The BEECK Product Range

Transcription

1 The BEECK Product Range Valid from 01/04/2014

2 Reference: Theatre stairwell in the Staatstheater Meiningen Content What is BEECK? 4 BEECK Mineral Paint Façade 8 Pure Crystalline Finish 9 Powdered Pigment 9 Fixative 10 Beeckosil Fine 10 Beeckosil Coarse 11 Full Colour Silicate Paint 11 Beecko-SOL Fine 12 Beecko-SOL Coarse 13 Concrete/Stone Glaze 14 Renosil Fine 14 Renosil Coarse 15 Universal Full Colour Silicate 15 BEECK Mineral Paints in Interiors 16 Maxil 17 Maxil Primer Fine 17 Maxil Primer Coarse 18 Insil 18 Quartz Paint 19 Protect Fine 19 Protect Coarse 20 Protect Full Colour Paint 20 Protect Primer 22 Kasolit Fine 22 Kasolit Coarse 23 Casein Primer 23 Lime Casein Paint 24 Soaked Marble Lime 25 Calcidin 26 Calcidan 26 Full Colour Lime Concentrate 27 BEECK Silicate Primers 28 Fixative 29 MBA-Fixative 29 Quartz Filler 30 Quartz Filler P 30 Bonding Coat Fine 32 Bonding Coat Coarse 32 Silane Primer 33 BEECK Building Preservatives 34 Silicone Plus 34 Natural Stone Hardener OH 35 Silane Primer 36 BEECK Auxiliaries 38 Etching Fluid 39 Paint Stripper 39 Fungicide 40 BEECK Stand Oil Paints 42 Exterior Stand Oil Paint 43 Interior Stand Oil Paint Satin Matt 43 Interior Stand Oil Paint Glossy 44 Oil Primer 45 Undercoat 46 Corrosions Protection Primer 46 Lacquer Thinner 47 BEECK Stand Oil Wood Glazes 48 Exterior Stand Oil Wood Glaze 49 Interior Stand Oil Wood Glaze 49 Oil Primer 50 BEECK Tools 52 Mineral Paint Brush 53 Oval Brush 53 Flat Brushes 53 BEECK Mineral Colour Chart 54 Mineral Colour Chart 54 Price groups 54 Miscellaneous 55 Soft Shell Activity Jacket 55 Content 3

3 What is BEECK? What is BEECK? / BEECK ASF What is BEECK? BEECK schen Farbwerke introduces itself. In 1894, the company founder Ludwig Beeck established his business in Breslau with the development and production of pure active silicification mineral paints based on water glass. He achieved inseparable bonding between the coating and microporous substrate with BEECK Pure Crystalline Finish, a mineral paint system suited for particularly valuable historical building materials in interior and exterior areas. These original formulae are still used today for the conservation of built heritage and impress with their large colours diversity and their enormous durability. Ecology Pure mineral paints are natural mineral paints. Obtained from practically unlimited resources of raw mineral materials, they are integrated in material cycles. Free from solvents, plasticisers and biocides, they enable a healthy living environment. A new and less expensive product category, synthetic resin emulsion paint, meant hard times for a resolute mineral paint manufacturer during the construction boom of the 1950s and 1960s. Mineral paints were nearly forgotten and structural damage caused by the improper use of synthetic resins on porous mineral building materials increased. Despite the clear trend towards synthetic resin emulsion paints, BEECK schen Farbwerke remained true to the development and production of pure, natural coating systems. Based on its experience with pure mineral paints made of lime and water glass, the company invested in developing pure plant-based paints. The AGLAIA Natural Paints brand created in 1968 has rounded off the BEECK product portfolio meaningfully ever since then. The following owner, Gerhard Osterle, as a specialist in mineral and natural paints, also especially dedicated himself to their continued development. With the construction of the new production facility in 1972 in Laichingen, in the Swabian Alp region, he invested in modern machines, an in-house development and application laboratory and outstanding specialists as the most important knowledge carriers. H 2 O K 2 SiO 3 Potassium silicate K2SiO 3 x H 2 O Potassium water glass BEECK FIXATIVE Mineral pigments, quartz, lime BEECK POWDERED PIGMENTS BEECK PURE CRYSTALLINE FINISH Silicification BEECK PURE CRYSTALLINE FINISH CYCLE CO 2 SiO 2 xh 2 O+K 2 CO 3 Silica gel, Silicified silicate coating The tradition of building had changed in the past decades, and with it came new requirements for high quality and modern coating materials. Since the company was founded, work had been consistently carried out using natural raw materials such as beeswax, linseed oil, dammar and paracasein. To this day, BEECK offers a selected paint product range, which satisfies the highest standards. CO ϒ C Washing + grinding Bronzing BEECK sche Farbwerke plant-based and mineral natural paints from a single source! Service Quality in materials, substrates and use is prerequisite for a coating to become what it should be a success for skilled trades workers, owners or developers and designers. BEECK offers its whole range of services for the success of the customer, from competent substrate evaluation and preparation of work recommendations to detailed tender specification texts and estimating. SiO 2 + K 2 CO 3 Quartz sand + potash Minerals References Nothing is more convincing than decades of clean and brilliantly beautiful façades that is the standard with BEECK Mineral Paints! Built heritage conservation BEECK has stood for top quality lime and soluble water paints suited for use on historical building materials for more than 120 years. Proven on critical substrates of listed buildings, on which synthetic resin bonded systems frequently fail. Economic efficiency The cheerful character, the play of colours and the lightfastness of the pure mineral pigmentation enhance the status of each building for many decades. This unsurpassed durability of BEECK Mineral Paints makes their use maintenance friendly and therefore economical. Building physics The capillary-active coatings have ideal open porosity, and are therefore extremely valuable in building physics terms. Thanks to silicification they form an inseparable mineral unit with the render, do not tend to flake and also do not form a vapour-tight, high-tension rind in when renovated. This open porosity also ensures a balanced, healthy living room climate. The high alkalinity of the coatings has a mould resistant and bactericidal effect. Free from solvents, plasticisers, biocides and preservatives they fulfil the strictest room air hygiene requirements. BEECKASF ActiveSilicateFormulation Silicification the microporous, inseparable unity of substrate and active silicate coating! Ideal building physics properties combined with extreme durability, the secret of true silicate coatings. Resistant to UV radiation as well as organic solvents and paint strippers. Weathering caused by weak chalking with active self-cleaning effect. Innovation The advantages of mineral coatings cannot just be used on traditional building materials but also on composite materials and lightweight building components. A wide range of primers also opens up their use on substrates with weak silicification. Aesthetics In aesthetic terms the matt coatings are unsurpassably attractive, especially in the modern ambience too. Traditional coating materials such as lime wash paints are especially compatible with historically valuable wall building materials such as air-lime plaster, clay or loam and natural stone. Reversible coatings and casein paints, with their vital character and blaze of colour are also firmly anchored in restoration and church painting, and lend every listed building a very special aura. Film formation with commonly used emulsion, silicone resin and passive silicate paints. Organic synthetic resin bonds the surface of the building material with pigments and extenders. This is disadvantageous from a building physics point of view, because it has a negative effect on diffusion. Film-forming coatings also tend to become brittle and flake, causing the façade coating to become an expensive dead-end after only a few renovation intervals. Is this practice the high art of the painting and decorating trade? Real mineral paint Emulsion paint resistant to stripping! detaches as a film 4 What is BEECK? /ASF What is BEECK? /ASF 5

4 Reference: Wilhelma-Theater in Stuttgart The BEECK product range The BEECK product range The BEECK product range fully developed mineral coating solutions to meet the highest standards BEECK Pure Crystalline Finish Pure two-pack silicate paint to VOB/C DIN , to be prepared by mixing BEECK Fixative and BEECK Powdered Pigment. Unsurpassed durability; aesthetic and colourfast. Beeckosil One-pack active silicate paint for mineral façade substrates; conforms to VOB/C DIN Extremely water vapour permeable and weather and UV resistant. BEECK Renosil Efficient renovation coating for synthetic resin coated façades and external thermal insulation composite systems (ETICS). Remineralised with optimum light and UV resistance. BEECK Concrete / Stone Glaze Semi-transparent active silicate glaze for mineral plaster, fair-faced concrete and natural stone in interior and exterior areas. BEECK Maxil User-friendly, highly opaque and efficient interior silicate paint to VOB/C DIN Pretreatment of gypsum substrates with BEECK Maxil Primer Fine / Coarse. BEECK Silicone Plus Highly alkali-resistant, water-repellent long-term preservation of mineral façades. Ideal for concrete, mineral render, opaque and glazed active silicate coatings. BEECK Mineral Paint Colour Chart 200 attractive mineral paint colours allow you to choose with confidence. The statements made in this brochure reflect our knowledge and practical experience. Subject to change without notice as part of our product development. Please find out more by referring to our current Technical Data Sheets and Safety Data Sheets under This brochure becomes invalid automatically when a new edition is published. Dated: 04 / 2014 BEECK Quartz Filler Fibre-reinforced, natural white priming coat for bridging over hairline cracks and minor structural defects in interior and exterior areas. BEECK Stand Oil Paints / Stand Oil Wood Glazes Classic oil paints for opaque and glazed wood coatings, for example, on half-timbering. Maintenance-friendly, true to historical linseed oil coatings, they are not prone to flaking, even under intense weathering. 6 What is BEECK? What is BEECK? 7

5 BEECK Mineral Paint Façade BEECK Mineral Paint Façade + Pure Crystalline Finish Pure two-pack active silicate paint to VOB/C DIN Unsurpassed in durability, water vapour permeability and ecological compatibility. To be mixed from BEECK Powdered Pigment and BEECK Fixative. Free from organic contents, in particular synthetic resins of all types. Opaque or glazed use on absorbent porous mineral plaster is possible. - Maximum colourfastness A1 (BFS-MB No. 26) - Mineral matt finish - Free from resins, solvents and biocides White, Off-White and the 200 colours of the BEECK Mineral Colour Chart including full colours. 1 kg / 5 kg / 10 kg / 30 kg (BEECK Fixative) and 4 kg / 8 kg / 25 kg (BEECK Powdered Pigment) - Can be repeatedly renovated - Ecologically compatible - Ideal building physics properties W 24 value: > 1.00 kg /(m 2 h 1/2 ) < 0.01 m 1.55 kg / L Organic content: 0 % approx kg BEECK Fixative and 0.15 kg BEECK Powdered Pigment per m 2 BEECK Mineral Paint Façade For more than 100 years, BEECK has stood for mineral coatings of unsurpassed durability thanks to the BEECK ActiveSilicateFormulation ASF. Their cheerful character, the play of colours of the highly porous surface and the lightfastness of the purely mineral pigmentation enhance the status of each building for decades. Façades with mineral coatings not only stand clean and free from algae for a long time, they also age with dignity. The coatings are capillary-active and have ideal open porosity, and are therefore extremely valuable in building physics terms. Thanks to silicification they form an inseparable mineral unit with the render, do not tend to flake and also do not form a vapour-tight, high-tension rind in when renovated. The extensive range of BEECK silicate paints provides the ideal economic coating solution for every requirements, whether historical render façade, external thermal insulation composite system, new build or renovation. Reference: Residential building in Landshut Powdered Pigment Tinted powder component in the BEECK Pure Crystalline Finish system Pure mineral powdered component, which when mixed with BEECK Fixative results in the pure two-pack silicate paint BEECK Pure Crystalline Finish to VOB/DIN Free from organic content. Unsurpassed silicification action, durable and maintains value with ideal building physics properties. - Maximum colourfastness A1 (BFS-MB No. 26) - Opaque and glazing - Can be repeatedly renovated White, Off-White and the 200 colours of the BEECK Mineral Colour Chart including full colours. 4 kg / 8 kg / 25 kg W 24 value: > 1.00 kg/(m 2 h 1/2 ) < 0.01 m 1.55 kg/l Organic content: < 0 % approx kg/m² - Timeless matt aesthetics - Colour pallet suitable for listed buildings lightfast colours - Contains no solvents or VOCs 8 BEECK Mineral Paint Façade BEECK Mineral Paint Façade 9

6 BEECK Mineral Paint Façade BEECK Mineral Paint Façade Potassium water glass as binder, free from organic content to VOB/DIN Primer and thinner for BEECK Silicate Paints. Forms an inseparable microporous unit by means of silicification with the mineral substrate such as plaster, natural stone or concrete. As a strengthening primer for absorbent, chalking and crumbling substrates. Levelling, quartz-filled priming and intermediate coat in the Beeckosil system on substrates with minor structural defects or hairline cracks. Thinning with BEECK Fixative. Ready-touse paste. Same colour topcoat with Beeckosil Fine. Use render to repair façades with cracks, chipped surface or structural defects and slurry uniformly with BEECK Quartz Filler. - Pure mineral - Ideal building physics properties - Moisture regulating - UV resistant - Optimum long lives - Full building biology compatibility - BEECK ASF ActiveSilicateFormulation - Texture grain 0.4 mm - Bridges over hairline cracks and levelling effect - Brightens up smooth surfaces - Non film-forming - Optimum silicification with substrate and topcoat Fixative Priming and binder for BEECK Silicate Paints including BEECK Pure Crystalline Finish Colourless / transparent 1 kg / 5 kg / 10 kg / 30 kg Beeckosil Coarse Fine slurry base coat in the active silicate system to VOB/DIN White, Off-White and the 200 ready-mixed colours of the BEECK Mineral Colour Chart. Same colour topcoat in Beeckosil Fine. 8 kg / 20 kg BEECKASF ActiveSilicateFormulation W 24 value: > 1.00 kg/(m 2 h 1/2 ) W 24 value: < 0.08 kg / (m 2 h 1/2 ) < 0.01 m < 0.02 m 1.16 kg / L 1.58 kg / L Organic content: 0 % Organic content: < 5 % approx kg / m² on a smooth substrate for priming approx kg / m² on a smooth substrate Ready-to-use one-pack water-glass paint with an absolutely mineral profile. For permanently representative façades made of render, brick, calcium silicate masonry and concrete. Thin with BEECK Fixative. Use BEECK Quartz Filler, alternatively Beeckosil Coarse, to apply a slurry base coat to substrates with hairline cracks and structural defects. Active silicate paints with pure mineral pigmentation to VOB/DIN for individual tinting of BEECK one-pack silicate paints such as Beeckosil, BEECK Concrete/Stone Glaze or BEECK Quartz Paint. Also for full colour decorative painting, stencil techniques and labelling in interior and exterior areas. Beeckosil Fine One-pack active silicate system to VOB/DIN BEECKASF ActiveSilicateFormulation - BEECK ASF ActiveSilicateFormulation - Maximum colourfastness A1 (BFS-MB No. 26) - Moisture regulating White, Off-White and the 200 ready-mixed colours of the BEECK Mineral Colour Chart. Tintable and full colour coatings with BEECK Full Colour Silicate Paints. 5 L / 12.5 L / 15 L - Non film-forming - Economical to use Full Colour Silicate Paint For tinting BEECK one-pack silicate paints and for full colour painting and decorating BEECKASF ActiveSilicateFormulation - BEECK ASF ActiveSilicateFormulation - Maximum colourfastness A1 (BFS-MB No. 26) - Pure inorganic pigmentation - Unlimited lightfastness and UV resistance Black, Umber, Ochre Yellow, Maize Yellow, Lemon Yellow, Green, Cobalt Blue, Ultra Blue, Wine Red, Oxide Red and Brown, see BEECK Mineral Colour Chart. Can be mixed as required with Beeckosil, BEECK Concrete / Stone Glaze or BEECK Quartz Paint White L / 5 L / 12.5 L - Non film-forming - Ready-to-use - One year shelf life - Thin with BEECK Fixative W 24 value: < 0.08 kg/(m 2 h 1/2 ) W 24 value: < 0.08 kg / (m 2 h 1/2 ) < 0.02 m 0.03 m 1.50 kg / L kg / L Organic content: < 5 % Organic content: < 5 % approx L / m² on a smooth substrate approx L / m² on a smooth substrate 10 BEECK Mineral Paint Façade BEECK Mineral Paint Façade 11

7 Reference: German school in Peking BEECK Mineral Paint Façade BEECK Mineral Paint Façade Silica-sol silicate system for universal use on lime and cement render, concrete and ETICS façades, also for renovating weathered, matt emulsion and silicone resin coatings. Thin with BEECK Fixative. Use BEECK Quartz Filler, alternatively Beecko-SOL Coarse, to precoat substrates with hairline cracks and structural defects. Levelling primer coat on lime and cement render, concrete and ETICS façades, and for renovating weathered, matt emulsion and silicone resin coatings. Covers localised hairline cracks, precoat critical substrates with greater structural defects with BEECK Quartz Filler. Topcoat: in the same colour with Beecko-SOL Fine. Beecko-SOL Fine Sol-silicate paint for mineral and for synthetic resin coated façades. Fulfils VOB/C DIN BEECKASF ActiveSilicateFormulation - BEECK ASF ActiveSilicateFormulation - Highly adherent even on synthetic-resin based substrates - Non film-forming White, Off-White and the 200 ready-mixed colours of the BEECK Mineral Colour Chart. Tintable pastel colour and full colour coatings with BEECK Universal Full Colour Silicate. Size 5 L / 15 L - Highly water vapour permeable - Maximum colourfastness A1 (BFS-MB No. 26) Beecko-SOL Coarse Slurry primer coat in the Beecko- SOL system for façades. Fulfils VOB/C DIN BEECKASF ActiveSilicateFormulation - BEECK ASF ActiveSilicateFormulation - Levels out hairline cracks and minormängel structural defects - Highly adherent even on synthetic-resin based substrates White, Off-White and the 200 ready-mixed colours of the BEECK Mineral Colour Chart. Tintable pastel colour and full colour coatings with BEECK Universal Full Colour Silicate. Size 8 kg / 20 kg - Texture grain 0.4 mm - Highly water vapour permeable - Low tension W 24 value: < 0.08 kg / (m 2 h 1/2 ) / Class W 3 W 24 value: 0.08 kg /(m 2 h 1/2 ) / Class W m / Class V kg / L Organic content: < 5 % approx kg / m² on a smooth substrate 0.01 m / Class V kg / L Organic content: < 5 % approx L / m² on a smooth substrate 12 BEECK Mineral Paint Façade BEECK Mineral Paint Façade 13

8 BEECK Mineral Paint Façade BEECK Mineral Paint Façade One-pack, glazed pigmentation silicate system to VOB/DIN For creative, colour glazed design of rendered façades and fair-faced concrete. For retouching and freshening up natural stone and brick during stone restoration work on listed buildings. Fair-faced stone glazing is possible or pretreatment with BEECK Quartz Filler. Coarse-grained primer and intermediate coating on ETICS, synthetic resin plasters and firm old emulsions with minor structural defects or hairline cracks. Ready-to-use, to be applied as thorough slurrying coat using the Mineral Paint Brush. Same colour topcoat with BEECK Renosil Fine. Apply render to façades with severe cracking or defects. Concrete / Stone Glaze Semi-transparent active silicate glaze for mineral surfaces - BEECK ASF ActiveSilicateFormulation - Maximum colourfastness A1 (BFS-MB No. 26) - Polychrome and monochrome White, Off-White and the 200 colours of the BEECK Mineral Colour Chart including full colours. Tintable with BEECK Full Colour Silicate Paints. 1 L / 5 L / 12.5 L - Thin with BEECK Fixative / water 1:1 - Extremely high yield Renosil Coarse Fine slurry base coat in the BEECK Renosil system - Grading curve with texture grain 0.4 mm - Bridges over hairline cracks - Levels out structural defects White, Off-White and the 200 ready-mixed colours of the BEECK Mineral Colour Chart. Tintable with BEECK Universal Full Colour Silicate. Same colour topcoat in BEECK Renosil Fine. 8 kg / 20 kg - Diffused light effect - Optimum bond - Thin with BEECK Fixative BEECKASF ActiveSilicateFormulation W 24 value: < 0.08 kg/(m 2 h 1/2 ) < 0.02 m 1.35 kg / L Organic content: < 5 % W 24 value: < 0.10 kg /(m 2 h 1/2 ) 0.07 m 1.58 kg / L approx kg / m² on a smooth substrate approx L / m² on a smooth substrate Renosil Fine Efficient silicate-based renovation coating for remineralising surfaces Water-thinnable, open-pored silicate system for universal use on external thermal insulation composite systems (ETICS), thin-layer renders and synthetic resin renders. Also for renovating adherent, firm emulsion coatings. - Can be used directly without a bonding agent - Efficient and universal - Water-thinnable White, Off-White and the 200 ready-mixed colours of the BEECK Mineral Colour Chart. Tintable and full colour coatings with BEECK Universal Full Colour Silicate 5 L / 12.5 L - Free from solvents - UV resistant and lightfast - Does not flake Universal Full Colour Silicate Lightfast full colour and tinting paint for BEECK Renosil, BEECK Maxil or BEECK Beecko-SOL Full colours, capable of silicification, for tinting BEECK Renosil, BEECK Maxil and BEECK Beecko-SOL. Also for full colour coatings and decorative painting in the respective system, in interior and exterior areas on uniform, prepared substrates. Maximum colourfastness A1 to BFS- MB No. 26. Avoid full colour coatings on sunlit external thermal insulation composite systems (ETICS) due to the heating effect (HBZ > 40). - Maximum colourfastness A1 (BFS-MB No. 26) - Efficient for shading - Water thinnable - Solvent free - Creative Specification to EN Wet-scrub resistance class 2 - Hiding power class 1 to 2 Black, Umber, Ochre Yellow, Maize Yellow, Lemon Yellow, Green, Cobalt Blue, Ultra Blue, Wine Red, Oxide Red and Brown, see BEECK Mineral Colour Chart. Can be mixed as required with BEECK Renosil, BEECK Maxil and BEECK Beecko-SOL, White L / 5 L / 12.5 L W 24 value: < 0.12 kg / (m 2 h 1/2 ) W 24 value: < 0.20 kg / (m 2 h 1/2 ) 0.08 m 0.08 m 1.45 kg / L kg / L approx L / m² on a smooth substrate approx L / m² on a smooth substrate 14 BEECK Mineral Paint Façade BEECK Mineral Paint Façade 15

9 BEECK Mineral Paints in Interiors BEECK Mineral Paints in Interiors Open-pored mineral coating for visually appealing interior walls made of plaster, gypsum board and fabric wallpaper. Also on smooth and white plasters under critical building and light conditions in representative rooms. Apply an undercoat of BEECK Maxil Primer, Fine or Coarse to critical substrates and gypsum board. - Premium quality - Tried and tested on buildings - Extremely economic - Maximum colourfastness A1 (BFS-MB No. 26) - Streak-free use Maxil Highly opaque interior silicate paint to VOB/C DIN for ambitious room design Specification to EN Wet-scrub resistance class 2 - Hiding power class 1 White, Off-White and the 200 ready-mixed colours of the BEECK Mineral Colour Chart. Tintable and full colour coatings with BEECK Universal Full Colour Silicate. 5 L / 15 L W 24 value: < 1.00 kg /(m 2 h 1/2 ) 0.02 m 1.46 kg / L Organic content: < 5 % approx L / m² on a smooth substrate Solvent free primer without texture grains for critical interior substrates with weak silicification. Suitable for gypsum, gypsum board and synthetic resin plasters and for firm, adherent emulsion-based existing paint coatings. - Levels out substrate effects - High hiding power - Efficient - Silicification bridge BEECK Mineral Paints in Interiors The advantages of mineral coatings can also be used outstandingly well in interiors. Their open porosity ensures a balanced, healthy living room climate. The high alkalinity of the coatings has a mould resistant and bactericidal effect. Free from solvents, plasticisers, biocides and preservatives they fulfil the strictest room air hygiene requirements. In aesthetic respects the matt coatings are unsurpassedly attractive, especially in a modern ambience on substrates such as gypsum board and nonwoven wall covering. Traditional coatings such as lime wash paints are especially compatible with historically valuable wall materials such as air-lime plaster, clay or loam and natural stone. In restoration and church painting, reversible coatings and casein paints with their cheerful appearance and blaze of colour are also securely anchored and lend each listed building a very special aura. Reference: Griesbachsches Haus of Friedrich-Schiller University Jena Maxil Primer Fine Highly opaque, white primer coating in the BEECK Maxil system Specification to EN Wet-scrub resistance class 3 - Hiding power class 2 White 5 L / 12.5 L W 24 value: 0.12 kg /(m 2 h 1/2 ) 0.10 m 1.60 kg / L ph value: 9 approx L / m² on a smooth substrate 16 BEECK Mineral Paints in Interiors BEECK Mineral Paints in Interiors 17

10 BEECK Mineral Paints in Interiors BEECK Mineral Paints in Interiors Opaque white textured coating for brush or roller application in the BEECK Maxil system. Brightens up the surface of smooth substrates made of gypsum or light-weight building board and levels out structural defects and hairline cracks. Ensure uniform particle-size distribution in streaked light and apply seamlessly. Extremely water vapour permeable, active silicate paint to VOB/C DIN for porous mineral substrates, especially lime plasters. Ideal for historical, repre-sentative buildings, even under critical building physics conditions. Timelessly authentic, mineral aesthetics. Thin with BEECK Fixative. Maxil Primer Coarse Slurry primer for further treatment with BEECK Maxil - Grading curve with coarse grain 0.4 mm - Fine plaster-like surface - Easy to use White 8 kg / 20 kg Quartz Paint Silicification active, water vapour permeable, interior silicate paint for historical interiors - BEECK ASF ActiveSilicateFormulation - Maximum colourfastness A1 (BFS-MB No. 26) - Moisture regulating Specification to EN Wet-scrub resistance class 2 - Hiding power class 2 - Matt with lustred lime effect - Can be repeatedly renovated - Free from solvents White, Off-White and the 200 ready-mixed colours of the BEECK Mineral Colour Chart. Tintable pastel colour and full colour coatings with BEECK Full Colour Silicate Paints. BEECKASF ActiveSilicateFormulation 5 L / 12.5 L W 24 value: 0.15 kg / (m 2 h 1/2 ) W 24 value: > 1.00 kg / (m 2 h 1/2 ) 0.09 m < 0.02 m 1.53 kg / L 1.54 kg / L approx kg / m² on a smooth substrate Organic content: < 5 % approx L / m² on a smooth substrate Insil Solvent free, open-pored interior silicate paint for living areas and commercial premises Ready-to-use interior silicate paint to VOB/C DIN for all firm interior substrates such as lime plasters, concrete, fabric and wood chip wallpapers. - Universal use - Easy to use Specification to EN Wet-scrub resistance class 3 - Hiding power class 2 White, Off-White Tintable pastel colour with BEECK Full Colour Silicate Paints. 5 L / 12.5 L - Free from solvents - Valuable room climate properties Protect Fine Reversible protective coating for historical interiors Highly water vapour permeable topcoat, white or tinted. For the protection of historical substrates, especially for wall paintings and colour façades in the preservation of listed buildings. Abrasion resistant and free from chalking. Can be renovated and painted over (not with lime wash paint!) in the system as often as required, can be gently removed at any time from water-resistant (!) historical substrates using water. - Can be removed again - One-pack - User friendly Specification to EN Hiding power class 1 - Mineral matt - Non vapour retarding White, Off-White and the 200 ready-mixed colours of the BEECK Mineral Colour Chart. Tintable and full colour coatings with BEECK Protect Full Colour Paint. 5 L / 12.5 L W 24 value: 0.20 kg/(m 2 h 1/2 ) W 24 value: > 1.00 kg / (m 2 h 1/2 ) < 0.02 m 0.03 m 1.43 kg / L 1.58 kg / L ph value: 9 Organic content: < 5 % approx L / m² on a smooth substrate approx L / m² on a smooth substrate 18 BEECK Mineral Paints in Interiors BEECK Mineral Paints in Interiors 19

11 BEECK Mineral Paints in Interiors Protect Coarse Slurry primer coating in the BEECK Protect system Fine grained, reversible primer and intermediate coating, white, for further treatment with BEECK Protect Fine. As a slurry base coat especially for historical substrates with structural defects, spot repairs and crazing. To be applied evenly and seamlessly with the Mineral Paint Brush. - Texture grain 0.4 mm - Opaque white White 8 kg / 20 kg - Levelling effect - Can be removed again W 24 value: > 1.00 kg /(m 2 h 1/2 ) 0.02 m 1.70 kg / L ph value: 9 approx kg / m² on a smooth substrate Südthüringer Staatstheater Meiningen The Task In 2010 the main building was generally modernised, which also included a new colour scheme for the entire interior design. The auditorium with the flat dome, the foyer and the staircases were all included in the redesign. The aim was to draw up a coherent colour and surface concept, appropriate for the building s cultural history significance. The effect of the coating systems used and the interaction of the different surfaces had to produce an authentic and period style image. Good building physics properties and a high degree of robustness were also required, not only to ensure high value stability, but also to ensure economic maintenance. The Project Stages First, extensive restoration work was carried out to check and to secure old findings and to compile a coherent and fine colour concept. Based on this, the lead restorer then created extensive sample areas ( Musterachsen ) in which to carry out tests and sample coatings, which ultimately led to the decision regarding the paint systems to be used not only with regard to technology but also the colour. The responsible firm of architects, the restorer and the responsible consultant of BEECK schen Farbwerke provided advice and documented the precise implementation of the largely very sophisticated coating work. Protect Full Colour Paint Lightfast full colour and tinting paint for BEECK Protect Purely mineral pigmented full colour paints in the BEECK Protect system. For individual shading of BEECK Protect Fine and Coarse. Also as a full colour coating for decorative painting and trompe l oeil. The primer coating should be applied to historical substrates in White (coarse or fine) to ensure better removability. - Maximum colourfastness A1 (BFS-MB No. 26) - Colour pallet suitable for listed buildings Black, Umber, Ochre Yellow, Maize Yellow, Lemon Yellow, Green, Cobalt Blue, Ultra Blue, Wine Red, Oxide Red and Brown, see BEECK Mineral Colour Chart. Can be mixed as required with BEECK Protect Fine, White L / 5 L / 12.5 L W 24 value: > 1.00 kg /(m 2 h 1/2 ) 0.03 m kg / L ph value: L / m² on a smooth substrate - Abrasion resistant and free from chalking - Can be painted over in the system - High hiding power and colouring capacity The Result The interior design of the main building appears today in renewed splendour, which appears absolutely authentic. The surfaces of the different paint systems and colours are harmoniously matched with each other and lend the historical ambience a coherent style. Product use: On lime-based old coatings, gypsum and stucco substrates: - Prime with BEECK Protect Primer - Basecoat /topcoat with BEECK Protect Fine On mineral old and new plaster or render surfaces: - Prime with BEECK Insil Primer Fine - Intermediate / basecoat with BEECK Insil On wooden doors and doorframes: - Prime with BEECK Oil Primer - Basecoat with BEECK Undercoat - Intermediate/basecoat with BEECK Interior Stand Oil Paint Satin Matt 20 BEECK Mineral Paints in Interiors BEECK Mineral Paints in Interiors 21

12 BEECK Mineral Paints in Interiors BEECK Mineral Paints in Interiors Colourless/transparent, high-penetration primer for highly absorbent substrates in the preservation of listed buildings, such as (air) lime, gypsum and clay. Reduces the absorbency, consolidates and strengthens without damaging the historical substrate and creates uniform coating surfaces for working on with BEECK Protect, Fine or Coarse. - Water thinnable - Solvent free - Universal - Reversible Fine grained casein emulsion coating for levelling out substrate defects and misses or holidays. Efficient application with brush or roller, finely slurrying and seamless. To coat preferably with BEECK Kasolit Fine, white or tinted. - Bridges hairline cracks - Like fine plaster - Texture grain 0.4 mm - Brightens up surfaces - Highly opaque white Protect Primer Removable primer coating in the BEECK Protect system Milky, transparent after drying 5 L / 12.5 L Kasolit Coarse Slurry, white primer coating in the BEECK Kasolit system White 8 kg / 20 kg W 24 value: > 1.00 kg / (m 2 h 1/2 ) W 24 value: 0.50 kg / (m 2 h 1/2 ) 0.03 m 0.02 m approx kg / L 1.57 kg / L ph value: 9 ph value: 9 approx L / m² on a smooth, normally absorbent substrate approx kg / m² on a smooth substrate User-friendly formulated, one-pack casein emulsion paint for open-pored coatings on all firm interior substrates. Ideal for valuable building biology substrates such as (air) lime plaster and clay, as well as gypsum, gypsum board, calcium silicate masonry and concrete. Pretreat highly absorbent substrates (gypsum, clay) with BEECK Casein Primer. Water-thinnable emulsion free from synthetic resins for interior substrates with high absorbency. Use on substrates containing gypsum and clay, porous lime plasters and lightweight building boards. Concentrate, to be thinned with 2 parts water. Further treatment with BEECK Kasolit, Fine or Coarse. Kasolit Fine Casein paint, free from synthetic resins, for highly water vapour permeable interior coatings - High hiding power - Free from chalking - Reversible in the interests of listed building preservation Specification to EN Wet-scrub resistance class 3 - Hiding power class 1 - Free from synthetic resin - Ideal building physics properties - Matt finish White, Off-White and factory-tinted pastel colours of the BEECK Mineral Colour Chart. Casein Primer Casein emulsion for priming highly absorbent substrates - High yielding - Consolidates and strengthens clay and gypsum Milky, uncoloured after drying 0.25 L / 1 L / 3 L / 10 L - Reduces flaring up effects - Valuable in building physics terms 5 L / 12.5 L W 24 value: 0.50 kg /(m 2 h 1/2 ) < 0.03 m 1.30 kg / L ph value: 8 approx L / m² on a smooth substrate W 24 value: 0.50 kg /(m 2 h 1/2 ) < 0.06 m 1.03 kg / L ph value: 8 approx L / m² concentrate on a smooth, normally absorbent substrate, corresponds to approx L water thinnable solution 22 BEECK Mineral Paints in Interiors BEECK Mineral Paints in Interiors 23

13 Reference: Griesbachsches Haus of Friedrich-Schiller-University Jena BEECK Mineral Paints in Interiors BEECK Mineral Paints in Interiors Lime Casein Paint Open-pored interior coating made from Soaked Marble Lime and paracasein for lime plasters and clay substrates Highly water vapour permeable, chalking free lime casein coating for lime-compatible substrates for use in restoring the interiors of listed buildings, such as air lime plaster and clay. Also for the renovation of historical lime and mineral paint coatings. High yield powder concentrate, mix with water to use. Apply using Mineral Paint Brush, regardless of the substrate in 2 to 3 passes. Pre-wetten clay. - Free from synthetic resins - Suitable for listed buildings - Moisture regulating - Low tension Lime White Can be tinted in pastel colours with BEECK Full Colour Lime Concentrate (max. 20 %). 5 kg / 10 kg - VOC-free powdered pigments - Lustred lime effect Soaked Marble Lime Wood-burned, pure slaked lime for restoration and church painting Marble lime slaked for many years for listed building preservation professionals. Suitable for lime washes and fresco painting on firm, lime-compatible substrates in the historical environment. Can be individually modified in consultation with the site engineers. It is essential to try it out on the original substrates. - Maximum purity - Absolutely suitable for listed buildings - Slaked for many years Lime White Can be tinted in pastel colours with BEECK Full Colour Lime Concentrate (max. 20 %) 6 kg / 18 kg - Deep light effect - Capillary active W 24 value: 0.80 kg/(m 2 h 1/2 ) < 0.02 m 1.35 kg / L approx kg powder / m² on a smooth substrate W 24 value: > 1.00 kg /(m 2 h 1/2 ) < 0.02 m approx kg / L Organic content: 0 % approx kg / m² on a smooth substrate 24 BEECK Mineral Paints in Interiors BEECK Mineral Paints in Interiors 25

14 BEECK Mineral Paints in Interiors BEECK Mineral Paints in Interiors Marble lime paint slaked for many years for lime-compatible interior substrates, for renovations and church painting. Modified, without using synthetic resins, to increase wipe resistance and hiding power. Sets through the chemical carbonization process. Attractive lustred lime effect. Does not form high-tension excessive coat thickness, even if painted over many times. Finely ground mineral pigments slaked and dispersed in Soaked Marble Lime. For pastel tinting of BEECK Lime Wash and Lime Casein Paint for interior areas, such as for church painting. Maximum added quantity: 20 %. Can also be used for full colour fresco painting on freshly felted lime plasters. Calcidin Soaked Marble Lime paint for lime plasters in interior areas - Ready-to-use - Hiding power if several coats are applied - Low chalking Lime White Can be tinted in pastel colours with BEECK Full Colour Lime Concentrate (max. 20%). 5 L / 12.5 L - Non vapour retarder Full Colour Lime Concentrate Lightfast mineral pigments, mixed as paste in Soaked Marble Lime - Maximum lightfastness - Shading suitable for listed buildings - Deep light effect - High yield Black, Umber, Ochre Yellow, Maize Yellow, Lemon Yellow, Green, Cobalt Blue, Ultra Blue, Wine Red, Oxide Red and Brown, see BEECK Mineral Paints Colour Chart. Addition to BEECK Lime Wash or Lime Casein Paints (max. 20 %) L / 5 L - Fully compatible with lime W 24 value: > 1.00 kg/(m 2 h 1/2 ) W 24 value: > 1.00 kg/(m 2 h 1/2 ) < 0.03 m < 0.02 m approx kg / L kg/l Organic content: approx. 1% Organic content: < 2 % approx L / m² on a smooth substrate approx L / m² on a smooth substrate User-friendly, organically modified lime wash paint for lime-compatible, firm substrates. Universal, opaque and high yield use. For exterior application, such as on the façades of listed buildings, always test product on the original substrates first. Unlike silicate paints, premature bronzing due to the chalking typical for lime. - Efficient - Low tension - Painter and decorator friendly - Non vapour retarder Calcidan Modified Soaked Marble Lime paint with high hiding power Lime White Can be tinted in pastel colours with BEECK Full Colour Lime Concentrate (max. 20%). 5 L / 12.5 L W 24 value: > 1.00 kg/(m 2 h 1/2 ) 0.03 m 1.25 kg / L Organic content: approx. 3 % approx L / m² on a smooth substrate 26 BEECK Mineral Paints in Interiors BEECK Mineral Paints in Interiors 27

15 BEECK Silicate Primers BEECK Silicate Primers Potassium water glass as binder, free from organic content to VOB/DIN Primer and thinner for BEECK Silicate Paints. Forms an inseparable microporous unit by means of silicification with the mineral substrate such as plaster, natural stone or concrete. As a strengthening primer for absorbent, chalking and crumbling substrates. Fixative Priming and binder for BEECK Silicate Paints including BEECK Pure Crystalline Finish - Pure mineral - Ideal building physics properties - Moisture regulating - UV resistant Colourless / transparent 1 kg / 5 kg / 10 kg / 30 kg - Optimum long lives - Full building biology compatibility W 24 value: > 1.00 kg/(m 2 h 1/2 ) < 0.01 m 1.16 kg / L Organic content: 0 % approx kg / m² on a smooth substrate for priming Priming and strengthening of porous mineral substrates, including those with a water-repellent surface or partially organic character, such as insulating plasters or existing coats which cannot be completely removed. Also as a glaze binder for BEECK Silicate Glazes on render, plaster and fair-faced concrete. - Optimum substrate adhesion - Can be colour-glazed with BEECK Powdered Pigment - Interior and exterior areas - Free from biocides BEECK Silicate Primers Primers fulfil diverse tasks and are as varied in their use as the substrates they are used to coat. BEECK Fixative consolidates porous, mineral building materials. On water repellent substrates BEECK MBA-Fixative is the first choice. BEECK Silane Primer acts as a water-repellent special primer for critical substrates such as brick and natural stone, while thanks to its excellent adhesion, BEECK Bonding Coat, whether Fine or Coarse, also makes weak silicification substrates accessible for mineral paint coatings. BEECK Quartz Filler is a slurrying primer that reliably bridges hairline cracks and minor structural defects. As a slurrying additive for silicate paints, BEECK Quartz Filler P in powder form can be used universally. Reference: Hermann-Lietz Schule in Haubinda MBA-Fixative Special fixative for weakly wettable substrates and for BEECK glazing technique Milky, transparent after drying 1 L / 5 L / 10 L W 24 value: > 1.00 kg /(m 2 h 1/2 ) 0.01 m 1.16 kg / L Organic content: < 5 % approx L / m² on a smooth substrate 28 BEECK Silicate Primers BEECK Silicate Primers 29

16 BEECK Silicate Primers Quartz Filler Fibre-reinforced priming coat for opaque or glazed silicate systems BEECKASF ActiveSilicateFormulation Quartz Filler P Slurrying additive in powder form for BEECK Silicate Paints for primer and intermediate coats Slurrying, natural white textured coating for levelling out mineral substrates and for bridging hairline cracks and structural defects. Coat the whole surface of made-good façades with BEECK Quartz Filler. Application with the Mineral Paint Brush. - BEECK ASF ActiveSilicateFormulation - Filling - Bridges hairline cracks and structural defects - Attractive, brushed surface Natural white opaquely pigmented 8 kg / 20 kg - Glaze primer for BEECK Concrete/Stone Glaze - Ideal building physics properties - Thin with BEECK Fixative W 24 value: 0.30 kg /(m 2 h 1/2 ) 0.02 m 1.56 kg / L Organic content: < 5 % approx kg / m², to be determined by testing first on a sample surface Fibre-reinforced powdered component for increasing the slurrying effect and bridging cracks. Can be universally used for BEECK Silicate Paints including BEECK Pure Crystalline Finish. As slurry additive: thoroughly mix one 4kg bag of BEECK Quartz Filler P in a 12.5 L bucket (e.g. Beeckosil Fine) and adjust with 2 to 4 kg BEECK Fixative until it is ready for coating. - Fine grained, fibre-reinforced - Active silicate powdered component - Bridges hairline cracks coats - Diffused light effect Light Grey, subtle colouring 4 kg / 8 kg / 25 kg - Ideal building physics properties - For primer and intermediate - Topcoat with Fine Gründerzeithaus Leopoldstraße 153 in Munich Task: The aim was to completely redesign the colour finish of the façade of this Gründerzeit building. Examination of the old coating showed that multiple layers of organically bonded, film-forming coatings had been applied to the mineral façade render and had resulted in building physics limitations. The surfaces were highly soiled due to thermoplastic effects and contained extensive fine hairline cracks. The following criteria were used to define the objective of the new colour finish: - The old multi-layered organic coating was to be removed completely from the façade through paint stripping. - A coating system with high weathering resistance and long lives, extreme water vapour permeability, and an unmistakeable matt, mineral character. - By creating sample areas, a suitable paint system and colour were to be found, which removed the hairline crack phenomena with suitable products. - The new coating system should only be applied using mineral paint techniques, very thinly with a brush. Project stages: Due to the existing condition of the surfaces found on site the old coating was removed completely. Sample areas were created using the defined technology. After making good existing render and applying new render the planned coating technology was applied. After the individual work steps were completed the responsible BEECK consultant examined the results and released the finished areas for further work. The work on site was checked and documented continuously with regard to the specified products and technology. Result: The standards worded in the objectives were achieved. The coating system and colour defined on the basis of old sample areas produced a true-to-style matt appearance and lends the façade surface a unique mineral profile. W 24 value: > 1.00 kg /(m 2 h 1/2 ) 0.01 m approx kg / L ph value: 9 Organic content: < 5 % (fibres!) kg / m², to be determined by testing first on a sample surface Product use: - Render neutralisation with BEECK Etching Fluid - Priming coat with BEECK Fixative - Priming coat with BEECK Quartz Filler - Intermediate and top coat with Beeckosil Fine 30 BEECK Silicate Primers BEECK Silicate Primers 31

17 BEECK Silicate Primers BEECK Silicate Primers Bonding Coat Fine Siliceous primer coating without texture grain as bonding agent Silicification bridge in interior and exterior areas on firm substrates such as stucco, concrete, fibrated cement or highly adherent, existing synthetic resin-based coatings. Further treatment with one-pack BEECK Silicate systems such as Beeckosil. - Highly adherent - Also on substrates with weak silicification - Low in solvents Natural white pigmented 5 L / 12.5 L - Without texture grain - White Pigmented - Water thinnable Silane Primer Water-repellent primer for efflorescent mineral substrates of façades Deep penetrating primer containing solvents based on organic silicon components. Suitable for porous mineral building materials such as brick, natural stone, calcium silicate masonry, mineral render or concrete. Equally suitable for alkaline or chemically neutral reacting substrates. Test on sample surface first to check effectiveness. Saturating application using the flow coating process. For commercial users only. - Deep action hydrophobic porous lining - Non vapour retarder - Prevents capillary water transport - Protects against drenching Colourless / transparent 5 L / 10 L - Prevents activation of structurally damaging salts - Non consolidating/strengthening - Highly alkali-resistant W 24 value: 0.10 kg/(m 2 h 1/2 ) W 24 value: 0.05 kg / (m 2 h 1/2 ) < 0.40 m 0.03 m 1.40 kg / L 0.79 kg / L ph value: 9 approx L / m² on a smooth substrate approx L / m², to be determined by applying on a test surface Universal primer coat with fine grained texture. Suitable for mineral plasters, external thermal insulation composite systems, gypsum and fibrated cement. Ensure uniform particle-size distribution when using on smooth substrates. Further treatment with one-pack silicate systems or plasters. Bonding Coat Coarse Silicate bonding agent with fine textured grain for substrates with weak silicification - Bonding agent - Texture grain (0.4 mm) - Optimum silicification of subsequent coats - Finely slurrying Natural white pigmented 8 kg / 20 kg - Brightening up of smooth substrates - White pigmented - Water thinnable - Low in solvents W 24 value: 0.10 kg/(m 2 h 1/2 ) < 0.35 m 1.53 kg / L approx kg / m² on a smooth substrate 32 BEECK Silicate Primers BEECK Silicate Primers 33

18 BEECK Building Preservatives Mineral building materials outdoors are exposed to diverse weathering. Rainwater results in increased building material moisture with all the associated harmful mechanisms such as corrosion, frost splitting, algae growth and the activation of structurally harmful salts. The combination of durable silicate coatings with pore hydrophobic silicon organic building preservatives has proven its worth for decades. BEECK Silicone Plus protects façades made of render, concrete and natural stone to achieve long-term conservation. BEECK Natural Stone Hardener OH finally consolidated crumbling façade building materials and is especially valuable for the restoration of historical sandstone buildings. Reference: Higher Regional Court, Cologne BEECK Building Preservatives BEECK Building Preservatives Permanent hydrophobing of porous mineral building materials in the façade area, suitable for render, natural stone, brick and concrete. Applied by flow coating until saturated. Also for the subsequent hydrophobing of BEECK Active Silicate Paints such as BEECK Pure Crystalline Finish or BEECK Concrete / Stone Glaze. In this combination, provides optimum contemporary building protection, verifiable by long-term references! Penetrates deep into the crumbling, leached out building material and results in controlled consolidation and strengthening of the stone and joint by depositing mineral silica gel. Can be subsequently coloured, for example with BEECK Concrete / Stone Glaze. For commercial users only. Test on sample surface on site first to check effectiveness on building. Subsequent hydrophobing with BEECK Silicone Plus is possible. Silicone Plus Highly alkaline resistant, long-term preservation of mineral façades - Long-term deep action preparation - Keeps the coating and the façade clean - Protects against moisture and building material corrosion - For alkaline and also chemically neutral substrates Colourless / transparent, not visually perceptible in dry weather conditions 1 L / 5 L / 10 L / 28 L - Ideal building physics properties - Maintains value and preserves - For commercial users only Natural Stone Hardener OH Silicic acid ester preparation for the consolidation and strengthening of porous bricks and natural stone - High degree of bonding agent deposition - Controlled hardening process - Without hydrophobing Transparent, test on site on building first for possible colour intensification. 5 L / 10 L / 28 L - High water vapour permeability - Rewash with solvent W 24 value: < 0.03 kg/(m 2 h 1/2 ) 0.03 m approx kg / L approx L / m², determine values for building by testing on a sample surface on site first W 24 value: < 1.00 kg /(m 2 h 1/2 ) 0.08 m 0.94 kg / L approx L / m², - determine values for building by applying to a sample surface first 34 BEECK Building Preservatives BEECK Building Preservatives 35

19 BEECK Building Preservatives Deep penetrating primer containing solvents based on organic silicon components. Suitable for porous mineral building materials such as brick, natural stone, calcium silicate masonry, mineral render or concrete. Equally suitable for alkaline or chemically neutral reacting substrates. Test on sample surface first to check effectiveness. Saturating application using the flow coating process. For commercial users only. Silane Primer Water-repellent primer for efflorescent mineral substrates of façades - Deep action hydrophobic porous lining - Non vapour retarder - Prevents capillary water transport - Protects against drenching Colourless / transparent 5 L / 10 L - Prevents activation of structurally damaging salts - Non consolidating/strengthening - Highly alkali-resistant W 24 value: 0.05 kg /(m 2 h 1/2 ) 0.03 m 0.79 kg / L approx L / m², to be determined by applying on a test surface Kurfürstliches Schloss Mainz Task: Since 2010, work has been underway to thoroughly repair the façade of this important building of the German Renaissance. The two-wing building with rich architectural structuring of the base areas, cornices, window reveals and pilasters made of Bunter sandstone and rendered surfaces showed signs of sanding, chalking of the old mineral coating and contour scaling and was therefore in need of fundamental rework and repair. After the fundamental addition and replacement of Bunter sandstone elements, the following aspects had to be taken into account for the new colour finish - What was needed was a coating system, which was not only highly weather resistant and had a long life, but also retained the matt mineral character. In addition, despite extreme water vapour permeability, the water transport of salts and harmful to the building materials and discolouring minerals were to be stopped. - The red to light-brown historical colour was to be determined authentically by trying out an individual colour recipe on test areas. - The new coating system should only be applied using mineral paint techniques, very thinly with a brush. - The coloured design of the new oak windows was to be applied with a glazing linseed oil system, especially with regard to good building physics properties and economic maintenance intervals. Project stages: Based on the existing findings and expertises on the surface character and the ideas of the objectives of the client, the City of Mainz, the competent built heritage conservation office and the firm of architects, the new coating system was tried out on test areas. In the factory, several colour samples had been formulated to specification and tried out on original substrates. After examining the sample areas and defining the application technology together with determining the precise application rates, the public invitation to tender for the pending coating work issued. The work was checked and documented with regard to the specified products and technology. Result: The standards worded in the objectives were achieved. With its matt appearance, the new special Schloss Mainz colour based on old findings is trueto-style and lends the sandstone of the façade surface a unique mineral profile. The colour design of the new oak windows with the stand oil system harmonises with the overall appearance of the historic building complex. Product use: Façade design: Oak windows: - Prime with BEECK Silane Primer - Prime with BEECK Oil Primer - Basecoat, intermediate and topcoat with Beeckosil Fine - Intermediate and top coat with BEECK Exterior Stand Oil Wood Glaze 36 BEECK Building Preservatives BEECK Building Preservatives 37

20 BEECK Auxiliaries BEECK Auxiliaries Aqueous acidic solution of fluorosilic acids for the removal of lime sinter layers on new mineral renders. Suitable for lime and lime cement renders in exterior areas. Can also be used to clean existing sintered renders. Not for use on external thermal insulation composite systems, thin renders, synthetic resin renders and gypsum. Acidic, corrosive concentrate, for commercial users only. Etching Fluid Acidic concentrate for sinter skin removal on new renders - Reliable against sinter skin - Creates porous, low tension substrates - No neutralisation required Colourless or tinted Pink 5 L / 10 L - Optimum silicification of subsequent silicate coats - Reduces absorbency and staining ph value: 1.20 kg/l 1 (unthinned) approx L/m² BEECK Auxiliaries A coating cannot be better than its substrate. This wise old decorator saying clearly shows the attention that should be paid to careful preparation of a substrate. Mineral façade renders often have a high-tension, glass-like brittle sinter layer. With BEECK Etching Fluid this can be removed safely and reliably, creating a porous, uniformly absorbent substrate for silicate coatings. BEECK Paint Stripper is used to remove old emulsion and synthetic resin coatings, and BEECK Fungicide protects mineral façades and external thermal insulation composite systems against lichens, algae and fungi. Reference: Residential building in Baden, Switzerland Paint Stripper Effective stripper for the removal of existing lacquer, latex and emulsion paints Paint stripper for the removal of coats from mineral substrates. Suitable for the removal of old synthetic resin based film-forming coats, special emulsion paints, on façades. Multilayer application for thick-layered, multilayered paint crusts. Can also be used on interior areas if good ventilation is provided. Can also be used for removing layers of coating from wood and metal. Test for effectiveness in advance. - Thixotropically adjusted - Does not damage mineral buildingmaterials No colouring 0.75 L / 5 L / 10 L / 25 L 1.10 kg / L ph value: 8 approx. 0.5 L / m² per pass - No neutralisation required - Free from aromatic and chlorinated hydrocarbons 38 BEECK Auxiliaries BEECK Auxiliaries 39

21 Reference: Griesbachsches Haus of Friedrich-Schiller-University Jena BEECK Auxiliaries Fungicide Aqueous active ingredient solution for the protection of mineral façades Biocidal protection against lichens, algae and mould on mineral façades and external thermal insulation composite systems. Optimum long-term effect on hydrophobic, microporous building materials which are not directly exposed to dirt and driving rain. Product suitability and an optimum, careful cleaning process should be tested first on site before use on the building. Only for commercial users and for use on exterior areas. - Wide range of effects - Free from organic solvents - Effective cleaning Colourless 5 L / 10 L ph value: kg / L - Protects against reinfestation - Alkali resistant approx L / m² for cleaning and follow-up treatment Griesbachsches Haus in Jena Task: The so-called princess s little palace built in 1784 in the style of German classicism was completely renovated between 2010 and Prior to the remediation, extensive work was carried out to secure findings, in order to be able to design the subsequent colouring largely true to the original in materiality and colourfulness. It was during this early phase that BEECK schen Farbwerke became active and, as a renowned manufacturer of paint systems compatible with built heritage conservation, it was involved in the preliminary planning. This was followed by close collaboration with the responsible restorer, the architects and the built heritage conservation authority, to draw up the detailed work steps for the respective interior and exterior substrates to clear restoration requirements, which were then summarised in tender specifications. Project stages: In the exterior area a new mineral render was applied to the façade. The paint system was also to have a classic mineral character and achieve its effect through timeless aesthetics. With the one-pack active silicate system Beeckosil an extremely durable façade paint was applied. This impresses through its exclusively mineral pigmentation and high colour resistance. All wooden elements such as cornices, windows and window shutters were redecorated with new colour using a weather resistant, colour-stable opaque stand oil wood glaze. The paint systems required in the interior which also not only had very good building physics properties but also lend the building a stylish look and at the same time are suitable for everyday public use. Due to the very different substrates, such as old coats and mineral as well as gypsum-based plasters, it was necessary to apply a paint system, which complied with the required good building physics properties with universal character. With BEECK Kasolit, a synthetic resin-free casein paint with convincing hiding power, abrasion and chalking resistance, all wall and ceiling surfaces were coated in subtle mineral colours. The result was a stylish, coherent colour concept with a fine surface look. The interior wooden elements such as doors, panelling and skirting boards were coated with BEECK Interior Stand Oil Paint. This was applied in thin coats and lends the building elements a true-to-style and material-compatible look. Result: This reference properly also illustrates graphically that where all kinds of different surface and therefore specific coating material requirements exist, the full range of BEECK schen Farbwerke products suitable for built heritage conservation can provide a high-quality solution. Product use: - Façade coat with the Beeckosil system - Interior Stand Oil Paints and Exterior Stand Oil Paints for wooden elements - BEECK Kasolit in the interior 40 BEECK Auxiliaries BEECK Auxiliaries 41

22 BEECK Stand Oil Paints BEECK Stand Oil Paints Mixture of boiled down linseed oil and stand oil containing finely ground mineral pigments with excellent durability and maintenance friendliness in exterior areas. True to traditional oil paint formulas, it does not tend to flake or become brittle, even under severe weather conditions. Suitable for both dimensionally stable (windows, external doors) and dimensionally unstable or conditionally stable wood-work (panelling, folding shutters, half-timbering, trusses). Exterior Stand Oil Paint Resin free, rich oil lacquer for woodwork exposed to weather conditions - High UV protection - Non flaking - Moisture regulating 8 standard colours and 126 colours of the BEECK Lacquer Colour Chart. Can be mixed together as required L / 0.75 L / 3 L / 10 L - Maintenance friendly - High solid - Suitable for listed buildings Gloss level: ph value: silk gloss 0.50 m approx kg/l (depending on colour) approx L/m² approx. 78 % (high solid) Abrasion resistant, old style linseed oil + hard resin lacquer, preferably for interior doors, furniture, wall and ceiling panelling. Style and material compatible for listed buildings and restoration. Also for the renovation of firmly adherent oil and alkyd resin lacquers. - Highly adherent and abrasion-resistant - Sorption capacity and diffusible - Non flaking - Earthy colour pallet suitable for listed buildings - High yielding BEECK Stand Oil Paints Oil paints are durable coatings that have been tried and tested for centuries on wood and ferrous metal surfaces in interior and exterior areas. The drying linseed oil acquired from cold-pressed linseed interlinks by absorbing oxygen and forms a resistant, waterproof coating film and securely integrates pigments. Stand oil paints are qualities which have been produced from seasoned linseed oil stored for lengthy periods a quality epitome with regard to drying, hardness and non-swellability in water! The product range of BEECK Stand Oil Paints now covers all application areas in restoration and historic building conservation. In true period style in terms of material and bronzing, suitable for listed buildings in terms of pigmentation and appearance, contemporary in terms of ease of maintenance and use properties, BEECK Stand Oil Paints have long since managed to make the leap from being niche products and set standards for modern coating qualities. Reference: Wartburg in Thuringia Interior Stand Oil Paint Glossy Opaquely pigmented hard resin stand oil lacquer for wood and ferrous metals 8 standard colours and 126 colours of the BEECK Lacquer Colour Chart. Can be mixed together as required L / 0.75 L / 3 L / 10 L Gloss level: glossy < 0.50 m approx kg / L (depending on colour) ph value: approx L / m² approx. 77 % 42 BEECK Stand Oil Paints BEECK Stand Oil Paints 43

23 Reference: Weißes Roß in Hartenstein BEECK Stand Oil Paints BEECK Stand Oil Paints Interior Stand Oil Paint Satin Matt Opaquely pigmented hard resin stand oil lacquer for wood and ferrous metals Abrasion resistant, old style linseed oil + hard resin lacquer, preferably for interior doors, furniture, wall and ceiling panelling. Style and material compatible for listed buildings and restoration. Also for the renovation of firmly adherent oil and alkyd resin lacquers. - Highly adherent and abrasion-resistant - Sorption capacity and diffusible - Non flaking 8 standard colours and 126 colours of the BEECK Lacquer Colour Chart. Can be mixed together as required L / 0.75 L / 3 L / 10 L - Earthy colour pallet suitable for listed buildings - High yielding Oil Primer Universal oil primer for absorbent wood Resin linseed oil primer for rough, absorbent woodwork. Can be equally used for dimensionally stable, dimensionally unstable and conditionally stable hardwood and softwood, such as windows, external doors, panelling and half-timbering or trusses. Not for tropical wood, test before using on oak. Further treatment with BEECK Undercoat, BEECK Exterior Stand Oil Paint / Interior Stand Oil Paint or with BEECK Stand Oil Wood Glazes. - Outstanding penetration power of creeping linseed oil molecules - Moisture regulating - Highly diffusible Transparent; decorative colour intensification on light-coloured woods 0.25 L / 1 L / 3 L / 10 L / 30 L - Also for half-timbering - Non flaking - Suitable for listed buildings to traditional formulas Gloss level: satin matt approx kg / L < 0.50 m Viscosity: approx. 34 sec. / 3 mm flow cup ISO 243 approx kg / L (depending on colour) < 0,5 m ph value: approx L / m² approx L / m² on planed softwood approx. 77 % 44 BEECK Stand Oil Paints BEECK Stand Oil Paints 45

24 BEECK Stand Oil Paints BEECK Stand Oil Paints Undercoat White matt linseed oil base coat for wood and metal Opaque white, filling undercoat for lacquering wood, wood-based materials and lacquering ferrous metals in interior and exterior areas. For dimensionally stable and dimensionally unstable wood. Also on firm pretreated existing coats of oil and alkyd resin based coatings. Further treatment with BEECK Exterior Stand Oil Paint or BEECK Interior Stand Oil Paint, white or tinted. - Highly adhesive, non flaking - Opaque white matt - High solid White. Can be tinted with coloured lacquers (20 %) for colourful topcoat L / 0.75 L / 3 L / 10 L - Diffusible - Low tension - Easy to use Lacquer Thinner Solvent and thinner for BEECK Stand Oil Paints Thinner especially matched to BEECK Stand Oil Paints, Primers and Stand Oil Wood Glazes. For adjusting the application viscosity as well as for cleaning tools and degreasing substrates. - High dissolving power - Mild odour - Universal for stand oil systems Transparent 0.25 L / 1 L / 3 L / 10 L Gloss level: Solids content: matt 1.36 kg/l approx L/m² approx. 77 % (high solid) Solvent content: 100 % approx kg / L Passivating, corrosion-inhibiting primer coat based on linseed oil and micaceous iron ore for iron and steel. Thoroughly grind or blast iron metals until they are bright, then apply one or two coats of BEECK Corrosion Protection Primer. Further treatment with BEECK Undercoat, topcoat with BEECK Exterior Stand Oil Paint (exteriors) or BEECK Interior Stand Oil Paint (interiors). Cannot be used in a highly corrosive climate, on non-ferrous metals or galvanized sheet steel! Corrosion Protection Primer Corrosion protection primer for ferrous metals and steel - Linseed oil with creep capability - Corrosion inhibiting - Suitable for listed buildings - Does not contain toxic heavy metals Grey-Brown. Further treatment with BEECK Undercoat, White L / 0.75 L / 3 L - Highly adherent, non flaking - Not for zinc, copper or aluminium Gloss level: Solids content: matt 1.40 kg/l approx L/m² approx. 80 % (high solid) 46 BEECK Stand Oil Paints BEECK Stand Oil Paints 47

25 BEECK Stand Oil Wood Glazes BEECK Stand Oil Wood Glazes Waterproof, resin-free stand oil boiled down mixture with finely ground mineral pigments, silk gloss finish. 15 standard colours for dimensionally stable, conditionally or dimensionally unstable woodwork such as windows, external doors, panelling and half-timbering and trusses. Ensure constructive wood preservation and wood quality free from blue stain. Exterior Stand Oil Wood Glaze Coloured glazing treatment of exposed wood - Weatherproof with high UV protection - Non flaking - Bronzing due to matt effect - Maintenance-friendly preservation 15 standard colour tones of the BEECK Standard Colour Chart. Can be mixed together as required. The wood s natural colour also determines the final colour L / 0.75 L / 3 L / 10 L - High yield - Diffusible - Moisture regulating - Ideal for woodwork in listed buildings Gloss level: silk gloss 0.50 m : approx kg / L (depending on colour) approx L / m² Viscosity: approx. 36 sec. / 3 mm flow cup ISO 2431 Subdued satin matt wood finish in 17 glazed colours as well as colourless for decorative exposed wood in interior areas. Suitable for wood and ceiling linings, panels, interior doors and furniture fronts. Also in kitchens and wet rooms outside of the spray water range and without intensive mechanical stresses. - Attractive, stain-like finish - Moisture regulating - Lightfast and durable - For restoration of listed buildings - Easy to use - High yielding and efficient BEECK Stand Oil Wood Glazes The wish for transparent, surface treatment of exposed wood often conflicts with poor durability and rapid weathering in exteriors. With their pure mineral, highly UV resistant pigmentation, BEECK Stand Oil Wood Glazes lend the best possible protection against weathering. Their low tendency to flake and the extremely thin layered application method make the coatings efficient and maintenance friendly. The oil molecules of the stand oil wood glazes anchor themselves deep in the wood. Absorbent, good gripping wood such as half-timbered buildings and rough-sawn formwork form an ideal substrate for oil-based wood glazes. Reference: Stadttheater Bielefeld Interior Stand Oil Wood Glaze Satin matt, diffusible stand oil wood glaze 17 standard colour tones of the BEECK Standard Colour Chart, plus colourless. Can be mixed together as required. The wood s natural colour also determines the final colour L / 0.75 L / 3 L / 10 L Gloss level: satin matt < 0.50 m : approx kg / L (depending on colour) approx L / m² Viscosity: approx. 34 sec. / 3 mm flow cup ISO BEECK Stand Oil Wood Glazes BEECK Stand Oil Wood Glazes 49

26 Reference: Rathaus Marktzeuln (Town hall), Upper Franconia BEECK Stand Oil Wood Glazes Oil Primer Universal oil primer for absorbent wood Resin linseed oil primer for rough, absorbent woodwork. Can be equally used for dimensionally stable, dimensionally unstable and conditionally stable hardwood and softwood, such as windows, external doors, panelling and half-timbering or trusses. Not for tropical wood, test before using on oak. Further treatment with BEECK Undercoat, BEECK Exterior Stand Oil Paint / Interior Stand Oil Paint or with BEECK Stand Oil Wood Glazes. - Outstanding penetration power of creeping linseed oil molecules - Moisture regulating - Highly diffusible Transparent; decorative colour intensification on light-coloured woods 0.25 L / 1 L / 3 L / 10 L / 30 L - Also for half-timbering - Non flaking - Suitable for listed buildings to traditional formulas : approx kg / L Viscosity: approx. 34 sec. / 3 mm flow cup ISO 2431 < 0.5 m approx L / m² on planed softwood Rathaus Marktzeuln Task: Between 2011 and 2013, the town hall, or Rathaus in Marktzeuln was completely renovated. This unique gem of the Franconian Baroque half-timbering skill was to be prepared extensively for reuse according to built heritage conservation aspects. The new colour finish of the façade and the overall interior structure played an important role, especially as the effect of such a historical building is defined by colours. Prior to the work on site, extensive preparations were carried out to secure findings, in order to be able to design the subsequent colouring largely true to the original in materiality and colourfulness. BEECK schen Farbwerke, as a renowned manufacturer of paint systems compatible with built heritage conservation, was involved in the preliminary planning during this early phase. This was followed by close collaboration with the responsible restorer, the architects and the built heritage conservation authority, to draw up the detailed work steps for the respective interior and exterior substrates to clear restoration requirements, which were then summarised in tender specifications. Project stages: After the old coatings had been completely removed, very weather-resistant and colour-stable opaque BEECK Stand Oil Paints were used for the exterior with its dominant half-timbered ensemble. The infill areas were given new colour with the one-pack active silicate system Beeckosil. This meant that paint systems were used, which are not only robust and have low resistance to water vapour diffusion, but also result in very cost-effective maintenance intervals. The paint systems required in the interior which also not only had very good building physics properties but also lend the building a stylish look and at the same time are suitable for everyday public use. Result: This reference properly illustrates graphically that where all kinds of different surface and therefore specific coating material requirements exist, the full range of BEECK schen Farbwerke products suitable for built heritage conservation can provide a high-quality solution on numerous substrates. The new colour decoration of the town hall in Marktzeuln is therefore a prime example of the performance and quality associated with BEECK. Product use: - BEECK Stand Oil Paints for half-timbering - Façade coating with Beeckosil - BEECK Interior Stand Oil Paints inside the building 50 BEECK Stand Oil Wood Glazes BEECK Stand Oil Wood Glazes 51

27 BEECK Tools BEECK Tools Mineral Paint Brush for efficient application of lime wash and silicate paints including BEECK Pure Crystalline Finish. Also ideal for slurry primer coats, such as BEECK Quartz Filler, on smooth and rough surfaces as well as for brushing into hairline cracks. Efficient for large surface silicate glazing techniques on façades, on screen walls and noise barriers. Effort-saving, ergonomically shaped handle, combined with the high paint absorption of the alkali-resistant, abrasion-proof natural bristles. A must-have for professionals and do-it-yourselfers for efficient and professional application of mineral paints! Mineral Paint Brush Robust, special brush for applying mineral paints - Raw wood handle with brass thread and metal mount Oval shaped distemper brush for watercolour-like glazing, creative design and decorative painting in interior and exterior areas with silicate, casein and lime wash paints. Ideal for smaller wall surfaces. Enables fatigueless, precise glazing due to its low weight and easy-to-handle brush format. Alkali-resistant and abrasion-proof natural bristles guarantee high paint absorption. Equally efficient for smooth and rough substrates. A must-have for finely shaded, polychrome colour levelling, retouching and visually appealing wiping and glazing techniques. - Raw wood handle with brass thread and metal mount Oval Brush Easy to handle special brush for wall glazing techniques BEECK Tools Mineral paint brushes and oval brushes are the right handtools for professional use of lime wash, silicate and casein paints. BEECK Flat Brushes have proven to be ideal for stand oil paints and wood glazes and produce streak-free coatings with optimum spreading. Reference: Meylandstraße Murten, Switzerland Flat Brushes Special brushes for oil paints Sturdy flat brushes for fast and efficient application of standard oil paints, stand oil wood glazes and oil primers on wood and metal. The combination of synthetic fibres and natural bristles enables a high degree of paint absorption, good brushability and optimum spreading on smooth, rough and even profiled substrates. Highly efficient on high-grip, large area substrates such as rough-sawn wood panelling and half-timbering or truss beams. Solventresistant, abrasionproof and leave no residues when cleaned for professionals and do-ityourselfers. - Beaver s tail raw wood handle - Brass mount Size 30 mm wide 50 mm wide 80 mm wide 52 BEECK Tools BEECK Tools 53

28 BEECK Mineral Colour Chart Miscellaneous Mineral Colour Chart 200 colours for contemporary colour design for use on mineral building materials, suitable for listed buildings All colours on the BEECK Mineral Colour Chart are available ready-mixed in the factory. Please refer to the individual product information for possible product-specific limitations. HBZ = brightness value. State-of-the-art colorimetry enables constant, reproducible shading. Minor colour differences can be caused by raw material influences, the texture and absorbency of the substrate, by diffused light effects and subjective colour perception. They do not constitute grounds for complaint. Please test the colour on a sample surface before use. Full colour paint White C-102 Off-White C-101 Black C-655 Umber C-652 Ochre Yellow C-651 Maize Yellow C-661 Lemon Yellow C-658 Green C-656 Cobalt Blue C-659 Ultra Blue C-657 Wine Red C-660 Oxide Red C-654 Brown C-653 Soft Shell Activity Jacket - Water-repellent - Windproof - Breathable - Integrated stretchy gloves with thumb hole - Hem with adjustable drawstring - Fashionably cut, longer back - Continuous YKK zip at the front - 2 spacious front pockets with zips - 1 inside pocket and 1 mobile phone pocket Material - Outer layer: 93 % polyester and 7 % elastane - Middle layer: waterproof, breathable and windproof TPU membrane - Inner layer: Microfleece Colour Yellow / Black Size S / M / L / XL / XXL Ready-mixed colours Price groups I-IV C-103 C-350 Price groups: No. PG No. PG No. PG No. PG No. PG No. PG No. PG No. PG No. PG C-101 I C-102 I C-103 I C-104 I C-105 I C-106 I C-107 I C-108 I C-109 I C-110 I C-111 I C-112 I C-113 II C-114 III C-115 II C-116 III C-117 III C-118 II C-119 III C-120 III C-121 III C-122 III C-123 II C-124 II C-125 II C-126 I C-127 I C-128 II C-129 III C-130 III C-131 III C-132 II C-133 I C-134 I C-135 I C-136 I C-137 I C-138 II C-139 III C-140 III C-141 III C-142 III C-143 II C-144 I C-145 I C-146 I C-147 I C-148 I C-149 I C-150 II C-151 III C-152 III C-153 III C-154 III C-155 II C-156 II C-157 II C-158 II C-159 I C-160 I C-161 I C-162 I C-163 I C-164 I C-165 I C-166 II C-167 II C-168 II C-169 III C-170 IV C-171 IV C-172 IV C-173 III C-174 IV C-175 I C-176 II C-177 III C-178 II C-179 III C-180 II C-181 II C-182 I C-183 I C-184 II C-201 I C-202 I C-203 I C-204 II C-205 III C-206 III C-207 IV C-208 III C-209 III C-210 II C-211 II C-212 I C-213 II C-214 III C-215 IV C-216 II C-217 II C-218 I C-219 I C-220 II C-221 III C-222 III C-223 III C-224 III C-225 III C-226 IV C-227 III C-228 III C-229 II C-230 I C-231 II C-232 II C-233 III C-234 III C-235 IV C-236 III C-237 III C-238 III C-239 III C-240 IV C-241 IV C-242 III C-243 II C-244 II C-245 II C-246 III C-247 III C-248 III C-249 II C-250 II C-251 I C-252 III C-253 IV C-254 IV C-255 IV C-301 I C-302 II C-303 II C-304 II C-305 III C-306 III C-307 II C-308 II C-309 I C-310 I C-311 I C-312 I C-313 I C-314 I C-315 I C-316 II C-317 II C-318 II C-319 I C-320 I C-321 II C-322 II C-323 I C-324 I C-325 II C-326 III C-327 III C-328 III C-329 III C-330 III C-331 II C-332 II C-333 I C-334 I C-335 II C-336 II C-337 II C-338 II C-339 I C-340 I C-341 I C-342 I C-343 I C-344 I C-345 I C-346 I C-347 II C-348 III C-349 II C-350 III C-651 III C-652 III C-653 III C-654 III C-655 III C-656 IV C-657 IV C-658 IV C-659 IV C-660 III C-661 IV No. = Number of the colour ( e. g. C-202) LV = Lightness value PG = Price groups 54 BEECK Mineral Colour Chart BEECK Miscellaneous 55