Brazing, Soldering, Adhesive, Bonding & Mechanical Fastening process Chapter 30
Joining process Brazing A filler metal is placed between two workpieces and heated until melted Two main types of Brazing Ordinary Braze welding Use of flux is very important
Filler Metals Available in a wide range of brazing temperatures They come in a wide range of shapes Choice of the filler metal and its composition are important Diffusion of the filler metal in to the workpeice is an important consideration Fig: a) Brazing b) Braze welding operation
Fluxes The use of flux in brazing is very important Generally made of: Borax Boric acid Borates Fluorides Chlorides Wetting agents may also be added
Torch Brazing Brazing Methods Performed by heating the joint with a torch Depositing the filler metal in the joint Suitable part thickness (0.25 6.0)mm Not a automated process More than one torch can be used in this process
Brazing Methods Furnace Brazing Precleaned & Preloaded with brazing metal Heated in a furnace Fig:An example of furnace brazing a)before b) after
Other Types Of Brazing Induction Brazing Resistance Brazing Dip Brazing Infrared Brazing Diffusion Brazing
Braze Welding Prepared like fusion welding Filler metal is deposited at the joint with the use of an oxyacetylene torch Considerably more filler is used Temperature is minimal compared to that of fusion welding; part distortion is minimal
Brazing Process Capabilities Dissimilar metals can be assembled with good joint strength Shear strength of brazed joints can reach 800Mpa Fig:Joint Designs commonly used in brazing operations.the clearance between the two parts being brazed is an important factor in joint strength.if the clearance is to small, the molten braze metal will not fully penetrate the interface.
Good/Poor Designs
Soldering Different types of soldering Torch Furnace Iron Induction Resistance Dip Infrared Ultrasonic reflow (paste) Wave
Reflow Soldering Solvents present in the paste are evaporated The Flux in the paste is activated and the fluxing action occurs The components are carefully preheated The solder particles are melted and wet the joint The assembly is cooled
Wave Soldering Popular approach to attaching circuits to circuit boards Fig: a)screening or stenciling paste onto a printed circuit board: 1) Stenciling process 2) a section of a typical stencil pattern b) wave soldering process
Types Of Fluxes Inorganic acids or salts clean the surface rapidly Noncorrosive resinbased used in electrical applications Soldering is used extensively in electronics industry
Adhesive Bonding Products are joined and assembled by the use of Adhesives Adhesives properties to be considered Strength Toughness Resistance to various fluids Ability to wet the surface to be bonded
Types of adhesives Surface must be clean for joining parts Should avoid joints that might be subjected to peeling forces Design for adhesive bonding
Adhesive Peeling Test Fig : Characteristic behavior of (a) brittle (b) tough adhesive in a peeling test
Joint Design in Adhesive Bonding Fig:Various joint design in adhesive bonding.
Configurations for adhesive bonds Fig : (a) single lap (b) double lap (c) scarf (d) strap
Threaded Fasters Bolts Screws Nuts Mechanical Fastening Other Fastening Methods Stapling Crimping Snap-in Fasteners Shrink and press fits
Rivets Fig:a)solid b)tubular c) split (bifurcated) d) compression Fig : Design guidelines for riveting (a)exposed shank is too long; the result is buckling instead of upsetting (b)rivets should be placed sufficiently far from edges to avoid stress concentrations (c)joined sections should allow ample clearance for riveting tools (d) section curvature should not interfere with the riveting process
Joining Plastics Heat softens the plastic to a molten state Then pressure added & fusion takes place External Heat Sources Hot air Heated tools & dies Electrical-Resistance Lasers Internal Heat Sources Ultrasonic welding Friction welding
THE END