Analysis of Surface Integrity of Honeycombed Aero Composite Material in Drilling with HSS Cutting Tool

Transcription

1 UNIVERSITI TEKNIKAL MALAYSIA MELAKA Analysis of Surface Integrity of Honeycombed Aero Composite Material in Drilling with HSS Cutting Tool Thesis submitted in accordance with the requirements of the Universiti Teknikal Malaysia Melaka for the Bachelor Degree of Manufacturing Engineering in Manufacturing Process By Mohd Azrul Hisham Bin Abdul Kadir (B ) Faculty of Manufacturing Engineering April 2007

2 ANALYSIS OF SURFACE INTEGRITY OF HONEYCOMBED AERO COMPOSITE MATERIAL IN DRILLING WITH HSS CUTTING TOOL MOHD AZRUL HISHAM BIN ABDUL KADIR UNIVERSITI TEKNIKAL MALAYSIA MELAKA

3 UNIVERSITI TEKNIKAL MALAYSIA MELAKA BORANG PENGESAHAN STATUS TESIS* JUDUL: ANALYSIS OF SURFACE INTEGRITY OF HONEYCOMBED AERO COMPOSITE MATERIAL IN DRILLING WITH HSS CUTTING TOOL SESI PENGAJIAN: 2006/2007 Saya MOHD AZRUL HISHAM BIN ABDUL KADIR (HURUF BESAR) mengaku membenarkan tesis (PSM/Sarjana/Doktor Falsafah) ini disimpan di Perpustakaan Universiti Teknikal Malaysia Melaka (UTeM) dengan syarat-syarat kegunaan seperti berikut: 1. Tesis adalah hak milik Universiti Teknikal Malaysia Melaka. 2. Perpustakaan Universiti Teknikal Malaysia Melaka dibenarkan membuat salinan untuk tujuan pengajian sahaja. 3. Perpustakaan dibenarkan membuat salinan tesis ini sebagai bahan pertukaran antara institusi pengajian tinggi. 4. **Sila tandakan ( ) SULIT TERHAD TIDAK TERHAD (Mengandungi maklumat yang berdarjah keselamatan atau kepentingan Malaysia yang termaktub di dalam AKTA RAHSIA RASMI 1972) (Mengandungi maklumat TERHAD yang telah ditentukan oleh organisasi/badan di mana penyelidikan dijalankan) Disahkan oleh: (TANDATANGAN PENULIS) Alamat Tetap: 694 KAMPUNG PADANG MACHANG, MANIR, KUALA TERENGGANU (TANDATANGAN PENYELIA) Cop Rasmi: Tarikh: 09/05/2007 Tarikh: * Tesis dimaksudkan sebagai tesis bagi Ijazah Doktor Falsafah dan Sarjana secara penyelidikan, atau disertai bagi pengajian secara kerja kursus dan penyelidikan, atau Laporan Projek Sarjana Muda (PSM). ** Jika tesis ini SULIT atau TERHAD, sila lampirkan surat daripada pihak berkuasa/organisasi berkenaan dengan menyatakan sekali sebab dan tempoh tesis ini perlu dikelaskan sebagai SULIT atau TERHAD.

4 APPROVAL This thesis submitted to the senate of UTeM and has been accepted as partial fulfillment of the requirements for the degree of Bachelor of Manufacturing Engineering (Manufacturing Process) The members of the supervisory committee are as follow:. Main Supervisor (Mr. Raja Izamshah Bin Raja Abdullah ) 13 April Co-Supervisor (En. Mohd. Hadzley bin Abu Bakar) 13 April 2007 i

5 DECLARATION I hereby, declare this thesis entitled Analysis of Surface Integrity of Honeycombed Aero Composite Material in Drilling with HSS Cutting Tool is the result of my own research except as cited in the references. Signature : Author s Name : Mohd Azrul Hisham Bin Abdul Kadir Date : 13 April 2007 ii

6 DEDICATION Especially dedicated to my parents, family and friends that helps me in completing this thesis. iii

7 ACKNOWLEDGEMENT Alhamdulillah. Thanks to Allah S.W.T because of the blessing I can complete this thesis. I would like to thanks to my supervisor Raja Izamshah Bin Raja Abdullah for guiding me in completing this thesis. Also a lot of thanks to the technician of material laboratory and the NDT lab in FKP for helping me in finishing the research successfully. A special thanks to my parents for their effort and endless support. iv

8 ABSTRACT This thesis investigates the effect of the drilling parameters, (cutting speed and cutter diameter) in drilling of aero composite material with different fiber fractions. Three speeds (low, medium and high) and five cutter diameter with different size are used in this study. The results show that the cutting speed and cutter diameter have direct effects on crack and surface roughness on the work piece. On the other hand, increasing the cutting speed reduces the associated crack and surface roughness, especially for large cutter diameter. The influence of cutting parameters on peel-up and push-out delaminations that occurs at drill entrance and drill exit respectively at the specimen surfaces have been investigated. No clear effect of the cutting speed on the delamination size is observed, while the delamination size decreases with increasing the cutter diameter. v

9 ABSTRAK Tesis ini menyiasat tentang kesan parameter penggerudian, (kelajuan dan diameter pemotong) penggerudian pada bahan komposit dengan pecahan-pecahan gentian berbeza. Tiga kelajuan digunakan iaitu (rendah, sederhana dan tinggi) dan lima jenis diameter pemotong digunakan dengan saiz yang berbeza Keputusan menunjukkan bahawa kelajuan pemotongan dan diameter pemotong adalah berkadar terus ke atas kesan keretakan dan kekasaran permukaan pada bahan kerja. Sebaliknya, peningkatan kelajuan proses pememotongan mengurangkan kesan keretakan dan kekasaran pada permukaan bahan kerja, terutamanya pada diameter pemotong yang bersaiz besar.parameter yang mempengaruhi pemotongan pada permukaaan kulit atas dan menghentikan delaminations yang berlaku di bahagian luar penggerudian dan menggerudi bahagian keluar pada spesimen permukaan-permukaan telah disiasat. vi

10 LIST OF CONTENT APPROVAL... i DECLARATION... ii DEDICATION... iii ACKNOWLEDGEMENT... iv ABSTRACT... v ABSTRAK... vi LIST OF CONTENT... vii LIST OF FIGURE... ix LIST OF TABLE... xii CHAPTER INTRODUCTION Background of Project Problem Statement Objective Project Scope of Project... 3 CHAPTER LITERATURE REVIEW Composite Material Composite background Composite Structure Principle of Machining Process Drilling Process Drilling Cutter Machining parameter Tool Wear Tool wear phenomena Operations SEM Observation of Flank, Face and Nose Wear of End Mill Tool Inserts Work Impact Failure Mechanism vii

11 2.3.4 Tool Failed Due to Excessive Wear Tool Nose Radius Effect On Cast Iron Milling PCBN Tooling Coating Scanning Electron Microscope (SEM) CHAPTER METHODOLOGY Selection of machine CNC machine Scanning electron microscope Selection of the work material Selection of cutting tool Selection of cutting parameters Experiment procedure Flow chart of experimental procedures CHAPTER RESULT AND DISCUSSION CHAPTER CONCLUSIONS AND RECOMMENDATIONS REFERENCES viii

12 LIST OF FIGURE Figure 1: Sandwich construction. [1]... 7 Figure 2: Schematic illustration of the basic principle of the drilling operation with important features/dimensions [2] Figure 3: Common Types of Drills Bits [2] Figure 4: Typical Drilling Processes [2] Figure 5: illustrate of term applying to Twist Drills Figure 6: Illustration of speed, feed and depth of cut Figure 7: Tool wear phenomena Figure 8: The above figure shows the image of the -45º rake tool before the cutting tests. [8] Figure 9: (a) Cutting edge of the tool after a total depth of cut of 25 µm (No appreciable tool wear can be seen. The cutting edge is degraded a little bit. (b) Cutting edge of the tool after a total depth of cut of 100 µm (The edge just starts to wear on the flank face. Flank wear is noticeable) [8] Figure 10: (a) Cutting edge of the tool after a total depth of cut of 175 µm (Rib like features which are similar to abrasive wear on the flank face could be clearly seen) Figure 11: Inserts Work material = 4140 Steel, TiN Coated Carbide Tool Inserts Tool-life (ISO standard: 0.8 mm localized flank wear) = 5 min. 54 sec. (V = 400 m/min, f = 2 m/min and a = 4 mm) [9] Figure 12: Work material = 4140 Steel, TiN Coated Carbide Tool Inserts Tool-life (ISO standard: 0.8 mm localized flank wear) = 9 min. 8 sec. (V = 400 m/min, f = 1 m/min and a = 7 mm) [9] Figure 13: PCBN tool illustrating mechanical impact failure of the cutting edge Figure 14: Photographs illustrating tool wear as a function of time for various steel 22 Figure 15: Tool Nose Radius Effect on Cast Iron Milling Larger Nose Radius Increases Thermal Breakdown [11] Figure 16: Surface finish or surface roughness ix

13 Figure 17: Surface characteristics Figure 18: Surface texture includes roughness and waviness. Many surfaces have lay: directional striations across the surface Figure 19: A profile is a two-dimensional picture of a three dimensional surface that may be thought of as the result of a sectioning place cutting the surface. Profiles are ordinarily taken perpendicular to the lay Figure 20: Illustrations of SEM machine Figure 21: CNC Milling Machine Figure 22: Shear Cutting Machine Figure 23: Composite specimen Figure 24: Scanning electron microscope machine (SEM) Figure 25: Nomenclature of SEM [23] Figure 26: Measurement process Figure 27: Print out of the surface roughness value Figure 28: Composite Material Figure 29: Cutting tool Figure 30: Raw Material from scrap CTRM Figure 31: Shear Cutting Machine Figure 32: Drill the holes Figure 33: Tight the drill bit in the drilling machine Figure 34: Remove the drill bit from the drilling machine Figure 35: Clean the machine Figure 36: Scanning Electron Microscope (SEM) Figure 37: Cut the specimen to check the surface roughness Figure 38: Specimen after cut using hand saw Figure 39: Portable Surface Roughness Tester Figure 40: Taking measurement Figure 41: Print out the result Figure 42: Experiment flowchart Figure 43: Ø 4.0 mm Figure 44: Ø 4.5 mm Figure 45: Ø 5.0 mm x

14 Figure 46: Ø 5.5 mm Figure 47: Ø 6.0 mm Figure 48: Ø 4.0 mm Figure 49: Ø 4.5 mm Figure 50: Ø 5.0 mm Figure 51: Ø 5.5 mm Figure 52: Ø 6.0 mm Figure 53: Ø 4.0 mm Figure 54: Ø 4.5 mm Figure 55: Ø 5.0 mm Figure 56: Ø 5.5 mm Figure 57: Ø 6.0 mm Figure 58: Crack at cutting speed 75 rpm at Ø 4 mm (Peel-up) Figure 59: Crack at cutting speed 75 rpm at Ø 4 5mm (Peel-up) Figure 60: Crack at cutting speed 75 rpm at Ø 6 mm (Peel-up) Figure 61: Crack at cutting speed 325 rpm at Ø 4 mm (Push-out) Figure 62: Crack at cutting speed 1050 rpm at Ø 4 mm (push-out) Figure 63: Morphology of drilling holes processes Figure 64: Graph of surface roughness vs. ø drill cutter for sampling length 0.25mm Figure 65: Graph of surface roughness vs. ø drill cutter for sampling length 0.08mm Figure 66: Graph of surface roughness vs. ø drill cutter for spindle speed 1050rpm 72 Figure 67: Graph of surface roughness vs. ø drill cutter for spindle speed 325 rpm. 72 Figure 68: Graph of surface roughness vs. ø drill cutter for spindle speed 75 rpm xi

15 LIST OF TABLE Table 1: Sampling length for appendices profile roughness parameter (R a, R q, R sk, R ku, RΔ q ) material ratio curve, probability density function and related parameter. 29 Table 2: Specifications of CNC Milling Machine Table 3: Surface roughness obtain using different diameter cutter and cutting speed for High Speed Steel Drill Bit (HSS) for sampling length 0.25mm Table 4: Surface roughness obtain using different diameter cutter and cutting speed for High Speed Steel Drill Bit (HSS) for sampling length 0.08mm xii

16 CHAPTER 1 INTRODUCTION 1.1 Background of Project Because composite material have superior properties such as high strength-toweight ratio, high stiffness-to-weight ratio, excellent fatigue resistance and low thermal expansion coefficient, they are generally used to fabricate a variety of component for automotive, aerospace, marine, and consumer product. Various cutting techniques are available to drill holes, but drilling is the common way in secondary machining of composite material owing to the need for structure joining. The mechanics of drilling composite material has been studies along with the quality of the hole and the effects of tool geometry and toll material. Several hole production processes, including conventional drilling, ultrasonic drilling, laser-beam drilling, water jet drilling, etc., have been proposed for a variety of economic and quality reasons. Conventional drilling is still the most widely used technique in industry today. A major concern that has received considerable attention in drilling holes in FRCM is the delamination, especially at the bottom surface of the workpiece (drill exit). The thrust force developed during the drilling process affects the width of the delamination zone. 1

17 1.2 Problem Statement The use of fiber-reinforced composite materials in automobile and aerospace industries has grown considerably in recent years because of their unique properties such as high specific stiffness and strength, high damping, good corrosive resistance, and low thermal expansion. Drilling is usually the final operation during the assembly of the structures in these applications. Any defects that lead to the rejection of the parts represent an expensive loss. For example, in the aircraft industry, drilling-associated delamination accounts for 60% of all part rejections during final assembly of an aircraft. The economic impact of this is significant considering the value associated with the part when it reaches the assembly stage. The quality of the drilled holes such as waviness/roughness of its wall surface, axial straightness, and roundness of the hole cross-section can cause high stresses on the rivet, which will lead to its failure. Stress concentration, delamination, and micro cracking associated with machined holes significantly reduce the composites performance. Thus this thesis will investigate the effect of cutting speed and cutter diameter in drilling of aero composite with honeycombed structure in order to reduce part rejection during final assembly of an aircraft.. 2

18 1.3 Objective Project 1) To understand the science and technology of surface integrity in machining process. 2) To determine the defect occur on the composite surface with difference drilling parameter (cutting speed and cutter diameter). 3) To measure the surface roughness of the drilled hole with different drilling parameter (cutting speed and cutter diameter). 1.4 Scope of Project 1) Drilling the aero composite with different drilling parameter (cutting speed and cutter diameter) using HSS cutting tool. 2) Measure the surface roughness of the drilled hole using profilometer. 3) Characterize the defects occur using SEM. 3

19 CHAPTER 2 LITERATURE REVIEW The literature review is conducted to achieve the objectives for this research. The literature is included information on coated carbide tools used in milling, coating materials for cutting tools, wear observation during turning operations and surface finish of the machined work material. All of this information is served as guideline in the course of the study. These research studies are involved in using the: 1) Composite Material 2) Drilling machine 3) Scanning Electron Microscope 4) Portable Surface Roughness Tester 4

20 2.1 Composite Material A composite material is a combination of a strong material (usually as a fiber) embedded in a weaker matrix. The combination produces a new material with properties that can greatly outperform the properties of either component [1] Composite background The principals of composite materials can be found all around us. Reinforced concrete is one example of a material in which various elements combine to create a stronger, tougher material than the sum of its individual components. Typically the term advanced composites refers to carbon, Kevlar or other highly engineered fibers embedded in an epoxy matrix. The epoxy matrix in composites serves to distribute stress loads evenly between the embedded fibers. The epoxy also stiffens the composite when cured into the desired form. [1]. The properties of certain fibers make them extremely strong in tension. Glass fibers, carbon fibers and Kevlar have very high tensile strength. Though strong and light weight these fibers lack stiffness on their own. Also, imperfections on the surface of the fibers can cause stress points, which will open to fractures under strain. When fibers are woven together the multiple fibers act to divide strain so that it is not concentrated in any one fiber. The combination of composite strength and low weight has been applied where high material performance is paramount. Initial applications of advanced composite technology were for military and space programs, where high strength to weight ratios were a necessity and cost was not critical. Since then, advanced composites have found their way into a variety of everyday uses. The Kevlar in bulletproof vests is incredibly tough. High performance sporting goods have been made from composites for decades and in addition to outperforming other materials they have produced more affordable and graceful shapes. 5

21 Fiberglass watercrafts are a mature technology that has dramatically changed the boat building industry. As composites have become better understood they have become preferred materials for aircraft. There are five key factors that determine the weight and cost of composite structures: 1) Labor content 2) Cost of machinery 3) Cost of materials 4) Tooling and assembly requirements 5) Curing requirements Early composite fabrication techniques used dry-fiber broad goods laid up by hand with resins applied by hand. Most current composites manufacturing relies on fiber broad goods that are pre impregnated with resin. These pre impregnated are still laboriously laid up by hand. These techniques use expensive materials and are very labor intensive, limiting their practical commercial application. Composite parts made using the current state-of-the-art methods typically include core stiffeners, including various kinds of specialized foams or honeycombs. These materials represent a significant cost in materials and labor for their application in addition to increasing weight and reducing usable volume. Spectrum s processes drastically reduce the need for core stiffeners. [2] Curing high performance composite parts generally requires applying both external heat and pressure to the part. This is typically accomplished using expensive autoclaves. With traditional composite fabrication techniques it can also be difficult to control the manufacturing process with verifiable precision. This and other knock-down factors force manufacturers to add weight and cost to load bearing parts in order to meet FAA certification requirements. This has tended to make testing, process controls and certification procedures expensive, limiting the use of composites in civil aircraft. 6

22 2.1.2 Composite Structure Composites are materials consisting of a com- bination of high-strength stiff fibers embedded in a common matrix (binder) material; for example, graphite fibers and epoxy resin. Composite structures are made of a number of fibers and epoxy resin laminates. These laminates can number from 2 to greater than 50, and are generally bonded to a substructure such as aluminum or nonmetallic honeycomb. The much stiffer fibers of graphite, boron, and Kevlar epoxies have given composite materials structural properties superior to the metal alloys they have replaced. The use of composites is not new. Fiber glass, for example, has been used for some time in various aircraft components. However, the term advanced composites applies to graphite, boron, and Kevlar, which have fibers of superior strength and stiffness. The use of these advanced composite materials does represent a new application for naval aircraft. [1] Figure 1: Sandwich construction. [1] Composite materials are replacing and supple- menting metallic materials in various aircraft structural components. The first materials were used with laminated fiber glass radomes and helicopter rotor blades. In recent years, the 7

23 replacement of metallic materials with more advanced composite materials has rapidly accelerated. This has become particularly evident with the advent of the F/A-18, AV- 8B, SH-60B, and CH 53E aircraft; and it is anticipated that composite materials will continue to comprise much of the structure in future aircraft. As a result, there is a growing requirement to train you in the use of advanced composite materials. There are numerous combinations of composite materials being studied in laboratories and a number of types currently used in the production of aircraft components. Examples of composite materials are as follows: graphite/epoxy, Kevlar /epoxy, boron poly- amide, graphite polyamide, boron-coated boron aluminum, coated boron titanium, boron graphite epoxy hybrid, and boron/epoxy. The trend is toward minimum use of boron/epoxy because of the cost when compared to current generation of graphite/epoxy composites. Composites are attractive structural materials because they provide a high strength/weight ratio and offer design flexibility. In contrast to traditional materials of construction, the properties of these materials can be adjusted to more efficiently match the requirements of specific applications. However, these materials are highly susceptible to impact damage, and the extent of the damage is difficult to determine visually. Nondestructive inspection (NDI) is required to analyze the extent of damage and the effectiveness of repairs. In addition, repair differs from traditional metallic repair techniques. 8

24 2.2 Principle of Machining Process Machining is essentially the process of removing unwanted material from wrought (roller) stock, forgings, or casting to produce a desire shape, surface finish and dimension. It is one of the four major types of manufacturing processes used to create product component. Machining is done by shaving away material in small pieces, called chips using very hard cutting tools powerful, rigid machine tools. The cutting tools may be held stationary and moved across the rotating workpiece as on a lathe or a rigid held work piece may move into a rotating cutting tool as a milling machine. Historically, machining process probably began with Besson in 1569 when he invented the screw-cutting lathe and later when a practical version was built by Henry Maudslay in Horizontal milling machine first appeared in 1820 when Eli Whitney used them for the manufacture of firearm, and the vertical milling first appeared in Machining processes remove material in the form of chips that are disposed or recycled. Machining is more costly than casting, molding, and forming processes, which are generally quicker and waste less material, but machining is often justified when precision is needed. [3] Drilling Process The drilling machine (drill press) is a single purpose machine for the production of holes. Drilling is generally the best method of producing holes. The drill is a cylindrical bar with helical flutes and radial cutting edges at one end. The drilling operations simply consist of rotating the drill and feeding it into the work piece being drilled. The process is simple and reasonably accurate and the drill is easily controlled both in cutting speed and feed rate. The drill is probably one of the original machining processes and is the most widely used. The spindle holds a drill chuck to hold the cutting tools (drill bits, center drills, deburring tools, etc.). 9