HKP 21 HKP 25 EDGEBANDING - CARTRIDGES Dorus is the original manufacturer of Cartridge Adhesives for Holz-Her automatic edgebanding machines. HKP 21 and HKP 25 were specifically formulated for and approved by Holz-Her. The viscosity, spread, and flow characteristics of these Cartridges were specially developed in conjunction with Holz-Her. Dorus adhesives will not clog or block the application nozzles on the special glue application head. Dorus Cartridges are without equal in the market, competitively priced, and easy to use. HKP 21 - PVC, ABS*, VENEER, POLYESTER, MELAMINE, SOLID WOOD* HKP 25 - PVC, ABS*, VENEER, POLYESTER, MELAMINE, SOLID WOOD*, HPL HKP 21 HKP 25 Viscosity (Brookfield) @ 200 C : 90,000 mpas 55,000mPas Softening Point : 108 C 108 C Heat Resistance : 90 C 90 C Heat-up Time : 2-4 Minutes Processing Temperature Application roller : 200-220 C 200-220 C Melting container : 190-200 C 190-200 C : 40ft./min. 30ft./min. HKP 21 - NATURAL, WHITE, BROWN HKP 25 - NATURAL, WHITE, BROWN, BLACK 45 CARTRIDGES PER 33 LB. CASE vapors can irritate respiratory organs. Adequate ventilation should be provided. product s suitability for your particular purpose. *Conditionally recommended applications. Suggest testing on specific application to determine suitability. Holz-Her is the registered trademark of Karl M. Reich of Nurtingen, Germany and licensed in the United States to Holz-Her US, Inc. Dorus is the Registered Trademark of Dorus Klebetechnik GmbH & Co. KG.
KS 201/4 EDGEBANDING/SOFTFORMING KS 201/4 is a high viscosity, multi-purposed EVA based Hot Melt, offering extremely high heat resistance. It was formulated specifically for use in automatic edgebanding equipment and is recommended for both normal edgebanding as well as soft forming. Its high viscosity and high application temperatures make it most suitable for larger or newer automatic edgebanding equipment. The spread and flow characteristics permit standard as well as very high feed speeds to be run without stringing. KS 201/4 is a premium grade, state of the art Hot Melt for automatic edgebanding applications. PVC, ABS*, VENEER, POLYESTER, MELAMINE, SOLID WOOD, HPL* Viscosity - (Brookfield) at 200 C : 140,000 mpas Softening Point : 148 C Heat Resistance : 110 C Application roller : 225 C Melting container : 210-220 C : 60 ft./min. STOCK COLOR AVAILABLE: NATURAL (D, S) 308 LB. DRUMS, 55 LB. SACK vapors can irritate respiratory organs. Adequate ventilation should be provided. without guarantee since the conditions of use are beyond our control. Please test and establish for yourself our products suitability for your particular purposes. Dorus is the registered trademark of Dorus Klebetechnik GmbH + Co. KG
KS 205 EDGEBANDING: KS 205 is a high viscosity, EVA - rubber based Hot Melt adhesive specially formulated for use in automatic edgebanding equipment. This premium grade Hot Melt has been modified with a rubber additive to provide an exceptionally strong and durable multi-purpose Hot Melt adhesive. KS 205 is recommended for all straightline edgebanding applications. Its high viscosity, excellent bonding characteristics, and high heat resistance make this the ideal allpurpose edgebanding adhesive. The spread and flow characteristics of KS 205 permit both moderate and high speed applications to be run without stringing. PVC, ABS, VENEER, POLYESTER, MELMAINE, SOLID WOOD, HPL Viscosity - (Brookfield) at 200 C : 150,000 mpas Softening Point : 120 C Heat Resistance : 95 C Application roller : 220-225 C Melting container : 200-220 C : 40 ft./min. NATURAL (D, S), WHITE (D, S) 308 LB. DRUMS, 55 LB. SACKS vapors can irritate respiratory organs. Adequate ventilation should be provided.
KS 208/2 EDGEBANDING: KS 208/2 is a high viscosity, multi-purpose, EVA based Hot Melt specially formulated for use in automatic edgebanding equipment. The fast melting properties and spread and flow characteristics permit both standard and high feed spreads to be run without stringing. The melting characteristics of this adhesive cause less charring and oxidization in the pot and therefore result in a cleaner operating Hot Melt. KS 208/2 is economically priced and easy to apply. PVC ABS* VENEER POLYESTER MELAMINE Viscosity - (Brookfield) at 200 C : 130,000 mpas Softening Point : 110 C Heat Resistance : 90 C Application roller : 190-200 C Melting container : 180-200 C : 50ft./min. NATURAL (D, S), WHITE (D, S), BLACK (S) 308 LB. DRUMS, 55 LB. SACKS
KS 217 EDGEBANDING: KS 217 is a low viscosity, EVA based Hot Melt specially formulated for use in automatic edgebanding equipment. This Hot Melt is strongly recommended for use in granular feed or quick step Hot Melt systems. The low viscosity of KS 217, fast melting properties, and easy spread and flow characteristics make it ideally suited for smaller or older automatic edgebanding equipment. This superior quality Hot Melt shows excellent wetting properties and superior bonding strength. KS 217 should run at moderate to high line speeds and is formulated not to string. PVC, ABS, VENEER, POLYESTER, MELAMINE, SOLID WOOD, HPL* Viscosity - (Brookfield) at 200 C : 55,000 mpas Softening Point : 105 C Heat Resistance : 90 C Application roller : 190-200 C Melting container : 180-200 C : 40 ft./min. NATURAL (D, S), BROWN (S), WHITE (S) 308 LB. DRUMS, 55 LB. SACKS
KS 224/2 EVA HOTMELT ADHESIVE FOR EDGEBANDING CHARACTERISTICS Low viscosity Low application temperature Fast melting Very good wetting High glue mileage Specifically designed for manually operated edgebanders. Adhesive can be applied directly onto the edgebanding. PVC, ABS*, VENEER, POLYESTER, MELAMINE, SOLID WOOD Viscosity - (Brookfield) at 200 C : 10,000 mpas Softening Point : 85 C Heat Resistance : 75 C Application roller : 120-140 C Melting container : 120-140 C : 30 ft./min. NATURAL 55 LB. SACKS
KS 350/2 EVA HOTMELT ADHESIVE FOR EDGEBANDING UNFILLED CHARACTERISTICS Medium viscosity Universal hotmelt adhesive Very clean working, produces tight joints virtually not visible High glue mileage Very good wetting Permits smooth surfaces even with very flexible edgebanding materials PVC*, ABS*, VENEER, POLYESTER, MELAMINE, HPL* Viscosity - (Brookfield) at 200 C : 110,000 mpas Softening Point : 125 C Heat Resistance : 85 C Processing Temperature Application roller : 190-210 C Melting container : 190-210 C : 50ft./min. CLEAR 55 LB. SACKS
Q 621 EDGEBANDING / SOFTFORMING Q 621 is a medium viscosity, multi-purpose, EVA based Hot Melt specially formulated for use in automatic edgebanding equipment. The fast melting properties and spread and flow characteristics permit both standard and high feed spreads to be run without stringing. The melting characteristics of this adhesive cause less charring and oxidization in the pot and therefore result in a cleaner operating Hot Melt. Q 621 is economically priced and easy to apply. It is also suitable for softforming applicators. PVC, VENEER, POLYESTER, MELAMINE, HPL* Viscosity - (Brookfield) at 200 C : 115,000 mpas Softening Point : 120 C Heat Resistance : 90 C Application roller : 190-210 C Melting container : 180-200 C : 50ft./min. NATURAL 55 LB. SACKS vapors can irritate respiratory organs. Adequate ventilation should be provided. without guarantee since the conditions of use are beyond our control. Please test and establish for yourself our product s suitability for your particular purposes.
Q 654 EDGEBANDING/SOFTFORMING Q 654 is a high viscosity, high temperature, multipurpose EVA based Hot Melt adhesive formulated for both straightline and softform applications in newer automatic edgebanding equipment. This clean processing, slightly filled Hot Melt creates tight, virtually invisible glue joints and provides excellent wetting and coverage. Q 654 is also highly recommended for machine processing centers such as the BAZ. PVC, ABS*, VENEER, POLYESTER, MELAMINE, HPL* Viscosity - (Brookfield) at 200 C : 140,000 mpas Softening Point : 115 C Heat Resistance : 95 C Processing Temperature Application roller : 200-210 C Melting container : 200-210 C : 20ft./min. CLEAR 55 LB. SACKS
US 241/4 EVA HOTMELT ADHESIVE FOR PROFILE WRAPPING CHARACTERISTICS Medium viscosity Fast melting, very suitable for high feed rate Good wetting Wrapping of profile cores made of particleboard, MDF or solid wood with backed or unbacked veneers and resin impregnated laminates. Viscosity - (Brookfield) at 200 C : 35,000 mpas Softening Point : 105 C Heat Resistance : 80 Open Time : 50 sec. Processing Temperature Application Roller : 180-200 C Melting Container : 180-200 C Recommended Application Amount With chipboard : 160 200q/m 2 With MDF or solid wood : 100 150g/m 2 NATURAL 55 LB. SACKS
DD 060 DOWEL INSERTION: DD 060 is a multi-purpose, low viscosity PVA adhesive formulated for use in both low and high-pressure dowel insertion systems. It is suitable for use in plywood, MDF, and particleboard. It offers good flow characteristics and very fast set up times with high bond strength. D 060 will not clog or block nozzle during application. DD 060 is also recommended for automatic knot hole filling and dovetail joint assembly equipment. Base : PVAc Dispersion *Viscosity - 20ºC : 225 mpas Minimum film forming temperature : 3ºC *According to Epprecht Viscometer TV/R2 and R3 Compression Ratio : 2:1 DD 060 is ready to use. Do not add water. Stir before use. The temperature and composition of substrate may affect adhesive set up times. It is recommended for optimum set up times that all materials be stored at room temperature for a minimum of 24 hours before use. 23 lb. plastic jug with screw cap. CLEANING: Tools can be cleaned with water. DD 060 may be stored for up to 12 months in original closed containers. Keep in cool and dry. PROTECT FROM FREEZING. NOTE: Statements made are based on our experience and tested. However, recommendations and suggestions are made Dorus is the Registered Trademark of Dorus Klebetechnik GmbH + Co. KG.