Adhesives & Polymers Raw Materials This publication describes chemical products available from Eastman Chemical Company. Although typical properties are given, Eastman makes no representation that shipments will conform to the value given. Sales specifications and technical data sheets are available on request.
CONTENTS Eastoflex Amorphous Polyolefins...... 1 Functionalized Polyolefins...... 2 Eastman AQ Polymers...... 2 Picco Aromatic Hydrocarbon Resins...... 2 Piccotac Aliphatic Hydrocarbon Resins from USA...... 3 Piccotac Aliphatic Hydrocarbon Resins from Europe...... 3 Eastotac Hydrogenated Hydrocarbon Resins...... 4 Regalite Hydrogenated Hydrocarbon Resins...... 5 Regalrez Hydrogenated Hydrocarbon Resins...... 6 Plastolyn Hydrocarbon Resins...... 6 Pure Monomer Resins...... 6 Rosin Resins From Asia...... 7 Rosin Resins From Europe...... 7 Rosin Resins From Mexico...... 8 Liquid & Specialty Rosin Resins From Europe...... 8 Tacolyn Rosin Ester Dispersions From Asia...... 8 Tacolyn Resin Dispersions From Europe...... 9 Tacolyn Resin Dispersions From USA...... 10 Dresinate Rosin Soaps from USA...... 11
Eastoflex Amorphous Polyolefins Propylene Homopolymers Thermosel Viscosity @ 190 C, mpa s ASTM D3236 Ring & Ball C ASTM E28 Glass Transition Temperature, C ASTM D3418 Penetration Hardness, dmm ASTM D5 Tensile Strength, MPa (psi) ASTM D412 Elongation, % ASTM D412 P1010PL a 1,000 155 10 18 1.38 (200) 200 P1023PL 2,300 155 10 18 1.38 (200) 100 Polypropylene/Propylene-Ethylene Copolymer Mixtures M1010PL 1,000 153 19 30 0.90 (130) 35 M1018PL 1,800 155 15 25 0.83 (120) 100 M1020PL 2,000 153 21 35 M1030PL 3,000 155 12 20 1.03 (150) 100 M1058PL 5,800 155 15 20 1.24 (180) 100 M2058PL 5,800 155 16 25 Propylene-Ethylene Copolymers E1016PL 1,600 140 25 50 E1045PL 4,500 140 22 40 E1060PL 5,700 140 20 35 E1200PL 17,000 143 22 25 a PL in the formula name indicates pelletized product form. Page 1
Functionalized Polyolefins Polymer Type DSC Tm, C Penetration Hardness, dmm a Acid No. (mg KOH/g) Brookfield Thermosel Viscosity, cps @ 190 C Melt Index 190 C Molecular Weight, Mw Eastman G 2608 Ma-PE 122 <1 8-8 65,000 Eastman G 3003 Ma-PP 158 <1 9 60000-52,000 Eastman G 3015 Ma-PP 156 <1 15 25000-47,000 Eastman G 3216 Ma-PP 142 <1 16 300-60,000 Eastman AQ Polymers Structure Odor Brookfield Thermosel Viscosity @ 177 C, cp b RBSP, C T g (DSC) C Color, Gardner (molten) max. Hydroxyl number AQ 1045 Branched Slight 4,500 85 5 4 47 AQ 1350 Branched Slight 35,000 105 2 4 51 AQ 1950 Branched Slight 95,000 115 3 4 57 AQ 14000 Branched Slight 400,000 133 7 4 51 AQ 2150 Branched None 15,000 80 9 5 16 AQ 2350 Branched None 39,000 92 11 5 12 AQ 38S Linear None 9,700 Poise c @ 200 C 38 <10 AQ 55S Linear None 42,000 Poise c @ 200 C 55 <10 Picco Aromatic Hydrocarbon Resins R&B, o C Color, Molecular Weight Distribution e Cloud Points, C Gardner d M n M w Pd M z DACP EMDA MMAP OMS End Use Picco A10 EU Liquid 9 f 420 750 1.8 1,850 24 106 0 Tackifying plasticizer, printing inks Picco A100 EU 101 9 570 930 1.6 2,200 < 40 58 35 Adhesives, rubber, ink, flooring Picco A120 EU 125 8 710 1,200 1.7 2,600 < 40 56 2 65 Adhesives, paint & varnish, bitumen Picco A120 PI EU 120 6 700 1,200 1.7 2,200 Picco A130 EU 135 6 870 1.650 1.9 3,100 Picco A140 EU 142 8 910 1,700 1.9 3,200 < 40 74 3 94 Picco A140 PI EU 138 6 900 1,700 1.9 3,200 Viscosity specification for printing inks Picco AR85 EU 87 9 520 710 1.6 1,090 < 40 39 3 < 30 Picco AR100 EU 100 8 600 800 1.4 1,200 < 40 43 4 < 30 Solvent based pressure sensitive adhesives a D5: Needle under 100g load for 5 s@25 C, tenths mm b Measured using Brookfield Thermosel viscometer RVDV-1+, 12g of each sample conditioned at 90 C for 16 hr in a vacuum oven prior to testing. c Sieglaff-McKelvey Capillary Rheometer, 100 sec -1 shear rate d Gardner 50% in toluene, if not otherwise mentioned. e Data for EU and USA are not comparable due to differences in setup. Page 2
Piccotac Aliphatic Hydrocarbon Resins from USA R&B, o C Color, Molecular Weight Distribution b Cloud Points, C Melt Viscosity, mpa.s Gardner a M n M w Pd M z DACP EMDA MMAP 140 C 160 C 180 C End Use Piccotac 1020 USA 5 3 c 800 1,380 1.7 2,600 43 174 92 Piccotac 1095 USA 94 3 800 1,700 2.1 3,500 52 179 94 6,000 1,000 Tackifier, plasticizer Piccotac 1098 USA 100 3 900 2,150 2.4 4,950 57 188 94 7,900 1,300 Pressure sensitive adhesives Piccotac 1100 USA 100 3 950 2,900 3.0 8,250 62 193 96 6,300 1,800 300 Hot melt roadmarking Piccotac 1115 USA 110 3 1,100 3,800 3.4 15,900 69 194 99 36,000 7,000 1,800 Hot melt pressure sensitive Piccotac 9105 USA 105 2 1,000 3,200 3.2 9,750 60 92 Hot melt adhesives Piccotac 9095 USA 94 3 850 1,900 2.3 4,250 47 88 Piccotac 8095 USA 95 3 850 2,200 2.6 5,500 38 76 Hot melt & solvent based pressure sensitive adhesives Piccotac Aliphatic Hydrocarbon Resins from Europe R&B, o C Color, Molecular Weight Distribution b Cloud Points, C Melt Viscosity, mpa.s Gardner a M n M w Pd M z DACP EMDA MMAP 140 C 160 C 180 C End Use Piccotac 7590-N EU 91 2 1,000 1,700 1.7 2,500 22 144 62 2,100 520 High quality hot melt adhesives, hot melt pressure sensitive adhesives a Gardner 50% in toluene, if not otherwise mentioned. b Data for EU and USA are not comparable due to differences in setup. c As it is. Page 3
Eastotac Hydrogenated Hydrocarbon Resins R&B, o C Color, Molecular Weight Distribution b Cloud Points, C Gardner a M n M w Pd M z DACP MMAP End Use Eastotac C-100R AP 100 1.5 550 1,100 2.0 2,100 56 78 Packaging, nonwovens, assembly, hot melt pressure sensitive adhesives Eastotac C-100L AP 100 <1 550 1,100 2.0 1,900 57 81 Eastotac C-100W AP 100 <1 550 1,000 1.8 1,900 64 83 Packaging, nonwovens, glue sticks, assembly, hot melt pressure sensitive adhesives Eastotac C-115R AP 115 1.5 550 1,150 2.1 2,300 60 78 Eastotac C-115L AP 115 <1 550 1,100 2.0 2,250 61 80 Packaging, assembly, hot melt pressure sensitive adhesives Eastotac C-115W AP 115 <1 550 1,050 1.9 2,000 68 85 Packaging, glue sticks, assembly, hot melt pressure sensitive adhesives Eastotac H-100R USA 100 1.5 450 1,050 2.3 2,550 68 79 Eastotac H-100L USA 100 <1 450 1,000 2.2 2,300 65 78 Packaging, nonwovens, assembly, hot melt pressure sensitive adhesives Packaging, nonwovens, glue sticks, assembly, hot melt pressure sensitive adhesives Eastotac H-100W USA 100 <1 450 1,000 2.2 2,150 69 81 Eastotac H-115R USA 115 1.5 450 1,050 2.3 2,450 76 82 Eastotac H-115L USA 115 <1 450 1,000 2.2 2,400 75 82 Packaging, assembly, hot melt pressure sensitive adhesives Eastotac H-115W USA 115 <1 450 950 2.1 2,100 68 80 Packaging, glue sticks, assembly, hot melt pressure sensitive adhesives Eastotac H-130R USA 130 1.5 500 1,050 2.1 2,400 70 81 Eastotac H-130L USA 130 <1 500 1,050 2.1 2,350 77 83 Eastotac H-130W USA 130 <1 500 1,000 2.0 2,200 76 83 Eastotac H-142R USA 142 1.5 500 1,050 2.1 2,300 74 82 Eastotac H-142W USA 142 <1 500 950 1.9 2,000 76 85 Packaging, assembly a Gardner 50% in toluene, if not otherwise mentioned. b Data for China, USA, and EU are not comparable due to differences in setup. Page 4
Regalite Hydrogenated Hydrocarbon Resins R&B, C Color, Molecular Weight Distribution b Cloud Points, C Melt Viscosity, mpa.s Gardner a M n M w Pd M z DACP MMAP OMS 120 C 140 C 160 C End Use Regalite R1010 EU Liquid <1 c 82 < 40 2,300 e Tackifier, plasticizer Regalite R1090 EU 88 +1.0 d 500 700 1.4 1,100 39 74 < 40 6,500 800 190 Regalite R1100 EU 100 +0.8 d 600 900 1.5 1,500 45 78 < 40 25,000 2,500 500 Regalite S1100 EU 100 <1 500 700 1.4 1,500 46 82 < 40 25,000 2,500 500 Regalite R1125 EU 123 +1.0 d 800 1,300 1.6 2,100 56 86 < 40 6,800 Hot melt adhesives, hot melt pressure sensitive adhesives, coatings, sealants Hot melt adhesives, coatings, sealants, plastic modification Regalite R9100 EU 99 +4.6 d 600 850 1.4 1,300 36 71 < 40 2,800 500 Hot melt adhesives, glue sticks Regalite C8010 AP Liquid <1 c 29 76 < 40 1,000 e Tackifier, plasticizer Regalite R7100 EU 102 <1 600 900 1.5 1,500 14 63 32 3,100 550 Hot melt adhesives High temperature hot melt adhesives, amorphous polyolefin based hot melt Regalite S7125 EU 122 <1 800 1,300 1.6 2,200 35 72 < 40 6,800 adhesives Packaging, nonwovens, glue sticks, Regalite C6100 AP 100 <1 610 1,010 1.7 1,880 23 55 < 50 2500 490 hot melt pressure sensitive adhesives Packaging, nonwovens, glue sticks, Regalite C6100L AP 100 <1 480 900 1.9 2,000 23 55 < 50 3900 700 hot melt pressure sensitive adhesives Hot melt adhesives & hot melt pressure Regalite S5100 EU 97 <1 600 900 1.5 1,800 8 59 5 3,800 600 sensitive adhesives, glue sticks a Gardner 50% in toluene, if not otherwise mentioned. b Data for China, USA, and EU are not comparable due to differences in setup. c As it is. d Hunterlab b, 5 cm path length, 50% in toluene. e Brookfield RVTD, spindle 21, 50 C. Page 5
Regalrez Hydrogenated Hydrocarbon Resins R&B, o C Color, Molecular Weight Distribution b Cloud Points, C YID a M n M w Pd M z DACP MMAP End Use Regalrez 1018 USA 19 6 300 350 1.2 500 14 64 Tackifier, plasticizer Regalrez 1094 USA 95 2 550 850 1.6 1,350 59 84 Regalrez 1126 USA 124 2 700 1,250 1.8 2,050 76 92 Regalrez 1139 USA 141 2 1,350 3,100 2.3 5,200 79 109 Regalrez 3102 USA 102 3 800 1,450 1.8 2,350 15 24 Regalrez 6108 USA 108 3 750 1,400 1.8 2,300 25 53 Plastolyn Hydrocarbon Resins R&B, C High stability tackifiers adhesives and sealants Plastic modification Color, Molecular Weight Distribution b Cloud Points, C YID a M n M w Pd M z DACP EMDA MMAP OMS End Use Plastolyn R1140 EU 140 <1 c 1,200 2,000 1.7 3,000 Aliphatic resin - Plastic modification, film modification. Plastolyn 240 USA 121 11 1,150 3,800 4.0 8,500 < 50 8 >180 Plastolyn 290 USA 140 13 1,350 5,200 3.3 14,000 44 9 >180 Pure Monomer Resins R&B, C Aromatic resins - Plastic modification, contact adhesives, footwear, reinforcing resin Color, Molecular Weight Distribution b Cloud Points, C YID a M n M w Pd M z DACP MMAP OMS End Use Endex 155 USA 153 5 2,400 6,950 3.0 13,850 23 16 129/121 Reinforcing resin for block copolymers Endex 160 USA 159 8 2,500 8,600 3.6 18,400 15 16 149/140 Kristalex 1120 USA 119 7 800 2,800 3.5 7,600 35 5 >180 Kristalex 3070 USA 70 7 650 950 1.5 1,450 < 50 0 8/3 Kristalex 3085 USA 85 4 650 1,150 1.8 1,900 < 50 1 36/32 Hot melt adhesives, bookbinding, packaging Kristalex 3100 USA 100 5 700 1,500 2.1 2,550 < 50 5 76/68 Kristalex 3115 USA 115 10 1,150 2,500 2.2 4,100 < 50 3 130/115 Kristalex 5140 USA 139 4 1,500 4,900 3.3 12,100 48 9 >180 Plastic modification, coatings, sealants Kristalex F85 EU 86 <1 c 750 1,200 1.6 1,950 < 50 1 46 Kristalex F100 EU 99 <1 c 800 1,400 1.8 2,200 < 50 2 73 Hot melt adhesives, bookbinding, packaging Kristalex F115 EU 117 <1 c 1,150 2,050 1.8 3,300 < 50 2 110 Piccolastic A5 USA 5 2 c 300 350 1.2 1,300 < 50 6 140/ 5 Piccolastic A75 USA 74 1 c 700 1,300 1.9 37,400 < 50 6 74/70 Adhesives, coatings, plastic modification Piccolastic D125 USA 126 2 c 1,300 37,400 28.5 179,000 32 13 >180 Adhesives, plastic modification Piccotex 75 USA 75 6 750 1,100 1.7 1,700 < 50 1 9/ 10 Piccotex 100 USA 98 6 1,000 2,200 2.2 3,600 < 50 7 26/20 Piccotex 120 USA 118 5 1,450 3,500 2.4 6,400 35 11 53/46 Hot melt adhesives, food packaging, coatings Piccotex LC USA 91 8 750 1,350 1.8 2,200 < 50 3 7/ 9 a YlD: Yellowness Index in 50% toluene, if not otherwise mentioned. b Data for EU and USA are not comparable due to differences in setup. c Gardner color. Page 6
Rosin Resins From Asia Chemical Type R&B, C Color, USRG Color, Gardner (50% in toluene) Acid No. End Use Rosin Ester Resins Eastman Ester Gum 8D-C Deodorized rosin ester 88 N O max 8 max Chewing gum, depilatory wax, composite compounding Chewing gum, depilatory wax, hot melt & solvent based pressure sensitive Staybelite Ester 5-C Partially hydrogenated rosin ester 80 N O max 8 max adhesives, wax modification, rubber compounding Hot melt adhesives for packaging & bookbinding, hot melt & solvent based pressure sensitive adhesives, flooring adhesives, depilatory wax, asphalt Permalyn 5095-C Stabilized rosin ester 88 2-4 10 max Permalyn 5110-C Stabilized rosin ester 101 2-6 16 max Polymerized Rosin Resins Poly-Pale Partially dimerized rosin 99-106 WG O 8 140 min Dymerex Dimerized rosin 138-151 K O 9 140 min Esters of Polymerized Rosins Eastman Ester Gum 10D Deodorized ester 108 WW O 5 Poly-Pale Ester 10 Glycerol ester 109 WG O 8 max Pentalyn C Pentaerythritol ester 126 11 10 Rosin Resins From Europe Chemical Type C a Color, Gardner b & bitumen modification, concrete curing Hot melt adhesives for packaging & bookbinding, hot melt roadmarking, wax modification, solvent based pressure sensitive adhesives, rubber compounding Adhesives, printing inks, solder flux Chewing gum, hot melt adhesives, solvent based pressure sensitive adhesives Packaging & woodworking hot melt adhesives, coatings, inks, solvent based adhesives Acid Melt Viscosity, mpa.s No. 120 C 140 C 160 C 180 C End Use Staybelite Resin-E Partially hydrogenated rosin 79 5 162 Foralyn-E Hydrogenated rosin 81 2 168 Hot melt adhesives, solder flux, pigment coating Foral AX-E Highly hydrogenated rosin 81 <1 166 Permalyn 5095 Stabilized rosin ester 92 3 8 3,300 560 150 Hot melt adhesives Eastman Ester Gum 8D Deodorized rosin ester 93 USRG WW 7 Chewing gum Staybelite Ester 5-E Partially hydrogenated rosin ester 85 USRG X 8 Chewing gum Staybelite Ester 10-E Partially hydrogenated rosin ester 86 6 8 1,800 330 90 Adhesives, cosmetics Foral 85-E Highly hydrogenated rosin ester 86 2 9 1,500 340 <100 Hot melt adhesives, solvent based adhesives Foralyn 90 Hydrogenated rosin ester 89 1 9 2,800 500 130 Permalyn 5110 Stabilized rosin ester 106 6 14 2,300 470 130 Hot melt adhesives Permalyn 6110 Stabilized rosin ester 110 <1 13 2,100 440 120 Pentalyn H-E Partially hydrogenated rosin ester 108 8 14 2,600 480 110 Pressure sensitive adhesives Foral 105-E Highly hydrogenated rosin ester 106 5+ 14 20,000 2,000 410 Hot melt adhesives, solvent based adhesives Foralyn 110 Hydrogenated rosin ester 109 2 14 3,100 650 150 a Eastman Drop Method. b 50% in toluene, if not otherwise mentioned. Page 7
Rosin Resins From Mexico Rosin Ester Resins Chemical Type R&B, C Color, USRG Color, Gardner (50% in toluene) Acid No. End Use Chewing gum, hot melt adhesives, solvent based pressure sensitive Eastman Ester Gum 8D-M Deodorized rosin ester 83-87 11 3-9 adhesives Permalyn 6110-M Pentaerythritol ester of gum rosin 113 < 3 13 Hot melt adhesives and solvent based contact adhesives Liquid & Specialty Rosin Resins From Europe Chemical Type C a Color, Gardner b Acid No. Melt Viscosity, mpa.s @ 25 C Liquid Rosins Foralyn 5020-F Partially hydrogenated rosin ester Liquid 3 c 6 5,400 Cosmetics, perfumery, tackifier, plasticizer Abitol-E Technical hydroabietyl alcohol Liquid Hunter 2 c 0.1 6,500 @ 50 C Tackifier, plasticizer Other Specialties Cellolyn 21-E Hydroabietyl phthalate 63 1 6 Tackifier for deep-freeze acrylic tape and label End Use Tacolyn Rosin Ester Dispersions From Asia Dispersed Phase C a ph Viscosity, cps @ 25 C mpa.s TSC % ph Tolerance Range Tacolyn 3179H-C 70 7 850 50 4 13 Tacolyn 3509-C 70 7 230 55 4 13 End Use It is recommended as a tackifier for acrylic latex polymers used in label, tape, and construction applications. It provides broad utility as a general purpose acrylic pressure sensitive adheisve tackifier promoting high peel and tack to polyolefin substrates and recycled corrugated board. It enhances specific adhesion acrylic latex polymers to polyolefin substrates and recycled corrugated board. Due to the low surface tension, it is generally not necessary for the post-addition of wetting agent during coating. It provides good cohesion and humidity resistance. a Eastman Drop Method. b 50% in toluene, if not otherwise mentioned. c As it is. Page 8
Tacolyn Resin Dispersions From Europe Dispersed Phase, Typical Properties Resin Dispersion, Typical Properties Viscosity @ TSC ph Tolerance Type C a ph 25 C mpa.s % Range Tacolyn 64 Hydrogenated rosin ester 60 7.0 300 50 4 13 Tacolyn 100 Aliphatic hydrocarbon 78 7.0 250 50 4 13 Tacolyn 2522 Stabilized rosin acid 59 8.0 200 50 4 13 Tacolyn 2751 Stabilized rosin acid 76 7.5 250 55 4 13 Tacolyn 3166 Stabilized rosin ester 74 7.0 3,000 58 4 13 Tacolyn 3179H Stabilized rosin ester 70 7.0 850 50 4 13 Tacolyn 3183 Stabilized rosin ester 75 7.0 600 53 4 13 Tacolyn 3189 Stabilized rosin ester 70 7.0 500 50 4 13 Tacolyn 3509 Stabilized rosin ester 73 7.0 230 55 4 13 Tacolyn 4056 Hybrid 70 7.0 300 57 4 13 Tacolyn 4177 Modified hydrocarbon 75 7.0 150 50 4 13 Tacolyn 4187 Stabilized rosin ester Liquid 7.0 400 50 4 13 Tacolyn 4503 Hybrid 75 7.0 400 55 4 13 Tacolyn 5193 Modified hydrocarbon 80 10 100 50 4 13 End Use It is recommended for use in tape and label applications where extended shelf life is required. It enhances tack and peel on polyethylene and carton board. It is an excellent tackifier for use in adhesives and laminations based on aqueous systems of natural and isoprene rubbers. It is designed for use in pressure sensitive adhesives based on acrylic polymer emulsions or carboxylated styrene-butadiene rubber latexes, where it greatly enhances the tack and peel to polyethylene and carton board. It is designed for adhesive applications requiring high cohesive strength retention in conjunction with improved adhesion properties. The high solids content aids drying in situations where forced air-drying is not available. It is recommended as a tackifier for acrylic based pressure sensitive adhesive applications. It provides broad utility as a general purpose acrylic pressure sensitive adhesives tackifier promoting high peel and tack to polyolefin substrates and recycled corrugated board. It is designed for use in pressure sensitive adhesives based on acrylic polymer emulsions or carboxylated styrene-butadiene rubber latexes, where it greatly enhances the tack and peel to polyethylene and carton board. It enhances specific adhesion of acrylic latex polymers to polyolefin substrates and recycled corrugated board. Due to the low surface tension, it is generally not necessary for the post-addition of wetting agent during coating. It is designed for use in pressure sensitive adhesives based on acrylic polymer emulsions or carboxylated styrene-butadiene rubber latexes, where it greatly enhances the tack and peel to polyethylene and carton board. It can be used as the sole tackifying resin with selected acrylic polymers. It has excellent adhesion to polyolefin and carton board substrates and is suggested for use in electronic data process (EDP) label formulations. It is designed for use in pressure sensitive adhesives based on acrylic and styrene-butadiene rubber copolymer emulsions where it increases tack to polyethylene. It also enhances the low temperature performance of the adhesives. It is designed for use in pressure sensitive adhesives based on acrylic polymer emulsions or carboxylated styrene-butadiene rubber latexes, where it greatly enhances the tack and peel to polyethylene and carton board. It is designed for use in pressure sensitive adhesives based on natural rubber latex or carboxylated styrene-butadiene rubber latexes, where it greatly enhances the tack and peel to polyethylene and carton board. a Eastman Drop Point Method. Page 9
Tacolyn Resin Dispersions From USA Dispersed Phase, Typical Properties Resin Dispersion, Typical Properties End Use Viscosity @ TSC ph Tolerance Type C a ph 25 C, mpa.s % Range Tacolyn 1070 Modified hydrocarbon 70 10 1,400 55 4 13 Hydrogenated rosin Tacolyn 3100 ester 92 10 900 55 4 13 Tacolyn 3179HA Stabilized rosin ester 70 b 7 400 50 4 13 Hydrogenated rosin Tacolyn 3280 ester 82 10 2,500 55 4 13 Tacolyn 3400 Hydrogenated rosin ester 92 10 1,100 55 >7 Tacolyn 4603 Hybrid 77 8 900 55 4 13 Tacolyn 5070 Aliphatic hydrocarbon 70 4 100 50 4 13 Tacolyn 5085 Aliphatic hydrocarbon 82 10 1,300 55 4 13 Tacolyn 5095 Aliphatic hydrocarbon 92 10 600 55 >7 Tacolyn 5194 Aromatic hydrocarbon 85 12 460 55 >7 Tacolyn 5002 Modified hydrocarbon 70 10.5 1,000 55 >7 Tacolyn 5003 Modified hydrocarbon 130 11 1,000 45 >7 a Ring and Ball Point Method. b Eastman Drop Point Method. It enhances specific adhesion to polyolefin substrates and recycled corrugated board. It promotes cohesive strength and offers good moisture resistance when used in pressure sensitive adhesives. It may be used in clear film label applications due to its good color retention and oxidation resistance. It is highly hydrogenated and promotes high temperature performance in waterborne pressure sensitive adhesives. It provides broad utility as a general purpose acrylic pressure sensitive adhesives tackifier promoting high peel and tack to polyolefin substrates and recycled corrugated board. It promotes excellent aging stability, high temperature performance, and enhances specific adhesion of adhesives to polyolefin substrates and recycled corrugated board. It is recommended for use in food packaging applications such as closures, lidding, and cold seal adhesives, as well as pressure sensitive adhesives that contact food. It is also used in adhesives applications requiring higher temperature strength such as in high temperature masking tapes, packaging tapes, and contact adhesives. It is recommended as a tackifier for acrylic latex where it delivers high peel adhesion, outstanding cohesive strength and high tack to adhesives for polyolefin substrates and corrugated board. It is ideal for low peel applications, as it imparts peel strength in small increments relative to resination level. It also exhibits good storage and mechanical stability. It is recommended as a tackifier for isoprene rubber and natural rubber latex polymers used in tape applications promoting high peel and cohesive strength. It is recommended as a tackifier for isoprene rubber and natural rubber latex polymers used in tape applications promoting high peel and cohesive strength. It is recommended as a tackifier for isoprene rubber and natural rubber latex polymers used in tape applications that require an exceptional degree of color retention, oxidation resistance, high temperature performance, and good moisture resistance. It is recommended for water-based contact adhesives where fast break properties are required as in foam to foam bonding applications. It is recommended as a single tackifier for anionic polychloroprene latex polymers used in contact adhesive applications. Page 10
Dresinate Rosin Soaps from USA Soap Type Solid Content, % Acid No. Density, kg/l Appearance End Use Dresinate 91 Potassium 88 15 1.06 Dark brown paste Used as an emulsifier ingredient in solvent cleaners and soluble oils for metal cleaning. Provides highly stable emulsions over a wide range of water hardness when used in combination with petroleum sulfonates in soluble oil formulations. Used as an emulsifier ingredient in solvent cleaners, Dresinate 91-44W Potassium 46 15 1.02 Dark brown viscous liquid metalworking, and industrial applications. It is designed mainly as an emulsifier promoting detergent or cleaning activity, particularly in highly built Dresinate TX Sodium 96 0.5 0.42 Small brown flakes industrial metal cleaners. Dresinate TX-60W Sodium 60 Nil 0.948 Dark brown viscous liquid Used as the soap emulsifier in the manufacture of road surfacing asphalt anionic emulsions of the RS and MS types. Page 11
NORTH AMERICA Eastman Chemical Company Corporate Headquarters P.O. Box 431 Kingsport, TN 37662-5280 U.S.A. Tel: (1) 423-229-2000 Fax: (1) 423-229-1193 www.eastman.com ASIA PACIFIC REGIONAL HEADUARTERS Eastman Chemical Asia Pacific Pte. Ltd. #05-04 Winsland House 1 3 Killiney Road Singapore 239519 Tel: (65) 6831-3100 Fax: (65) 6732-4930 Eastman Chemical Ltd., Shanghai Rep. Office 1206, CITIC Square No. 1168 Nanjing Road (W) Shanghai 200041, P.R. China Tel: (86) 21-6120-8700 Fax: (86) 21-5213-5265 Eastman Chemical Ltd., Guangzhou Rep. Office 33 JianShe 6th Road Guangzhou 510060, P.R. China Tel: (86) 20-8383-4301 Fax: (86) 21-8383-4023 Eastman Chemical Ltd., Taiwan Branch 8F/1, No. 13, Sec. 2 Pei Tou Road Pei Tou 112 Taipei, Taiwan Tel: (886) 2-2893-5132 Fax: (886) 2-2891-9303 Eastman Chemical Japan Ltd. AIG Aoyama Building 5F 2-11-16 Minami Aoyama Minato-ku, Tokyo 107-0062, Japan Tel: (81) 3-3475-9510 Fax: (81) 3-3475-9515 Eastman Chemical Korea Ltd. 6 th Floor, Royal Building 5 Dangju-dong, Chongro-ku Seoul, Korea 110-721 Tel: (82) 2-720-1103 Fax: (82) 2-720-1104 Eastman Chemical Ltd., Thailand Liasion Office 16th Fl., Ploenchit Center Building 2 Sukhumvit Road, Klong-Toey Bangkok, Thailand 10110 Tel: (66) 2-656-8077 Fax: (66) 2-656-8084 Eastman Chemical Ltd., India Liaison Office C403, Delphi Building Hiranandani Gardens Powai, Mumbai 400 076, India Tel: (91) 22-5551-9000 Fax: (91) 22-5551-9099 www.tackifier.com Material Safety Data Sheets providing safety precautions, that should be observed when handling and storing Eastman products, are available online or by request. You should obtain and review the available material safety information before handling any of these products. If any materials mentioned are not Eastman products, appropriate industrial hygiene and other safety precautions recommended by their manufacturers should be observed. Neither Eastman Chemical Company nor its marketing affiliates shall be responsible for the use of this information, or of any product, method or apparatus mentioned, and you must make your own determination of its suitability and completeness for your own use, for the protection of the environment and for the health and safety of your employees and purchasers of your products. NO WARRANTY IS MADE OF THE MECHANTABILITY OR FITNESS OF ANY PRODUCT, AND NOTHING HEREIN WAIVES ANY OF THE SELLER'S CONDITIONS OF SALE. Abitol, Cellolyn, Dresinate, Dymerex, Eastman, Eastman AQ, Eastman G, Eastoflex, Eastotac, Endex, Foral-E, Foralyn, Kristalex, Pentalyn, Permalyn, Picco, Piccolastic, Piccotac, Piccotex, Plastolyn, Poly-Pale, Regalite, Regalrez, Staybelite-E and Tacolyn are trademarks of Eastman Chemical Company. Eastman Chemical Company, 2007. Publication WA-110A October 2007 Printed in P.R. China