Copyright 2000, Society of Photo-Optical Instrumentation Engineers This paper was published in Optical Microlithography XIII, Volume 4000 and is made

Similar documents
Mutually Optimizing Resolution Enhancement Techniques: Illumination, APSM, Assist Feature OPC, and Gray Bars

Reducing Proximity Effects in Optical Lithography

Copyright 1997 by the Society of Photo-Optical Instrumentation Engineers.

Comparative Study of Binary Intensity Mask and Attenuated Phase Shift Mask using Hyper-NA Immersion Lithography for Sub-45nm Era

Key Photolithographic Outputs

Optical Lithography. Keeho Kim Nano Team / R&D DongbuAnam Semi

Effect of Reticle CD Uniformity on Wafer CD Uniformity in the Presence of Scattering Bar Optical Proximity Correction

Copyright 2000 by the Society of Photo-Optical Instrumentation Engineers.

Tutor43.doc; Version 8/15/03 T h e L i t h o g r a p h y E x p e r t (November 2003)

Lithography. Development of High-Quality Attenuated Phase-Shift Masks

OPC Rectification of Random Space Patterns in 193nm Lithography

Copyright 2000 by the Society of Photo-Optical Instrumentation Engineers.

Process Optimization

Purpose: Explain the top advanced issues and concepts in

immersion optics Immersion Lithography with ASML HydroLith TWINSCAN System Modifications for Immersion Lithography by Bob Streefkerk

Developing an Integrated Imaging System for the 70 nm Node Using High Numerical Aperture ArF Lithography

Copyright 1998 by the Society of Photo-Optical Instrumentation Engineers.

Development of a Sub-100nm Integrated Imaging System Using Chromeless Phase-Shifting Imaging with Very High NA KrF Exposure and Off-axis Illumination

CONTACT HOLE IMAGING AT THE 0.13 µm NODE USING KrF LITHOGRAPHY

OPC Scatterbars or Assist Features

Optolith 2D Lithography Simulator

Design Rules for Silicon Photonics Prototyping

Resolution. T h e L i t h o g r a p h y E x p e r t (Winter 1997) Chris A. Mack, FINLE Technologies, Austin, Texas

Resist Process Window Characterization for the 45-nm Node Using an Interferometric Immersion microstepper

Holistic View of Lithography for Double Patterning. Skip Miller ASML

Copyright 2002 by the Society of Photo-Optical Instrumentation Engineers.

Photolithography I ( Part 1 )

Optical Lithography. Here Is Why. Burn J. Lin SPIE PRESS. Bellingham, Washington USA

Double Exposure Using 193nm Negative Tone Photoresist

16nm with 193nm Immersion Lithography and Double Exposure

OPTICAL LITHOGRAPHY INTO THE MILLENNIUM: SENSITIVITY TO ABERRATIONS, VIBRATION AND POLARIZATION

Critical Dimension Enhancement of DUV Photolithography on the ASML 5500/300. Francesca Calderon Miramonte High School August 13th, 2015

Optical Microlithography XXVIII

Performance data of a new 248 nm CD metrology tool proved on COG reticles and PSM s

The End of Thresholds: Subwavelength Optical Linewidth Measurement Using the Flux-Area Technique

Section 2: Lithography. Jaeger Chapter 2 Litho Reader. The lithographic process

Section 2: Lithography. Jaeger Chapter 2. EE143 Ali Javey Slide 5-1

What s So Hard About Lithography?

Section 2: Lithography. Jaeger Chapter 2 Litho Reader. EE143 Ali Javey Slide 5-1

Lithography. 3 rd. lecture: introduction. Prof. Yosi Shacham-Diamand. Fall 2004

Line End Shortening. T h e L i t h o g r a p h y E x p e r t (Spring 2000) Chris A. Mack, FINLE Technologies, Austin, Texas

Mask Technology Development in Extreme-Ultraviolet Lithography

Optimizing FinFET Structures with Design-based Metrology

Photolithography II ( Part 2 )

Major Fabrication Steps in MOS Process Flow

Aerial image based mask defect detection in dense array structures

Challenges of EUV masks and preliminary evaluation

Eun-Jin Kim, GukJin Kim, Seong-Sue Kim*, Han-Ku Cho*, Jinho Ahn**, Ilsin An, and Hye-Keun Oh

Immersion Lithography: New Opportunities for Semiconductor Manufacturing

Sub-12nm Optical Lithography with 4x Pitch Division and SMO-Lite

EE143 Fall 2016 Microfabrication Technologies. Lecture 3: Lithography Reading: Jaeger, Chap. 2

Development of a LFLE Double Pattern Process for TE Mode Photonic Devices. Mycahya Eggleston Advisor: Dr. Stephen Preble

2009 International Workshop on EUV Lithography

TECHNOLOGY ROADMAP 2006 UPDATE LITHOGRAPHY FOR

Copyright 2004 by the Society of Photo-Optical Instrumentation Engineers.

Shot noise and process window study for printing small contacts using EUVL. Sang Hun Lee John Bjorkohlm Robert Bristol

MICROCHIP MANUFACTURING by S. Wolf

DOE Project: Resist Characterization

Optical Proximity Effects

Purpose: Explain the top 10 phenomena and concepts. BPP-1: Resolution and Depth of Focus (1.5X)

Photolithography. References: Introduction to Microlithography Thompson, Willson & Bowder, 1994

Optical Proximity Effects, part 2

Lecture 5. Optical Lithography

Using the Normalized Image Log-Slope, part 2

* AIT-5: Maskless, High-NA, Immersion, EUV, Imprint

Flare compensation in EUV lithography

Lithographic Process Evaluation by CD-SEM

THE CHARACTERIZATION OF CHROMELESS PHASE SHIFT MASK TECHNIQUE FOR SUB-45NM LITHOGRAPHY TAN SOON YOENG

Decomposition difficulty analysis for double patterning and. the impact on photomask manufacturability

Double Patterning Combined with Shrink Technique to Extend ArF Lithography for Contact Holes to 22nm Node and Beyond

Analysis of Focus Errors in Lithography using Phase-Shift Monitors

Horizontal-Vertical (H-V) Bias

Impact of 3-D Mask Effects on CD and Overlay over Image Field in Extreme Ultraviolet Lithography

Recent Activities of the Actinic Mask Inspection using the EUV microscope at Center for EUVL

Microlens formation using heavily dyed photoresist in a single step

Lithography. International SEMATECH: A Focus on the Photomask Industry

Synthesis of projection lithography for low k1 via interferometry

Optical Requirements

AOARD REPORT The Photomask Japan '94 Held 22 April 94 at Kawasaki Science Park, Kanagawa, Japan

MICROBUMP LITHOGRAPHY FOR 3D STACKING APPLICATIONS

Lecture 8. Microlithography

Optical Maskless Lithography - OML

The future of EUVL. Outline. by Winfried Kaiser, Udo Dinger, Peter Kuerz, Martin Lowisch, Hans-Juergen Mann, Stefan Muellender,

INTERNATIONAL TECHNOLOGY ROADMAP SEMICONDUCTORS 2001 EDITION LITHOGRAPHY FOR

Update on 193nm immersion exposure tool

A Study of Wafer Plane Analysis with Mask MVM-SEM using 2D and 3D Images

Advanced Mix & Match Using a High NA i-line Scanner

IIL Imaging Model, Grating-Based Analysis and Optimization

Optical Maskless Lithography (OML) Project Status

ECSE 6300 IC Fabrication Laboratory Lecture 3 Photolithography. Lecture Outline

Feature-level Compensation & Control

MICRO AND NANOPROCESSING TECHNOLOGIES

Defect printability of thin absorber mask in EUV lithography with refined LER resist

Photolithography Technology and Application

EUV Lithography Transition from Research to Commercialization

TSMC Property. EUV Lithography. The March toward HVM. Anthony Yen. 9 September TSMC, Ltd

optical and photoresist effects

Semiconductor Manufacturing Technology. Semiconductor Manufacturing Technology. Photolithography: Resist Development and Advanced Lithography

i- Line Photoresist Development: Replacement Evaluation of OiR

Results of Proof-of-Concept 50keV electron multi-beam Mask Exposure Tool (emet POC)

Transcription:

Copyright 00, Society of Photo-Optical Instrumentation Engineers This paper was published in Optical Microlithography XIII, Volume 4000 and is made available as an electronic reprint with permission of SPIE. One print or electronic copy may be made for personal use only. Systematic or multiple reproduction, distribution to multiple locations via electronic or other means, duplication of any material in this paper for a fee or for commercial purposes, or modification of the content of the paper are prohibited.

Header for SPIE use High transmission attenuated PSM Benefits and Limitations through a validation study of 33%, % and 6% transmission masks Nishrin Kachwala*, John S. Petersen**, Martin McCallum* Nishrin.Kachwala@sematech.org *International Sematech, 2706 Montopolis Drive, Austin, TX 78741 **Petersen Advanced Lithography, P.O. Box 162712 Austin, TX 78716 ABSTRACT Simulations indicate high transmission attenuated phase shift mask to improve resolution, reduce line end shortening, corner rounding and provide process window enhancements for some pitches. They also indicate that as the transmission is increased for line features, the Normalized image log slope (NILS) increases for all pitches. In this work the performance of 33% and % attenuated masks has been compared against 6% and binary masks. Imaging results were obtained for 160nm features at various pitches with a 0.6NA 248nm SVGL MSIII with conventional and annular illumination. Performance of high transmission in terms of Depth of Focus, Overlapping process windows (ODOF), Exposure latitude and Proximity effects with the various % transmissions. Critical issues such as manufacturing of tri-tone masks, Inspection, Repair and material availability for High transmission (HiT) masks will be addressed. INTRODUCTION For gate level lithography Alternating PSM (alt. PSM) is a popular choice for features below 160nm with 248nm lithography. However for certain applications, the layout of Alternate phase shifted and unshifted structures can be complicated and require double exposure to get rid of phase edges. From literature (1) it is known that low transmission (5-6%) attenuated PSM (att. PSM) provide a benefit for gate type structures with off-axis illumination. High transmission attenuated PSM can provide as much resolution and Depth of Focus (DOF) as an alternating PSM (2), except for MEF. Also layout and fabrication of an att. PSM is simpler than an alt. PSM. Simulations have indicated that, high transmission masks provide benefits over the conventional transmission ones in terms of resolution, DOF, better pattern fidelity through focus i.e. reduced corner rounding and line end shortening (3). The goal of this work was to establish the benefits of HiT att. PSM and study limitations if any. 1. Experimental conditions: 160nm line/space features with no OPC correction were imaged with duty cycles 1:1,1:1.25, 1:1.5, 1:2, 1:2.5, 1:3, 1:5 and 1:10. Bare silicon wafers were coated with 0.450µm resist MG (JSR) and UV6 (Shipley) on 60nm DUV-30 (Brewer Science) BARC. Softbake 140º/60sec for MG and 130º/60 for UV6and Post exposure bake was 130º /90sec. A 248nm SVGL MSIII scanner with a 0.6NA and 0.8σ= conventional illumination and a 0.6 inner sigma and 0.8 outer sigma for the annulus was used.== CD measurements and Profiles were made using a KL8100 CD SEM and Hitachi cross-section SEM respectively. Process windows were derived using PRODATA from Finle Technologies. 2. Reticles : The attenuated material for the 6% and 33% was MoSi, and for the % was Cr/CrF. All three masks are tri-tone; i.e. MoSi had chrome over it in some areas (Figure 1 and 3). Simulations indicated that features only above 300nm would require chrome shielding as too much light through the leaky material would otherwise degrade its performance. Blanks coated with films with transmissions above 5-6% are not readily available, as they are not yet in production. To achieve higher transmission masks without developing new blanks a 6% attenuated material was used. Using Matrix theory for analysis of multilayer systems (4), the transmission can be tuned by varying the optical properties and thickness of the thin film layers, assuming that the incident radiation angle and λ are fixed. For a fixed n (refractive index) and k (extinction coefficient) of the 6% material, by reducing the thickness of the MoSi, the transmission through the film can be increased. The π phase difference for optical interference was adjusted by etching into the quartz (Figure 2).

3. Imaging results: 3.1. Conventional Illumination 0.6NA, 0.8σ For conventional illumination lower coherence was chosen based on simulations and some verification with imaging. For on-axis the illumination sigma could modulate the CD when with high %Transmission. The weak shifter like the binary mask does have zero diffraction order in the lens pupil. Thus the NA and partial coherence were optimized in the same way as typically done for binary chrome mask. The DOF from XSEM analysis at best dose for all the reticles is shown in Table 1 and the Exposure Latitude from XSEM analysis at best focus for the binary, 6% and 33% mask is shown in Table 2. We have excluded results from the % mask, as they did not confirm certain predictions. This may be due to the CD errors observed on this mask. The dense 1:1 features do not resolve with the binary, 6%, % or 33% attenuated masks with conventional illumination. This may be related to the resolution limit of (λ/na). The binary mask showed poor depth of focus (less than 0.6µm at 6% Exposure Latitude) for the dense and isolated pitches. For the semi-dense pitches its performance was reasonable but less than 0.75µm DOF. For the 6% mask, the DOF performance improves up to 45% over the binary. For the 33% mask DOF improvement up to 35% is seen over the 6% mask. There is not much improvement in the isolated line performance with the attenuated PSM over the binary, but 6% better than % better than 33% attenuated PSM. From Table 2 it is seen that Exposure Latitude gets better with higher transmission and improvement in EL for isolated features is seen. Table 1 DOF at best Dose for 160nm features, with 0.6NA and 0.8σ Line/Space BINARY 6%ATT 33%ATT 0.16/0. 0.45 0.80 0.90 0.16/0.24 0.65 0.60 >>1.04 0.16/0.30 0.70 0.65 1.00 0.16/0.34 0.73 0.82 0.90 0.16/0.42 0.72 0.75 0.70 0.16/0.80 0.50 0.75 0.80 0.16/--/ 0.50 0.55 0.70 Table 2 Exposure Latitude at best focus for 160nm features, with 0.6NA and 0.8σ Line/Space BINARY 6%ATT 33%ATT 0.16/. 10.0 8.0 17.0 0.16/0.24 9.5 12.0 17.5 0.16/0.30 12.0 10.0 15.0 0.16/0.34 6.0 9.0 15.0 0.16/0.42 6.0 9.0 18.0 0.16/0.80 6.0 12.0 15.0 0.16/--/ 6.0 14.0 15.0 %EL limits >15% 10-12% <10% DOF limits µm >0.8 0.6 to 0.8 <0.6 Across Pitch bias (Figure 4): Excluding pitches below λ/na for both 6% and 33% mask is the same. The TIR is about 27nm. The CD through pitch behavior for the 6% and 33% is same as the binary mask. Linearity (Figure 5): Isolated features linear to 0.14µm for all masks and may be linear below. Dense features linear to 0.14µm for the % and 33% mask, and may not be below. Larger dense and isolated features are not linear beyond 0.3µm, except for the dense 6% att. feature. Note: smallest feature on mask 0.14µm and largest 0.30µm The Process windows and its output for the 6% att. mask for all pitches except the 1:1 are shown in Figures 6-8. Individual DOF improved by 10-40% for the 6% att. Mask over the binary mask. Including duty cycles from 1.5 to isolated, 0.45µm overlapping DOF (ODOF) is obtained at 6%EL. Thus OPC would be required for overlap of dense features (pitch less than 240) with the pitches larger than 240nm. For the % mask, for pitches above 240 nm a DOF from 0.5 1.1 µm is seen in Figures 9-11. No process window overlap is seen between features. Excluding isolated features an ODOF of 0.5µm can be obtained. Isolated features can be overlapped with the dense by applying scattering bar OPC (5). The 33% attenuated dense and semi-dense features showed a DOF of about 0.7-1.0µm. No ODOF between pitches with this transmission (Figures 12-14). The 33% mask does show the EL to be highest for the isolated features. The performance improvement of isolated lines is least, but 33% slightly better than 6% slightly better than binary. It was observed that the 33 %T PSM tends to required higher exposure dose than the %. The %, in turn, required higher dose over 6%. The higher transmission inherently produces a better resolution or higher aerial image contrast (3). Data confirmed the case between 33% and 6% but not the %. This may be due to the mask CD s being smaller on the % mask.

We can make an observation with conventional illumination that as transmission increases the ODOF reduces due to high contrast on the isolated features. 3.2. Annular Illumination, σ I = 0.6 and σ o = 0.8 3.2.1. Process Window Results In order to increase the DOF of dense features, annular illumination is used with a 0.6 inner sigma and a 0.8 outer sigma. The choice of the annulus was limited by the tool configuration. The results of the 6% mask in Figures 15-17 showed features with duty cycles less than 2 to have a good DOF, from 0.7-1.1µm. Isolated features performance is below the specification of 0.6µm DOF at 6%. Loss of Exposure Latitude is observed with off-axis illumination. Loss of EL is made up in the gain in DOF for dense features. With off-axis illumination, proximity effects were enhanced. No overlap of process windows was observed between pitches for any transmission. For 6% the ODOF reduced from 0.45 µm to 0.0 µm. The 33% attenuated mask (Figures 18-) when imaged with annular illumination showed 0.8-1µm DOF for features with duty cycles up to 3. For Isolated features the performance was marginal, but still better than 6% mask. Better resolution was observed with the 33% mask, 1:1 features were well resolved than with the 6% mask. Simple 1-D OPC on dense features and scattering bar type OPC can cause process windows to overlap. 3.2.2. Pattern Fidelity through Defocus Figure 21 shows a Modified Brunner structure for the 6% and 33% mask for best dose and focus and at best dose and 0.2mm defocus. Less proximity bias is seen on the 33% mask then on the lower transmission mask. Also the dense-iso bias holds better through defocus with higher transmission. Pattern fidelity of the Brunner structures on the mask through defocus showed more robustness with the higher transmission, which agrees with past simulation studies (3). This indicates higher transmission requires less aggressive OPC. 4. Addressing Mask Fabrication : 4.1. Material availability High transmission blanks are not in production today. Though an increase in demand has been seen over the past year for %-attenuated material. This will be no issue about material if there is enough demand and a consensus on the transmission in the semiconductor industry. However high transmission may be an issue in some other areas as noted below. 4.2. Defect Inspection Today inspection capability at 365nm is in manufacturing, inspection at actinic wavelength in development. High transmission mask inspection not at actinic wavelength may cause problems. Lack of contrast between the attenuated material and glass and the attenuated material and chrome due to the high transmission makes it difficult to inspect the HIT att. PSM. Inspection capability of high transmission (18%) MoSi on quartz has been demonstrated (6). A critical inspection is that of the tri-tone layer i.e. chrome on the MoSi; especially when chrome is used for sidelobe suppression in contact hole applications. Attempts at inspection of the tri-tone reticles failed at 363nm wavelength. Currently, Tri-tone inspection algorithms are in a development state by some vendors. 4.3. Repair Repair of opaque and clear defects using Focus Ion Beam techniques has been demonstrated for attenuated masks. Post repair effects such as Gallium stains and river bedding are a concern. A variety of techniques such as gas assisted etching (7), biased repair method (8) or edge wall with wet etching (9) help restore the full process window. There should be no additional issues with repair of High transmission masks. A different stoichiometry and thickness of the material may require some minor process adjustment in repair techniques.

4.4. Tri-tone Fabrication Tri-tone masks require the additional chrome layer on top of the attenuating material to have tight tolerances. The CD and overlay of chrome to the attenuating layer must be well controlled. Overlay tolerances specified by the mask makers today (approx. 40-50nm) is not sufficient for critical area chrome shields (i.e. chrome shields for sidelobe suppression), chrome scattering bars or rims that are not self-aligned. The overlay of the layer needs to be tightened to less than 25nm, for no adverse effect due to the misalignment on process windows. 5. Summary: Dense features benefit most from high transmission. Largest with 33% mask, about 1µm. For duty cycles larger than 1:3 the performance of 33% slightly better than 6%, 6% slightly better than binary. Exposure Latitude increases as %Transmission increases. Proximity effect TIR (total indicated range) with conventional illumination same for all transmissions. Resist profiles had smooth sidewalls greater than 87. Exposed and small (<0.3µm) unexposed areas were not affected by the transmitted portion of the light through the attenuated areas, Figure 22. ACKNOWLEDGEMENTS International Sematech, Optical Extension program manager Gilbert Shelden and the Optical Extension Technical steering committee for their support. Fung Chen from ASML masktools for helpful discussions. REFERENCES 1. Attenuated phase-shifting mask in combination with off-axis illumination: a way towards quarter micron deep-uv lithography for random logic applications, Microelectronic Engineering, Vol 23, 133 (1994) 2. Process capability analysis of DUV Alternating PSM and DUV Attenuated PSM Lithography for 100nm Gate Fabrication, Keeho Kim, et al, SPIE Vol. 4000, Optical Microlithography XIII, 00 3. Assessment of a Hypothetical roadmap that extends optical Lithography over the 70nm technology node, J. S. Petersen, et al., SPIE Vol. 3546, p. 288, Annual BACUS Symposium on Photomask Technology, 12/1998 4. Design of optical interference coatings, Thelen Alfred, McGraw-Hill, c1989 5. Imaging contrast improvement for 160-nm line features using subresolution assist features with binary, 6% ternary attenuated phase-shift mask with process-tuned resist, Kachwala, Nishrin et al; Proc. SPIE Vol. 3679, p 55-67, Optical Microlithography XII, 07/1999 6. High transmission PSM inspection sensitivity, Chun-Hung Wu et al; Proc. SPIE Vol. 3873, p 117-126, Annual BACUS Symposium on Photomask Technology, 09/1999 7. H. Nakamura, et al, Jpn. J. Appl. Phy Vol. 31, 1992, p. 3055 8. Focused Ion Beam Repair of Embedded Phase Shift Masks, Z. Cui et al, SPIE Vol. 3051, p 276, Optical Microlithography X, 07/1997 9. M. Matsumoto, et al, SPIE Vol. 3096, Photomask and X-Ray Mask Technology IV, 8/1997

CHROME 6% T and π phase MoSi Quartz Figure 1: a)tri-tone 6% attenuated PSM CHROME 33% T and π phase Figure 2: High transmission tri-tone PSM made by reducing the MoSi thickness, etch of the quartz for π phase difference Figure 3 : SEM view of the tritone mask, showing the chrome shields on top of the MoSi

0. 0.19 CD µm 0.18 0.17 Binary 6% MASK 33% MASK 0.16 0.15 0.14 0.6NA, 0.8σ 1:1.5 1:2 1:2.5 1:3 1:5 1:30 Duty Cycle Figure 4: Proximity Effect with conventional illumination, NA=0.6 and σ=0.8 for pitches above λ/na Measured CD µm 0.35 0.30 Dense 1:2 0.25 0. 33% % 0.15 6% 0.10 0.12 0.17 0.22 0.27 0.32 Drawn CD µm Measured CD µm 0.35 Isolated 0.30 0.25 0. 0.15 33% % 6% 0.10 0.12 0.17 0.22 0.27 0.32 Drawn CD µm Figure 5: Linearity of dense and Isolated features with conventional Illumination, NA=0.6 and σ=0.8

Dose (mj/cm2) 60 55 50 45 40 06%L16S24 06%L16S30 06%L16S38 06%L16S46 06%L16S80 06%L16-ISO OVERLAP 35-0.6-0.4-0.2 0.0 0.2 0.4 0.6 0.8 1.0 Focus Figure 6: Process Windows for 6% attenuated mask, NA=0.6 and σ=0.8 Exposure Latitude (%) 25 SPACE DOF@6 %EL 0. 0.56 0.24 0.75 0.30 0.91 0.46 0.67 0.80 0.83 1.60 0.60 Figure 7: DOF for 6% attenuated mask from process window with NA=0.6 and σ=0.8 15 10 5 06%L16S24 06%L16S30 06%L16S38 806%L16S46 06%L16S80 06%L16-ISO 0 0.0 0.2 0.4 0.6 0.8 1.0 1.2 Depth of Focus (um) Figure 8: Exposure Latitude vs. DOF for 6% attenuated mask, NA=0.6 and σ=0.8

Dose (mj/cm2) 60 55 50 45 40 %L16S24 %L16S30 %L16S38 %L16S46 %L16S80 %L16-ISO OVERLAP 35-0.6-0.4-0.2 0.0 0.2 0.4 0.6 0.8 1.0 Focus Figure 9: Process Windows for % attenuated mask, NA=0.6 and σ=0.8, Excluding isolated features ODOF is 0.5µm at 6% EL Exposure Latitude (%) 30 SPACE DOF@ 6%EL 0. 0.54 0.24 1.00 0.30 1.10 0.46 0.72 0.80 0.52 1.16 0.70 10 %L16S24 %L16S30 %L16S38 %L16S46 %L16S80 %L16-ISO Figure 10: DOF for % attenuated mask with NA=0.6 and σ=0.8 0 0.0 0.2 0.4 0.6 0.8 1.0 1.2 1.4 1.6 Depth of Focus (um) Figure 11 Exposure Latitude vs. DOF for % attenuated mask, NA=0.6 and σ=0.8

Dose (mj/cm2) 45 40 35 30 33%L16S 33%L16S24 33%L16S30 33%L16S38 33%L16S46 33%L16S80 33%L16-ISO \ 25-0.4-0.2 0.0 0.2 0.4 0.6 Focus Figure 12: Process Windows for 33% attenuated mask, NA=0.6 and σ=0.8 with UV6 process Exposure Latitude (%) 40 SPACE DOF@6%EL 0. 0.80 0.24 0.90 0.30 0.85 0.38 0.65 0.46 0.60 0.80 0.75 1.60 0.70 Figure 13: DOF for 33% attenuated mask with NA=0.6 and σ=0.8, UV6 process 30 10 33%L16S 33%L16S24 33%L16S30 33%L16S38 33%L16S46 33%L16S80 33%L16-ISO 0 0.0 0.2 0.4 0.6 0.8 1.0 Depth of Focus (um) Figure 14: Exposure Latitude vs. DOF for 33% attenuated mask, NA=0.6 and σ=0.8 with UV6 process

Dose (mj/cm2) 34 32 30 28 26 24 22 T6L16S T6L16S24 T6L16S30 T6L16S38 T6L16S46 T6L16S80 T6L16-ISO 18-0.4-0.2 0.0 0.2 0.4 0.6 Focus Figure 15: Process Windows for 6% attenuated mask, NA=0.6 and annulus 0.6/0.8, with UV6 process Exposure Latitude (%) 25 15 10 5 T6L16S T6L16S24 T6L16S30 T6L16S38 T6L16S46 T6L16S80 T6L16-ISO SPACE DOF@10 %EL 0. 0.98 0.24 0.98 0.30 0.70 0.46 0.55 0.80 0.53 1.60 0.38 Figure 16: DOF for 6% attenuated mask with NA=0.6 and annulus=0.6/0.8, 0.6/0.8,=with UV6 process 0 0.0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 1.0 Depth of Focus (um) Figure 17: Exposure Latitude vs. DOF for 6% attenuated mask, NA=0 6 and annulus 0 6/0 8 with UV6 process

Dose (mj/cm2) 35 30 25 T33L16S T33L16S24 T33L16S30 T33L16S38 T33L16S46 T33L16S80 T33L16-ISO -0.4-0.2 0.0 0.2 0.4 0.6 Focus Exposure Latitude (%) 25 Figure 18: Process Windows for 33% attenuated mask, NA=0.6 and annulus 0.6/0.8, with UV6 process SPACE DOF@10%EL 0. 1.00 0.24 0.90 0.30 1.00 0.38 1.00 0.46 0.78 0.80 0.60 1.60 0.53 15 10 5 T33L16S T33L16S24 T33L16S30 T33L16S38 T33L16S46 T33L16S80 T33L16-ISO Figure 19: DOF for 33% attenuated mask with NA=0.6 and annulus=0.6/0.8, 0.6/0.8,=with UV6 process 0 0.0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 1.0 Depth of Focus (um) Figure : Exposure Latitude vs. DOF for 33% attenuated mask, NA=0.6 and annulus 0.6/0.8, with UV6 process

BEST FOCUS 0.2 µm DEFOCUS 33% ATT. 6% ATT. Figure 21: Pattern Fidelity of 6% and 33% attenuated masks through defocus BINARY 6% ATT PSM % ATT PSM 33% ATT PSM Figure 22: Resist profiles of Binary, 6%, % and 33% masks for 1:2 160nm features with conventional illumination, NA=0.6 and σ=0.8