for SOMO Optical O-SOM

Transcription

1 TEST RESULTS and REPORT for SOMO Optical O-SOM by COLTS Laboratories maintains A2LA accreditation to ISO/IEC for the tests listed on Certificate # Any tests not included on this certificate have been identified on the appropriate test result page. - Results in this report only relate to the samples analyzed. - This report shall not be reproduced, except in full, without written approval from COLTS Laboratories. - Unless otherwise requested, test samples will be discarded 60 days from the report date.

2 COLTS Laboratories U.S.Highway 19 N Clearwater, FL TEL: FAX: info@colts-laboratories.com URL: A2LA Accredited-Cert.# SOMO Optical O-SOM Table of Contents Tint Consistency-SQ - 1 Test(s) Tint Rate-SQ - 1 Test(s) Tint/Color Fade - QUV-SQ - 1 Test(s) Luminous Transmittance-SQ - 1 Test(s) Tumble-SQ - 1 Test(s) Cycle Humidity Oven/Crosshatch-Convex-SQ - 1 Test(s) Authorizing Signature: Name and Title Lab Manager This report shall not be reproduced except in full, without written approval of COLTS-Laboratories. Page 1 of 1

3

4 COLTS Laboratories U.S.Highway 19 N Clearwater, FL TEL: FAX: info@colts-laboratories.com URL: SUMMARY REPORT SOMO Optical O-SOM Tint Consistency Tint Rate Poly SOMO EZ-Tint See Report See Report Tint/Color Fade - QUV See Report Luminous Transmittance After 30 min of Tinting Tumble 3.68 *CHOCA (cx) cx Effects A 5.0 Effects B 5.0 Effects D 5.0 * Cycle Humidity Oven/Crosshatch results represent the average effects measured at 16 hours cx = Convex Report Date: 09/29/2006 Report Valid Thru: 03/29/2007

5 EXHIBIT A Subjective Delamination, Crazing and Crosshatch ratings. Rate and record the performance for the surface exposed on each lens according to the following classification and description. Classification Category A - Crazing Classification A5 A4 A3 A2 A1 A0 Description No visible Crazing. Hairline Crazing only just visible points or cracks. Hairline Crazing up to 25% of the lens surface. Hairline Crazing up to 75% of the lens surface. Hairline Crazing over the entire lens surface. Severe Fern-like or Matt-like Crazing over any region of lens. Classification Category B - Delamination - Interlayer detachment. Classification B5 B4 B3 B2 Description No Delamination of individual layers over entire lens surface. Partial Delamination of individual layers up to 25% of the surface. Partial Delamination of individual layers up to 75% of the surface. Total Delamination of individual layers over the entire lens surface. Classification Category C - Delamination - complete coating detachment Classification C5 C4 C3 C2 Description No Coating Delamination of all layers from the lens surface. Delamination of all layers up to 25% of the surface. Delamination of all layers up to 75% of the surface. Complete Coating Delamination over the entire lens surface. Classification Category D - Crosshatch See exhibit B for classifications and descriptions. NOTE: Classification B relates to either a single layer hard coat or the thin film coating where one is delaminating and where one or both have been applied to the lens depending on the product type. (i.e., HC, Thin Film, HC & Thin Film) Classification C relates to a dual coated product where both a hard coat and a thin film coating has been applied and together are delaminating. (i.e. HC & thin film) For each lens tested, note any evidence of stains, smears, streaks or cloudiness.

6 EXHIBIT B

7

8

9 COLTS Laboratories U.S.Highway 19 N Clearwater, FL TEL: FAX: info@colts-laboratories.com URL: RESULTS REPORT A2LA Accredited-Cert.# SOMO Optical For Test: COLTS Internal Control Number: Tint Consistency-SQ O-SOM Lens Sample Group Description Lens Samples Substrate (lens material) Coatings (Hard Coat,AR) One lens sample group Frame Material: Polycarbonate Manufacturer: SOMO /Gia Index of Refraction: Lens Type: FSV Lens density: NA Requested by: Mike Jacobson Report valid thru: 3/29/2007 Coating Type: Comments: Poly SOMO EZ-Tint HC Test Number Dye Color Dye Temp Tinting Time %T Blotching O-SOM Black O-SOM Black O-SOM Black O-SOM Black O-SOM Black O-SOM Black O-SOM Black O-SOM Black O-SOM Black O-SOM Black Yes Yes Yes Yes Yes Yes Yes Yes Yes Yes Report Date: 9/29/2006 Lab Temp ( C) : 23 Lab Rh : 48 This report shall not be reproduced except in full, without written approval of COLTS-Laboratories.

10 Tint Consistency Avg Bath Temp (202 ) O-SOM Visible Light %T Max Min Avg Max Min Avg Lens Description

11

12 100.0 Tint Rate Avg Bath Temp (202 ) O-SOM Visible Light %T Std PC/Tintable Time in minutes

13

14 COLTS Laboratories U.S.Highway 19 N Clearwater, FL TEL: FAX: info@colts-laboratories.com RESULTS REPORT A2LA Accredited-Cert.# SOMO Optical Sample: Poly Gia SunColors Tintable 3 For Test: Tint/Color Fade QUV-SQ COLTS Internal Control Number: O-SOM Sample Group Description Samples Substrate/Material Coatings (Hard Coat, AR) One sample group Material: Polycaronate Type: HC Manufacturer: SOMO/Gia Index of Refraction: Comments: Lens Type: FSV Report Date: 09/29/2006 Lens density: NA Report valid thru: 03/29/2007 Requested by: Mike Jacobson Lab Temp: ( C): 23 Lab Rh: 44 Poly SOMO EZ-Tint Test Number %T Initial %T After Tint % T After 72hr Exposure Delta Initial After Tint % loss during exposure O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM This report shall not be reproduced except in full, without written approval of COLTS-Laboratories.

15 Tint/Color fade - QUV -SQ O-SOM % Transmittance Wavelength - nm Clear Tinted After QUV

16

17 COLTS Laboratories U.S.Highway 19 N Clearwater, FL TEL: FAX: info@colts-laboratories.com URL: A2LA Accredited Certificate # RESULTS REPORT SOMO Optical Sample: Poly SOMO EZ-Tint For Test: Luminous Transmittance-SQ - After 30 min tint Samples One sample group Manufacturer: SOMO /Gia Lens Type: FSV Lens density: NA Requested by: Mike Jacobson Colts Internal Control Number: O-SOM Sample Group Description Substrate/Material Coatings (Hard Coat,AR) Material: Polycarbonate Type: HC Index of Refraction: Comments: Report Date: 9/29/2006 Poly SOMO EZ-Tint Report Valid thru: 3/29/2007 Lab Temp ( C) : 23 Lab Rh : 49 Test Number % Transmittance O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM Average Transmittance This report shall not be reproduced except in full, without written approval of COLTS-Laboratories.

18

19 COLTS Laboratories U.S.Highway 19 N Clearwater, FL TEL: FAX: info@colts-laboratories.com URL: A2LA Accredited Certificate # RESULTS REPORT Samples One sample group Manufacturer: SOMO /Gia Lens Type: FSV Lens density: NA Requested by: Mike Jacobson SOMO Optical Sample: Poly Gia SunColors Tintable 3 For Test: Tumble-SQ Colts Internal Control Number: O-SOM Sample Group Description Substrate/Material Coatings (Hard Coat,AR) Material: Polycarbonate Type: HC Index of Refraction: Comments: Report Date: 9/29/2006 Poly SOMO EZ-Tint Report Valid thru: 3/29/2007 Lab Temp ( C) : 23 Lab Rh : 44 Standard Lenses Test Lenses Ratio Test Number Before After Delta Before After Delta Standard/Test O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM O-SOM Average Standard Delta 2.44 Average Test Delta 0.66 Average Ratio 3.68 The COLTS Laboratories lens standards used for this test were a 4 diopter base curve rather than the specified 6 diopter base curve. This was done because the test sample lenses were only available in 4 diopter base curve. Test results may be slightly different than if using the 6 diopter base curve but tests within COLTS Laboratories confirms that the difference will be This report shall not be reproduced except in full, without written approval of COLTS-Laboratories.

20 COLTS Laboratories U.S.Highway 19 N Clearwater, FL TEL: FAX: info@colts-laboratories.com URL: A2LA Accredited Certificate # RESULTS REPORT Samples One sample group Manufacturer: SOMO /Gia Lens Type: FSV Lens density: NA Requested by: Mike Jacobson SOMO Optical Sample: Poly Gia SunColors Tintable 3 For Test: Tumble-SQ Colts Internal Control Number: O-SOM Sample Group Description Substrate/Material Coatings (Hard Coat,AR) Material: Polycarbonate Type: HC Index of Refraction: Comments: Report Date: 9/29/2006 Poly SOMO EZ-Tint Report Valid thru: 3/29/2007 Lab Temp ( C) : 23 Lab Rh : 44 Current Market TUMBLE RATIO Polycarbonate - Hard Coated Frequency TUMBLE RATIO -----> Better This report shall not be reproduced except in full, without written approval of COLTS-Laboratories.

21 COLTS Laboratories U.S.Highway 19 N Clearwater, FL TEL: FAX: info@colts-laboratories.com URL: A2LA Accredited Certificate # A2LA Accredited-Cert.# RESULTS REPORT ACME Optical For Test: Tumble COLTS Control Number: O-ACME Lens Sample Group Description Lens Samples Substrate (Lens Material) Coatings (Hard Coat, AR, etc) One Lens Sample Group Lens Material: Hard Resin Type: AR Manufacturer: ACME Optical Index of Refraction: Comments: Lens Type: FSV Lens Density: Requested By: John Doe Report valid thru: 00/00/2002 Standard Lenses Test Lenses Ratio Test Item Before After Delta Before After Delta Standard/Test O-ACME O-ACME O-ACME O-ACME O-ACME O-ACME Due to process changes that occur in a lens manufacturing process the accuracy of the data reported is limited to 6 months. Frequency Average Standard Delta 4.39 Average Test Delta 1.76 Difference between Before and After. Current Market TUMBLE RATIO Hard Resin - AR TUM BLE RATIO ----> Better Average Ratio 2.50 The Test Lens ranking compared to the three-year rolling average from the COLTS Database of all similar samples that have been tested at COLTS. The Ratio equals the number of times more scratch resistant the sample lens is when compared to an uncoated CR-39 (Standard) lens. The Ratio is created by dividing the Test Lens average delta into the Standard Lens average Delta. This report shall not be reproduced except in full, without written approval of COLTS-Laboratories.

22 Tumble - In this abrasion test that was created based on actual clinical study data of normal wear for glass, uncoated plastic lenses and coated plastic lenses. It is used by most lens manufacturers in the US and Europe and has repeatedly exhibited good correlation to actual wear experience. Sample lenses are placed into a barrel approximately 9" (28cm) wide and 18" (44cm) in diameter. Media in is placed in the barrel, which will abrade the lenses.

23

24 COLTS Laboratories U.S.Highway 19 N Clearwater, FL TEL: FAX: info@colts-laboratories.com URL: A2LA Accredited Certificate # RESULTS REPORT Test Number SOMO Optical CRAZING hrs Sample: Poly SOMO EZ-Tint For Test: Cycle Humidity Oven/Crosshatch-Convex-SQ Samples One sample group Manufacturer: SOMO /Gia Lens Type: FSV Lens density: NA Requested by: Mike Jacobson Colts Internal Control Number: O-SOM Sample Group Description Substrate/Material Coatings (Hard Coat,AR) Material: Polycarbonate Type: HC Index of Refraction: Comments: Report Date: 9/29/2006 Poly SOMO EZ-Tint Report Valid thru: 3/29/2007 Lab Temp ( C) : 24 Lab Rh : 43 DELAMINATION-B DELAMINATION-C CROSSHATCH hrs hrs hrs O-SOM A5 A5 A5 B5 B5 B5 D5 D5 D1 O-SOM A5 A5 A5 B5 B5 B5 D5 D5 D1 O-SOM A5 A5 A5 B5 B5 B5 D5 D5 D0 O-SOM A5 A5 A5 B5 B5 B5 D5 D5 D2 O-SOM A5 A5 A5 B5 B5 B5 D5 D5 D0 O-SOM A5 A5 A5 B5 B5 B5 D5 D5 D1 O-SOM A5 A5 A5 B5 B5 B5 D5 D5 D5 O-SOM A5 A5 A5 B5 B5 B5 D5 D5 D2 O-SOM A5 A5 A5 B5 B5 B5 D5 D5 D0 O-SOM A5 A5 A5 B5 B5 B5 D5 D5 D0 Notes: If rating is blank, test does not apply See Exhibits A and B for explanation of results CC = Concave CX = Convex: If not noted test was on convex side This report shall not be reproduced except in full, without written approval of COLTS-Laboratories.

25 Cycle Humidity Oven Polycarbonate - Hard Coated - Convex Side "A" Effects - 16 Hours Cycle Humidity Oven Polycarbonate - Hard Coated - Convex Side "B" Effects - 16 Hours Cycle Humidity Oven Polycarbonate - Hard Coated - Convex Side "D" Effects - 16 Hours Frequency Frequency Frequency A0 A1 A2 A3 A4 A5 A Effects > Better B2 B3 B4 B5 B Effects > Better D0 D1 D2 D3 D4 D5 D Effects > Better SOMO Optical O-SOM Report Date: 09/29/2006 Report Valid Thru: 03/29/2007

26 COLTS Laboratories U.S.Highway 19 N Clearwater, FL TEL: FAX: info@colts-laboratories.com URL: A2LA Accredited Certificate # A2LA Accredited-Cert.# ACME Optical RESULTS REPORT For Test: Cycle Humidity Oven/Crosshatch-Both Sides COLTS Control Number: O-ACME Lens Sample Group Description Lens Samples Substrate (Lens Material) Coatings (Hard Coat, AR, etc) One Lens Sample Group Lens Material: Hard Resin Type: AR Manufacturer: ACME Optical Index of Refraction: Comments: Lens Type: FSV Lens Density: Requested By: John Doe Report valid thru: 00/00/2002 Test Number CRAZING DELAMINATION-B DELAMINATION-C CROSSHATCH hrs hrs hrs hrs O-ACME CC A2 A1 A1 B5 B4 B4 C5 C5 C5 D5 D5 D5 O-ACME CX A3 A1 A1 B5 B5 B5 C5 C5 C5 D5 D5 D5 O-ACME CC A3 A2 A2 B5 B5 B5 C5 C5 C5 D5 D5 D4 O-ACME CX A3 A2 A2 B5 B4 B4 C5 C5 C5 D5 D5 D5 O-ACME CC A2 A1 A1 B5 B5 B5 C5 C5 C5 D5 D5 D4 O-ACME CX A3 A1 A1 B5 B5 B5 C5 C5 C5 D5 D5 D4 O-ACME CC A3 A1 A1 B5 B5 B5 C5 C5 C5 D5 D5 D4 O-ACME CX A3 A1 A1 B5 B5 B5 C5 C5 C5 D5 D5 D4 O-ACME CC A2 A1 A1 B5 B5 B5 C5 C5 C5 D5 D5 D4 O-ACME CX A3 A1 A1 B5 B5 B5 C5 C5 C5 D5 D5 D4 Notes: If rating is blank, test does not apply See Exhibit A and B for explanation of results CC = Concave CX = Convex: If not noted test was on convex side ID No. and Convex (CX) or Concave (CC) surface Unsatisfactory crazing on 0 to 5 scale with 5 being best. Occurred in the first 8 hours. Sample has deteriorated to very unsatisfactory at the end of the 24 hours of testing (3 cycles) Sample shows no issues for adhesion as no delamination was seen on the sample. This category represents the delamination of AR coating layers and to date has not been witnessed on any sample ever tested at COLTS Due to process changes that occur in a lens manufacturing process the accuracy of the data reported is limited to 6 months This report shall not be reproduced except in full, without written approval of COLTS-Laboratories. Crosshatch Adhesion follows each cycle and is ranked as shown in another appendix. This sample has some delamination from the tape pull at the end of 24 hours on the concave side of the sample.

27 Cycle Humidity Oven/Crosshatch Adhesion (CHOCA)- Lenses are placed in sealed desiccators, which maintain 95% relative humidity. The oven maintains 65 C for a period of 8 hours then the lenses are removed and inspected for crazing, delamination and then tape is placed on the crosshatched area and pulled (done three times in succession) to evaluate this more severe delamination test. All lenses are left in ambient laboratory conditions (72 F; 50% RH) for 16 hours and then the steps are repeated twice more. Typical effects seen from this test are crazing and delamination of the coating. This test has been correlated to actual wear through clinical studies. If effects are seen at the end of the first cycle (day) there is a very high probability that the same effects will be seen during the first 6 to 10 months of normal wear. Effects seen during the second cycle have a very high probability of being seen in one to two years of normal wear. The third cycle illustrates effects that may be seen after two years.