3) orm the
More informationWelding-Oxy Fuel Metals Joining
Western Technical College 31442301 Welding-Oxy Fuel Metals Joining Course Outcome Summary Course Information Description Career Cluster Instructional Level Total Credits 1.00 Total Hours 36.00 Introduction
More informationApplication Note. Soldering Guidelines for Module PCB Mounting Rev 13
Application Note Soldering Guidelines for Module PCB Mounting Rev 13 OBJECTIVE The objective of this application note is to provide ANADIGICS customers general guidelines for PCB second level interconnect
More informationAssembly Guidelines Sterling Silver & MacStan Immersion Tin Coated PCB s
Assembly Guidelines Sterling Silver & MacStan Immersion Tin Coated PCB s By: MacDermind Final Finish Team MacDermid Inc. Flat solderable surface finishes are required for the increasingly dense PCB designs.
More informationClass AB stereo headphone driver
FEATURES Wide temperature range No switch ON/OFF clicks Excellent power supply ripple rejection Low power consumption Short-circuit resistant High performance high signal-to-noise ratio high slew rate
More informationB. Flip-Chip Technology
B. Flip-Chip Technology B1. Level 1. Introduction to Flip-Chip techniques B1.1 Why flip-chip? In the development of packaging of electronics the aim is to lower cost, increase the packaging density, improve
More informationModule 4 Design for Assembly IIT BOMBAY
Module 4 Design for Assembly Lecture 8 Case Studies - IV Instructional objectives The objective of this lecture is to exhibit how real components are designed in industry following some of the principles
More informationRB&W. GLOBAL LIGHTWEIGHT MATERIAL PRESENTATION April 14, SPAC Applications 1
RB&W GLOBAL LIGHTWEIGHT MATERIAL PRESENTATION April 14, 2015 SPAC Applications 1 Global Market Trend CO2 Emission Fuel Efficiency Vehicle Weight Reduction INCREASED USAGE High Strength Steels Aluminum
More informationTransistor Installation Instructions
INTRODUCTION When inserting high power RF transistor packages into amplifier circuits there are two important objectives. Firstly, removing heat and, secondly, providing a longterm reliable solder joint
More informationTest methods for lead-free solders- Part 5 : Methods for tensile tests and shear tests on solder joints
IS JAPANESE STRIAL STANDARD Translated and Published by Japanese Standards Association Test methods for lead-free solders- Part 5 : Methods for tensile tests and shear tests on solder joints ICs 25.160.50
More informationEUROPEAN ADHESIVE ENGINEER
I03 NATIONAL ADAPTATION AND TRANSLATION OF THE CURRICULA EUROPEAN ADHESIVE ENGINEER MODULE 3.4 HYBRID JOINTS ERASMUS + REFERENCE 2015 -I- PT 01- KA202-012915 This project has been co-funded with support
More informationMedical secondary operations guide
Medical secondary operations guide Contents Methods for joining/bonding.................... 3 Chemical............................. 3 Thermal................................. 3 Mechanical...............................
More informationDESIGN AND TECHNOLOGY 6043/01 Paper 1 Technology For Examination from 2016 SPECIMEN MARK SCHEME 2 hours 30 minutes MAXIMUM MARK: 100
Cambridge International Examinations General Certifi cate of Education Ordinary Level DESIGN AND TECHNOLOGY 6043/01 Paper 1 Technology For Examination from 2016 SPECIMEN MARK SCHEME 2 hours 30 minutes
More informationA Practical Update on Advanced Copper Alloys and On-Site Joining Methods for HVACR Systems. Educate Promote Defend Support Inspire
A Practical Update on Advanced Copper Alloys and On-Site Joining Methods for HVACR Systems A Practical Update on Advanced Copper Alloys and On-site Joining Methods for HVACR Systems Presented by: John
More information3M Dual Lock Reclosable Fasteners
3M Dual Lock Reclosable Fasteners 3M 2011. All Rights Reserved. Agenda Features & Advantages Performance Characteristics Stem Densities Stem Combinations Products Design Considerations Key Design Parameters
More informationPanel fencing system 2D 6/5/6
tel.: +8 7 2 2 mobile: +8 09 9 e-mail: kontakt@ Panel fencing system 2D // fencing panels tel.: +8 7 2 2 mobile: +8 09 9 e-mail: kontakt@ type 2D H H Panel height 0 80 00 20 0 0 80 200 220 20 Horizontal
More informationSECTION SHEET METAL FLASHING AND TRIM
SECTION 07620 PART 1 - GENERAL 1.1 SUMMARY A. Section Includes: 1. Formed roof drainage sheet metal fabrications. 2. Formed low-slope roof sheet metal fabrications. 1.2 SUBMITTALS A. Shop Drawings: Show
More informationPAGE 1/6 ISSUE SERIES Micro-SPDT PART NUMBER R516 XXX 10X. (All dimensions are in mm [inches]) R 516 _ 1 0 _
PAGE 1/6 ISSUE 15-10-18 SERIES Micro-SPDT PART NUMBER R516 XXX 10X R516 series: the RAMSES concept merges with the SLIM LINE technology, breaking up the frequency limits of SMT switches : - FULL SMT TECHNOLOGY
More informationHigher Product Design
Higher Product Design Processes Processes Methods of joining Click on appropriate star Processes Wood processes Metal processes Plastic processes Click on appropriate star Wood processes Laminating Routing
More informationSmithing force is applied to manipulate the metal Forging force is applied to manipulate the metal
FORGING Smithing It is a process of performing various operations on relatively small work pieces, heated in an open fire (hearth) and force is applied to manipulate the metal by means of hand hammers
More informationOroville Union High School District Industrial Technology
Oroville Union High School District Industrial Technology Industrial Technology - ROP Fabrication ROP Fabrication COURSE TITLE: ROP Fabrication LENGTH OF COURSE: One Year (2 hours per day) GRADE LEVEL:
More informationForming and Assembling Pipework Systems F/508/4663
Unit Title Ofqual unit reference number (code) Organisation Reference Forming and Assembling Pipework Systems F/508/4663 QU051481 Unit Level Level 2 Unit Sub Level None GLH 64 Unit Credit Value 14 Sector
More information9/8/98 AC B CAUTION THE FOLLOWING TORQUE VALUES ARE DERIVED FROM OIL FREE CADMIUM PLATED THREADS.
TABLE 7-1. Recommended torque values (inch-pounds). CAUTION THE FOLLOWING TORQUE VALUES ARE DERIVED FROM OIL FREE CADMIUM PLATED THREADS. TORQUE LIMITS RECOMMENDED FOR INSTAL- LATION (BOLTS LOADED PRIMARILY
More informationCeramic Monoblock Surface Mount Considerations
Introduction Technical Brief AN1016 Ceramic Monoblock Surface Mount Considerations CTS ceramic block filters, like many others in the industry, use a fired-on thick film silver (Ag) metallization. The
More information1. Enumerate the most commonly used engineering materials and state some important properties and their engineering applications.
Code No: R05310305 Set No. 1 III B.Tech I Semester Regular Examinations, November 2008 DESIGN OF MACHINE MEMBERS-I ( Common to Mechanical Engineering and Production Engineering) Time: 3 hours Max Marks:
More information